Diatomite plate and processing method thereof

A production method and technology of diatomite, which is applied in the field of interior decoration materials, can solve the problems of diatomite board component configuration and production process that have not been reported in the literature and have no practical application, are not easy to cut for building construction, and the weight of the board is too heavy. , to achieve scientific and reasonable production methods, reliable plate structure and good quality

Inactive Publication Date: 2016-08-24
NORTHEAST DIANLI UNIVERSITY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese Patent Publication No.: CN103880349A discloses a method for manufacturing diatomite cement boards. The boards produced by this method are not only heavy in weight, but also too hard to cut for construction.
So far, there are no literature reports and practical applications on the detailed composition configuration and manufacturing process of diatomite boards.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: the manufacture method of a kind of diatomite plate of embodiment 1, comprises the following steps:

[0020] 1) Preparation materials:

[0021] 55kg of natural diatomite, 4kg of cement, 3kg of kaolin of 325-500 mesh, 5kg of attapulgite of 325-1000 mesh, 5kg of sepiolite mineral powder of 200-320 mesh, 8kg of bentonite of 325-1000 mesh, and expanded pearl of 200-500 mesh 8kg of rock powder, 4kg of natural flax fiber with a length of 2-3cm, 0.5kg of 80-100 mesh hypromellose powder, 0.1kg of emulsified silicone oil, and 10kg of water are placed in a mixer at a stirring speed of 1000-3000n / min for 20- Prepared in 25 minutes to obtain a homogeneously mixed material slurry;

[0022] 2) Molding:

[0023] The material slurry in step 1) is filtered and dehydrated in the fourdrinier machine, the water content is ≤20%, and the blank is opened into a blank with a thickness of 1-2cm;

[0024] 3) Cut and dry:

[0025] Cut the blank obtained in step 2) into plates wi...

Embodiment 2

[0026] Embodiment 2: the manufacture method of a kind of diatomite plate of embodiment 2, comprises the following steps:

[0027] 1) Preparation materials:

[0028] 60kg of natural diatomite, 5kg of cement, 4kg of kaolin of 325-500 mesh, 8kg of attapulgite of 325-1000 mesh, 4kg of sepiolite mineral powder of 200-320 mesh, 9kg of bentonite of 325-1000 mesh, expanded pearl of 200-500 mesh 9kg of rock powder, 2kg of natural flax fiber with a length of 2-3cm, 0.7kg of 80-100 mesh hypromellose powder, 0.3kg of emulsified silicone oil, and 13kg of water are placed in a mixer at a stirring speed of 1000-3000n / min for 20- Prepared in 25 minutes to obtain a homogeneously mixed material slurry;

[0029] 2) Molding:

[0030] The material slurry in step 1) is filtered and dehydrated in the fourdrinier machine, the water content is ≤20%, and the blank is opened into a blank with a thickness of 1-2cm;

[0031] 3) Cut and dry:

[0032] Cut the blank obtained in step 2) into plates with a...

Embodiment 3

[0033] Embodiment 3: the manufacture method of a kind of diatomite plate of embodiment 3, comprises the following steps:

[0034] 1) Preparation materials:

[0035] 65kg of natural diatomite, 6kg of cement, 4kg of kaolin of 325-500 mesh, 10kg of attapulgite of 325-1000 mesh, 3kg of sepiolite mineral powder of 200-320 mesh, 10kg of bentonite of 325-1000 mesh, expanded pearl of 200-500 mesh 10kg of rock powder, 5kg of natural flax fiber with a length of 2-3cm, 1kg of 80-100 mesh hypromellose powder, 0.5kg of emulsified silicone oil, and 15kg of water are placed in a mixer at a stirring speed of 1000-3000n / min for 20-25min Prepare a homogeneously mixed material slurry;

[0036] 2) Molding:

[0037] The material slurry in step 1) is filtered and dehydrated in the fourdrinier machine, the water content is ≤20%, and the blank is opened into a blank with a thickness of 1-2cm;

[0038] 3) Cut and dry:

[0039] Cut the blank obtained in step 2) into plates with a size of 1200mm×600...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a processing method for a diatomite plate. The processing method is characterized by including the steps of preparing materials, wherein natural diatomite, cement, kaolin, attapulgite, sepiolite mine powder, bentonite, expanded perlite powder, natural linen fibers, hydroxypropyl methylcellulose powder, emulsified silicone oil and water are stirred according to the amount, and evenly-mixed material slurry is prepared; forming, wherein the prepared material slurry is subjected to water filtering and dewatered in a fourdrinier-wire salvaging machine, and a blank is prepared; cutting and drying, wherein the blank is cut into a plate with the size of 1,200 mm*600 mm to be dried, cooling is carried out at the room temperature, and the diatomite base plate is prepared. The method is scientific and reasonable, the weight of the made diatomite plate is light, cutting is easy to achieve, indoor decoration and indoor construction are convenient, and indoor environmental protection can be achieved.

Description

technical field [0001] The invention belongs to the technical field of interior decoration materials, and relates to a diatomite board and a manufacturing method thereof. Background technique [0002] At present, various decorative materials made of diatomite as the main raw material have increasingly become the main trend of the development of modern interior decoration materials, and have been widely used in various interior decoration and decoration. Modern healthy life brings security. Chinese Patent Publication No.: CN103880349A discloses a method for manufacturing a diatomite cement board. The board manufactured by this method is not only heavy in weight, but also too hard to cut for construction. Chinese Patent Publication No.: CN105130331A discloses the component configuration of a lightweight diatomite board, and does not involve the production process. So far, there are no literature reports and practical applications on the detailed composition configuration and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B14/04C04B14/08C04B14/10C04B14/18C04B16/02C04B24/38C04B24/42
CPCC04B28/02
Inventor 刘晓林
Owner NORTHEAST DIANLI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap