A kind of weekly disposable peelable armor glue and preparation method thereof

A technology of armor and methyl, which is applied in the field of peelable armor glue and its preparation, which can solve the problems of injury, skin burn, undisclosed health and environmental protection glue, etc., to achieve easy peeling or tearing, Excellent wear resistance and fullness, the effect of improving the problem of easy breakage

Active Publication Date: 2018-06-12
LES FINS NETWORK TECH
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nail polish is very irritating, and it also has a certain burning sensation and injury when it touches the skin.
Simultaneously, in the prior art, there is no health-friendly, easy-to-peel or tear-off armor glue disclosed in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of weekly disposable peelable armor glue and preparation method thereof
  • A kind of weekly disposable peelable armor glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0109] The peelable armor adhesive for weekly throwing contains the following components in parts by weight: 11,14-dioxa-2,9-diazaheptadecane-16-enoic acid-4,4,6,16-tetramethyl - 40 parts of 10,15-dioxo-2-[(2-methyl-1-oxo-2-propenyl) oxo] ethyl ester;

[0110] 0.01 part of compound of formula I;

[0111] 28 parts of acrylate oligomer;

[0112] 2.8 parts of 1-hydroxycyclohexyl phenyl ketone;

[0113] 2.6 parts of (2,4,6-trimethylbenzoyl) bisphenylphosphine oxide;

[0114] 10 parts of hydroxyethyl methacrylate.

[0115] After the above ingredients are mixed, stir at high speed and mix evenly to make weekly throwable peelable and tearable armor glue.

Embodiment 2

[0117] The peelable armor adhesive for weekly throwing contains the following components in parts by weight: 11,14-dioxa-2,9-diazaheptadecane-16-enoic acid-4,4,6,16-tetramethyl - 35 parts of 10,15-dioxo-2-[(2-methyl-1-oxo-2-propenyl) oxo] ethyl ester;

[0118] 0.02 part of compound of formula I;

[0119] 23 parts of acrylate oligomer;

[0120] 2.2 parts of 1-hydroxycyclohexyl phenyl ketone;

[0121] 2.2 parts of (2,4,6-trimethylbenzoyl) bisphenylphosphine oxide;

[0122] 14 parts of hydroxyethyl methacrylate.

[0123] After the above ingredients are mixed, stir at high speed and mix evenly to make weekly throwable peelable and tearable armor glue.

Embodiment 3

[0125] The peelable armor adhesive for weekly throwing contains the following components in parts by weight: 11,14-dioxa-2,9-diazaheptadecane-16-enoic acid-4,4,6,16-tetramethyl -50 parts of 10,15-dioxo-2-[(2-methyl-1-oxo-2-propenyl)oxy]ethyl ester;

[0126] 0.03 part of compound of formula I;

[0127] 30 parts of acrylate oligomer;

[0128] 3.2 parts of 1-hydroxycyclohexyl phenyl ketone;

[0129] 3.2 parts of (2,4,6-trimethylbenzoyl) bisphenylphosphine oxide;

[0130] 9 parts of hydroxyethyl methacrylate.

[0131] After the above ingredients are mixed, stir at high speed and mix evenly to make weekly throwable peelable and tearable armor glue.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a strippable nail-protecting glue for weekly use. The strippable nail-protecting glue comprises, by weight, 35 to 50 parts of 11,14-diox-2,9-diazaheptadecane-16-gadoleic acid-4,4,6,16-tetramethyl-10,15-dioxo-2-[(2-methyl-1-oxo-2-allyl)oxo]ethyl ester, 0.01 to 0.05 part of a compound as shown in a formula I, 23 to 30 parts of acrylate oligomer, 2.2 to 3.2 parts of 1-hydroxycyclohexyl phenyl ketone, 2.2 to 3.2 parts of phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide, 9 to 14 parts of hydroxylethyl methacrylate. The nail-protecting glue provided by the invention can be cured to form a film only through LED light curing for 1 to 2 min, and has a full color and good luster and durability, and the lasting time of the glue reaches one to two weeks; a polish removing solution and wrapping with tinfoil are not needed in removing the nail-protecting glue, and the nail-protecting glue is not removed via a nail-beautifying pusher or abraded via a filling strip; and in removal of the nail-protecting glue, the glue can be integrally and easily stripped, so the glue has nail nursing effect and exerts strengthening and protection effect on fragile nails.

Description

technical field [0001] The invention relates to the field of cosmetic synthesis, in particular to a disposable peelable armor glue and a preparation method thereof. Background technique [0002] Nail gel is a very popular cosmetic product among women of all ages. Beauty lovers apply it on their nails to make them colorful and shiny. At present, there are many brands of armor glue on the market, good and bad. [0003] CN102908266A (2013-2-6) announced a kind of environmental protection nail polish and preparation method thereof, described environmental protection nail polish comprises emulsion, film-forming agent, water-based environmental protection colorant and deionized water; Wherein, the unit of described emulsion preparation The body includes butyl acrylate, styrene, methacrylic acid and vinyl hydroxy silicone oil; the initiator is azobisisobutyronitrile. Although the patent claims that its nail polish is an environmentally friendly nail polish, it is not. [0004] C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/891A61K8/81A61K8/86A61K8/49A61K8/73A61K8/55A61K8/37A61Q3/02
Inventor 赵明
Owner LES FINS NETWORK TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com