Waterborne epoxy anticorrosive antirust paint and preparation method thereof

An anti-corrosion and anti-rust, water-based epoxy technology, applied in the direction of anti-corrosion coatings, fire-proof coatings, coatings, etc., to achieve high adhesion, easy access to raw materials, and better anti-corrosion effects

Active Publication Date: 2016-07-27
卢朝霞
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on the combined use of water-based zinc phosphate and aluminum tripolyphosphate as anti-corrosion fillers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne epoxy anticorrosive antirust paint and preparation method thereof
  • Waterborne epoxy anticorrosive antirust paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A water-based epoxy anti-corrosion and anti-rust paint, based on water-based epoxy emulsion, adding various pigments, fillers and additives, the components and their mass percentages are as follows:

[0020] components

Mass percentage content

Waterborne Epoxy Emulsion

54.0％

Aqueous Zinc Phosphate

6.0％

Modified aluminum tripolyphosphate

3.0％

Rutile Titanium Dioxide

10.0％

Coalescent

2.0％

Water-based defoamer

1.0％

Thickener SN-636

2.0％

Wetting agent PE-100

2.0％

Bactericidal preservatives

2.0％

Anti-flash rust agent

2.0％

Dispersant 5040

1.5％

leveling agent

2.5％

Deionized water

12.0％

[0021] According to the preparation method of the water-based epoxy anti-corrosion and anti-rust paint, according to the mass percentage content, the modified aluminum tripolyphosphate and the water-based zinc phosphate are first mixed...

Embodiment 2

[0024] A water-based epoxy anti-corrosion and anti-rust paint, based on water-based epoxy emulsion, adding various pigments, fillers and additives, the components and their mass percentages are as follows:

[0025] components

[0026] The preparation method of described water-based epoxy anti-corrosion and rust-proof paint and the preparation method of water-based epoxy emulsion are the same as embodiment 1.

Embodiment 3

[0028] A water-based epoxy anti-corrosion and anti-rust paint, based on water-based epoxy emulsion, adding various pigments, fillers and additives, the components and their mass percentages are as follows:

[0029]

[0030]

[0031] The preparation method of described water-based epoxy anti-corrosion and rust-proof paint and the preparation method of water-based epoxy emulsion are the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water resistanceaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterborne epoxy anticorrosive antirust paint. With a waterborne epoxy elusion as a matrix, a plurality of pigment fillers and assistants, the waterborne epoxy anticorrosive antirust paint comprises a waterborne epoxy emulsion, water-based zinc phosphate, modified aluminum triphosphate, rutile titanium dioxide, a coalescing agent, a water-based defoamer, a thickener SN636, a wetting agent PE-100, a fungicidal preservative, a flash rusting agent, a dispersing agent 5040, a flatting agent and deionized water. The waterborne epoxy anticorrosive antirust paint is environmentally friendly; the raw materials are low in price; the preparation process is simple; meanwhile, the salt-water resistance is excellent; the adhesive force is high; and the flash rusting effect is good.

Description

technical field [0001] The invention belongs to the technical field of antirust paint, in particular to a water-based epoxy anticorrosion and antirust paint and a preparation method thereof. Background technique [0002] Traditional solvent-based antirust coatings mainly use organic solvents as the dispersion medium. Therefore, a large amount of organic compounds, namely Volatile Organic Composition (VOC for short), will volatilize in the process of preparation and use. The volatilization of VOC is a potential threat to the living environment and human health. On the other hand, the price of crude oil has risen sharply, which has forced the price of oil-based paints to increase continuously, and the cost of raw materials has also continued to increase. Therefore, scholars and researchers from various countries have gradually shifted their research focus from oil-based paints to water-based paints. [0003] Water-based coatings use water as a solvent (or as a dispersion me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D5/08C09D7/12C08F283/10C08F212/08C08F220/14C08F220/18
CPCC08F283/10C08K3/22C08K3/32C08K13/06C08K2003/2241C08K2003/327C08K2003/328C09D5/084C09D5/18C09D151/08C08F212/08
Inventor 卢朝霞叶斌王立升刘宇恒黄伊琳黄幸顾传君刘瑶
Owner 卢朝霞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More