Barium calcium zirconate titanate leadless piezoelectric ceramic material and preparation method thereof

A barium calcium zirconate titanate and lead-free piezoelectric technology, which is applied in the field of barium calcium zirconate titanate lead-free piezoelectric ceramic materials, can solve the problems of high sintering temperature of piezoelectric ceramics and difficult application of lead-free piezoelectric ceramics, etc. Achieve the effect of good performance stability and high safety

Inactive Publication Date: 2016-08-24
JIANGSU UNIV
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some researchers have used CaTiO 3 -BaZrO 3 -BaTiO 3 compound to form a solid solution, which greatly improves the piezoelectric performance, and the CaTiO obtained by this method 3 -BaZrO 3 -BaTiO 3 Piezoelectric coefficient (d 33 ) is 482PC / N, radial electromechanical coupling coefficient (K P ) is 0.48, however, its Curie temperature is about 90°C, and the sintering temperature of its piezoelectric ceramics is relatively high (1500-1600°C), and it is difficult to apply this system of lead-free piezoelectric ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Barium calcium zirconate titanate leadless piezoelectric ceramic material and preparation method thereof
  • Barium calcium zirconate titanate leadless piezoelectric ceramic material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018]The present invention will be further described in conjunction with embodiment now. Table 1 provides the formulas of a total of 4 samples of the embodiment of the present invention.

[0019] The main raw material of the formula of totally 4 samples of the embodiment of the present invention adopts piezoelectric ceramic raw material, at first adopts conventional chemical raw material to synthesize respectively with solid-phase method during preparation (Ba 0.85 Ca 0.15 )(Ti 0.9 Zr 0.1 )O 3 、BiFeO 3 、 Bi 2 WO 3 , Ba(Yb 1 / 2 Nb 1 / 2 )O 3 , and then according to the above formula ingredients, the prepared material is mixed with dehydrated alcohol by planetary ball mill ball mill, material: ball: dehydrated alcohol=1:3: (0.6~1.0) (mass ratio), after ball milling for 4~8 hours , dry to obtain dry powder, add the polyvinyl alcohol solution that accounts for its weight 8~10% concentration and be 10% (percentage by weight) in the dry powder, carry out granulation, pass th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Curie pointaaaaaaaaaa
piezoelectric charge coefficientaaaaaaaaaa
Curie pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of inorganic nonmetallic materials, in particular to a barium calcium zirconate titanate leadless piezoelectric ceramic material. A formula comprises components as follows: 91wt.%-98 wt.% of (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3, 0.1 wt.%-7.0wt.% of BiFeO3, 0.01 wt.%-1wt.% of Bi2WO6, 0.1wt.%-4wt% of Ba(Yb1 / 2Nb1 / 2)O3 and 0.01wt.%-1.8wt.% of Co2O3, wherein (Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 is prepared from ordinary chemical raw materials for piezoelectric ceramics, the leadless piezoelectric ceramics which are cadmium-free and have a high-tension electricity property are prepared, the sintering temperature of the piezoelectric ceramics can be greatly reduced, the barium calcium zirconate titanate leadless piezoelectric ceramic material is suitable for preparing a piezoelectric ceramic sensor, and the cost of the piezoelectric ceramics can be greatly reduced.

Description

technical field [0001] The invention relates to the technical field of inorganic non-metallic materials, in particular to a barium calcium zirconate titanate lead-free piezoelectric ceramic material. It adopts common chemical raw materials of piezoelectric ceramics to prepare lead-free piezoelectric ceramics with lead-free and cadmium-free high-voltage performance, and can greatly reduce the sintering temperature of piezoelectric ceramics. The piezoelectric ceramics are suitable for the preparation of piezoelectric ceramic sensors , can greatly reduce the cost of piezoelectric ceramics, conforms to the development direction of piezoelectric ceramics, can replace lead-containing piezoelectric ceramics in applications in some fields, and does not pollute the environment during preparation and use. Background technique [0002] Piezoelectric material is a new type of functional material capable of energy conversion. It can realize the conversion between mechanical energy and el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/49C04B35/622
CPCC04B35/49C04B35/622C04B2235/3208C04B2235/3215C04B2235/3224C04B2235/3251C04B2235/3258C04B2235/3274C04B2235/3275C04B2235/3298
Inventor 黄新友殷佳高春华岳振星李军
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products