Rosin glycerin ester production method

A technology of rosin glyceride and production method, which is applied in the field of deep processing of rosin, can solve the problems of low purity of rosin glyceride and restrictions on popularization and application of rosin glyceride, and achieve the effect of high softening point

Active Publication Date: 2016-07-13
FINJET CHEM IND LTD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The purity of the rosin glyceride that this method makes is generally low, makes the popularization and application of rosin glyceride restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This rosin glyceride comprises the following preparation steps:

[0020] A, raw material 100kg rosin is evacuated and decompressed and distilled to obtain refined rosin;

[0021] B. In the stirring state, put the refined rosin obtained in step A into the reaction kettle, and add 0.0001kg of tetraethyl orthosilicate, 5kg of hydroquinone, 15kg of glycerin and 0.02kg of sodium acetate in sequence, and then Under pressure, heated to 220°C, stirred at constant temperature, and reacted for 2 hours;

[0022] C. Put the material obtained in step B into the distillation tower, and put 0.0001kg of anthraquinone and 0.001kg of 4,4`-thiobis(6-tert-butyl-3-methylphenol), and then Distillation is carried out under the conditions of 0 MPa and temperature of 280°C to obtain rosin glyceride.

[0023] The softening point of the rosin glyceride prepared in this example is as high as 120° C., and the purity is as high as 99%.

Embodiment 2

[0025] This rosin glyceride comprises the following preparation steps:

[0026] A, raw material 100kg rosin is evacuated and decompressed and distilled to obtain refined rosin;

[0027] B. In a stirring state, put the refined rosin obtained in step A into the reactor, and add 0.00016 kg of tetraethyl orthosilicate, 6 kg of hydroquinone, 25 kg of glycerin and 0.017 kg of sodium acetate in sequence, and then Under the pressure of MPa, heat to 200°C, stir at constant temperature, and react for 4 hours;

[0028] C. Put the material obtained in step B into the distillation tower, and put 0.00016kg of anthraquinone and 0.0015kg of 4,4`-thiobis(6-tert-butyl-3-methylphenol), and then Distillation is carried out under the conditions of 0.01MPa and 270°C to obtain rosin glyceride.

[0029] The softening point of the rosin glyceride prepared in this example is as high as 125° C., and the purity is as high as 99.1%.

Embodiment 3

[0031] This rosin glyceride comprises the following preparation steps:

[0032] A, raw material 100kg rosin is evacuated and decompressed and distilled to obtain refined rosin;

[0033] B. In the stirring state, put the refined rosin obtained in step A into the reaction kettle, and add 0.0002kg of tetraethyl orthosilicate, 8kg of hydroquinone, 20kg of glycerin and 0.01kg of sodium acetate in sequence, and then Under the pressure of MPa, heat to 205°C, stir at constant temperature, and react for 3 hours;

[0034] C. Put the material obtained in step B into the distillation tower, and put 0.0002kg of anthraquinone and 0.002kg of 4,4`-thiobis(6-tert-butyl-3-methylphenol), and then Distillation is carried out under the conditions of 0.005MPa and 205°C to obtain rosin glyceride. .

[0035] The softening point of the rosin glyceride prepared in this example is as high as 120° C., and the purity is as high as 99.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of deep processing or rosin and discloses a rosin glycerin ester production method.Rosin glycerin ester is prepared from, by weight, 100 parts of rosin, 0.0001-0.0002 part of anthraquinone, 0.0001-0.0002 part of tetraethoxysilane, 5-8 parts of hydroquinone, 0.001-0.002 part of 4,4'- thio-bis(6-tert-butyl-3-methyl phenol), 15-25 parts of glycerin and 0.01-0.02 part of sodium acetate.The rosin glycerin ester production method includes: refining the rosin, adding the tetraethoxysilane, the hydroquinone, the glycerin and the sodium acetate under the condition of stirring, and reacting under a specific pressure and at a specific temperature; adding the anthraquinone and the 4,4'- thio-bis(6-tert-butyl-3-methyl phenol), and distilling under a specific pressure and at a specific temperature.The rosin glycerin ester produced according to the method has the advantages of high softening point and high purity.

Description

technical field [0001] The invention belongs to the technical field of rosin deep processing, and in particular relates to a production method of rosin glyceride. Background technique [0002] Rosin glyceride is an irregular transparent block, flake or granular solid, which has good oxidation resistance and thermal stability, aging resistance, and good compatibility with polymer materials (NR, CR, SBR, SIS, EVA, etc.) , Good initial adhesion, can be used in yellow glue to improve initial adhesion, and can also be used as hot-melt pressure-sensitive adhesive, oil-soluble pressure-sensitive adhesive, self-adhesive, laminating adhesive, EVA hot-melt adhesive, polyamide hot-melt adhesive Tackifying resins for melt adhesives, sealants, varnishes, bookbinding adhesives, pipe adhesives, laminating adhesives, decorative adhesives, label adhesives, tape adhesives, etc. [0003] The traditional preparation method of rosin glyceride is that rosin or light-colored rosin is modified and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09F1/04
CPCC09F1/04
Inventor 叶旗周卓瑜
Owner FINJET CHEM IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com