Flame-retardant and antibacterial polyester fiber for mattress filling and production method thereof

A polyester fiber, a production method technology, applied in the direction of fire-retardant and flame-retardant filament manufacturing, fiber processing, fiber type, etc., can solve the problems of poor flame-retardant performance, weakened flame-retardant performance, poor flame-retardant sponge, etc. performance and comfort, improved mechanical properties, good thermal insulation

Active Publication Date: 2017-12-05
福建亿泰隆化纤股份有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

People's research on the modification of polyester fiber has never stopped, especially the research on flame-retardant polyester fiber. The polyester fiber before modification is easy to melt and decompose when heated, and it will melt and drip when burned. The key to polyester fiber lies in the use of flame retardants, and the key technical solutions for improving the flame retardant properties of most flame retardant polyester fibers with good performance are still kept secret. At present, the flame retardant modification methods of polyester fibers mainly include copolymerization Flame retardant modification, blending flame retardant modification, grafting flame retardant modification and post-finishing flame retardant modification, copolymerization flame retardant modification means adding flame retardants and other additives during the polymerization of polyester fibers to achieve Flame retardant effect, but this method is prone to side reactions, and has high requirements for the stability of flame retardants; blending flame retardant modification, that is, adding flame retardant additives to the spinning melt; grafting flame retardant modification The permanent process is more complicated, not easy to master, and the research and development period is long, and the investment is relatively large; after flame-retardant finishing, the polyester fiber is impregnated with a finishing agent to endow it with flame-retardant properties. The disadvantage is that many flame-retardant polyester fibers after finishing, Its flame retardant properties will gradually weaken with the number of washes and use time
[0003] Many traditional mattresses use sponge as a filling, because the sponge is soft and comfortable, and has good warmth retention. However, the flame retardancy of the sponge is poor, and the burning speed is extremely fast, and the cost of flame-retardant cotton is relatively high.
At present, polyester fiber is widely used in clothing fillings and other fields, and it is also widely used in the field of mattresses. When it is used as mattress filling, it not only needs to have the comfort and warmth of sponge, but also needs to have good flame retardancy. , but at present, most polyester fiber mattresses have poor flame retardancy and some do not even have flame retardancy. Polyester fiber mattresses are easy to breed bacteria and mildew in humid environments, and some even have mildew spots on the bottom. Therefore, the research on flame-retardant and antibacterial polyester fibers for mattresses is of great significance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant and antibacterial polyester fiber for mattress filling and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for making a flame-retardant and antibacterial polyester fiber for mattress filling, comprising the following steps:

[0023] Step 1, raw material treatment: vacuum-dry PET resin at 95°C for 35 hours to obtain PET resin dry material, vacuum-dry nano-montmorillonite at 65°C for 4 hours to obtain nano-montmorillonite dry material, and dry nano-silica powder at 115 Vacuum drying at ℃ for 32 hours to obtain dry nano-silica powder;

[0024] Step 2, PET resin modification: according to the number of parts by mass, after mixing and stirring 55 parts of PET resin dry material, 1.25 parts of nanometer montmorillonite dry material and 0.6 part of nano silicon micropowder dry material, then add 0.13 part of six ( 4-formylphenoxy)cyclotriphosphazene, continue to mix and stir evenly, granulate at 242°C, and then melt-spin at 292°C to obtain polyester fibers, wherein the mixing and stirring use a high-speed mixer Carry out, stirring speed is 900r / min;

[0025] Step 3, poly...

Embodiment 2

[0028] A method for making a flame-retardant and antibacterial polyester fiber for mattress filling, comprising the following steps:

[0029] Step 1, raw material treatment: vacuum-dry PET resin at 90°C for 35 hours to obtain PET resin dry material, vacuum-dry nano-montmorillonite at 60°C for 5 hours to obtain nano-montmorillonite dry material, and dry nano-silica powder at 110 Vacuum drying at ℃ for 35 hours to obtain dry nano-silica powder;

[0030] Step 2, PET resin modification: according to the number of parts by mass, after mixing and stirring 50 parts of PET resin dry material, 1.2 parts of nano-montmorillonite dry material and 0.4 part of nano-silica powder dry material, and then adding 0.1 part of six ( 4-formylphenoxy)cyclotriphosphazene, continue to mix and stir evenly, granulate at 240°C, and then melt-spin at 290°C to obtain polyester fibers, wherein the mixing and stirring uses a high-speed mixer Carry out, stirring speed is 800r / min;

[0031] Step 3, polyester...

Embodiment 3

[0034] A method for making a flame-retardant and antibacterial polyester fiber for mattress filling, comprising the following steps:

[0035] Step 1, raw material treatment: vacuum-dry PET resin at 100°C for 30 hours to obtain PET resin dry material, vacuum-dry nano-montmorillonite at 65°C for 3 hours to obtain nano-montmorillonite dry material, and dry nano-silica powder at 120 Vacuum drying at ℃ for 30 hours to obtain dry nano-silica powder;

[0036] Step 2, PET resin modification: according to the number of parts by mass, after mixing and stirring 60 parts of PET resin dry material, 1.3 parts of nanometer montmorillonite dry material and 0.8 part of nano silicon micropowder dry material, then add 0.15 part of six ( 4-formylphenoxy)cyclotriphosphazene, continue to mix and stir evenly, granulate at 245°C, and then melt-spin at 295°C to obtain polyester fibers, wherein the mixing and stirring use a high-speed mixer Carry out, stirring speed is 1000r / min;

[0037] Step 3, pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to flame-retardant and antibacterial polyester fiber for mattress filling and a manufacturing method of the fiber, and belongs to the technical field of polyester fiber fillers. The manufacturing method of the flame-retardant and antibacterial polyester fiber for mattress filling comprises the steps of step I, raw material treatment; step II, PET resin modification; step III, polyester fiber modification; step IV, loosening. According to the flame-retardant and antibacterial polyester fiber for mattress filling and the manufacturing method of the fiber, blending modification of nano-montmorillonite, nano silica micro powder, HAPCP and PET resin is adopted, the polyester fiber with permanent flame retardant performance is prepared, and then the polyester fiber is endowed with excellent antibacterial property and comfort through immersion treatment of treating fluid. Besides, the flame-retardant and antibacterial polyester fiber for mattress filling has excellent heat retention property, mildew resistance and antibacterial activity, and at the same time, the mechanical property of the polyester fiber is improved greatly.

Description

technical field [0001] The invention belongs to the technical field of polyester fiber fillers, and in particular relates to a flame-retardant and antibacterial polyester fiber for mattress filling and a production method thereof. Background technique [0002] Polyester, that is, polyethylene terephthalate, polyester fiber is widely used in the field of textiles because of its many advantages, and has become the most widely used and most consumed fiber raw material in the field of textiles. People's research on the modification of polyester fiber has never stopped, especially the research on flame-retardant polyester fiber. The polyester fiber before modification is easy to melt and decompose when heated, and it will melt and drip when burned. The key to polyester fiber lies in the use of flame retardants, and the key technical solutions for improving the flame retardant properties of most flame retardant polyester fibers with good performance are still kept secret. At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/62D01F1/07D01F1/10D06M13/144D06M101/32
CPCD01F1/07D01F1/103D01F6/62D06M13/144D06M2101/32
Inventor 施文强
Owner 福建亿泰隆化纤股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com