Sanitary ceramics slip and preparation technology thereof

A technology for sanitary ceramics and preparation process, applied in the field of sanitary ceramics, can solve the problems of lower product qualification rate, high sintering temperature, easy deformation during sintering, etc., and achieve the effects of long cracking time, high sintering qualification rate, and not easy to crack.

Active Publication Date: 2016-06-29
福建科福材料有限公司
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The sintering temperature of the slurry made of this raw material is as high as 1200-1280 degrees. During the sintering process, the energy consumption is relatively large, the loss on ignition rate is high, and the product is easily deformed; in addition, the use of too many hard materials makes the plasticity worse. The strength is reduced, and the product qualification rate is reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sanitary ceramics slip and preparation technology thereof
  • Sanitary ceramics slip and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] In order to make the technical problems, technical solutions and beneficial effects to be solved by the present invention clearer and clearer, the present invention will be further described in detail below in conjunction with the embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0020] The sanitary ceramic mud of the present invention is mainly composed of the following raw materials in parts by weight: illite clay 30-70, kaolin 5-15, ball clay 6-14, potassium feldspar 8-13, pyrophyllite 5-10, sericite 5 -10, dolomite 0.1-3, water 40-45.

[0021] Among them, the illite-type clay is made of illite-type china clay through weathering, crushing, cone beating, elutriation, sieving, iron removal, decay, and pressure filtration in sequence, and the average weight of the illite-type clay obtained after treatment The particle size is 4.0-5.5um, and particles wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses sanitary ceramics slip and a preparation technology thereof. The sanitary ceramics slip mainly comprises, by weight, 30-70 parts of illite-structure clay, 5-15 parts of kaolin, 6-14 parts of ball clay, 8-13 parts of potassium feldspar, 5-10 parts of pyrophyllite, 5-10 parts of sericite, 0.1-3 parts of dolomite and 40-45 parts of water. Sanitary ceramics prepared from the sanitary ceramics slip are low in firing temperature, little in energy consumption and high in strength, and slip casting qualified rate, semi-finished product qualified rate and firing qualified rate can reach 98%, 96% and 92% respectively.

Description

technical field [0001] The invention relates to the field of sanitary ceramics, in particular to mud for sanitary ceramics and a preparation process thereof. Background technique [0002] The main raw materials of the existing sanitary ceramic mud are potassium feldspar, quartz and kaolin. The sintering temperature of the slurry made of this raw material is as high as 1200-1280 degrees. During the sintering process, the energy consumption is large, the loss on ignition rate is high, and the product is easy to deform when fired; in addition, the use of too many hard materials makes the plasticity worse. The strength is reduced, and the product qualification rate is reduced. Contents of the invention [0003] In order to solve the above problems, the present invention provides a sanitary ceramic slurry with illite-type clay as the main raw material and its preparation process. The sanitary ceramics made from the slurry have low firing temperature, low energy consumption and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/04
CPCC04B33/04C04B33/13C04B35/62605C04B2235/321C04B2235/3463C04B2235/3472C04B2235/96
Inventor 林培灿陈维尧张向卫
Owner 福建科福材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com