Mugwort fiber and preparation method thereof

A technology of wormwood fiber and wormwood, applied in the field of materials, to achieve the effects of treating and preventing human sub-health, strengthening health care functions, preventing and treating high blood pressure

Inactive Publication Date: 2016-03-30
JIANGSU TRYD TEXTILE RES INST +1
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But also rarely report for the research of wormwood fiber, especially the research of wormwood fiber for weaving

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: get the diameter and leaf part of wormwood, wash to remove impurities such as soil and dust on the diameter and leaves, and dry the diameter and leaves after the removal of impurities in an oven at a low temperature at a temperature of 40°C-60°C. The time is 6-12 hours, the diameter and leaves after air-drying are put into a mechanical pulverizer, and fully pulverized into wormwood powder, and the wormwood powder and sodium dodecylbenzenesulfonate, hydroxymethyl cellulose, N-methyl Morpholine-N-oxide, anti-oxidant PG and water are mixed in a certain proportion, fully stirred and mixed at 60-80°C, and then the mixture is filtered, defoamed, and wormwood fiber is spun by wet spinning.

Embodiment 2

[0017] Embodiment 2: Take the diameter and leaf part of Artemisia wormwood, wash with water to remove impurities such as soil and dust on the diameter and leaves, and dry the diameter and leaves after the removal of impurities in an oven at a low temperature at a temperature of 60°C-80°C. The time is 4-8 hours, the diameter and leaves after air-drying are put into a mechanical pulverizer, and fully pulverized into wormwood powder, and the wormwood powder and sodium dodecylbenzenesulfonate, hydroxypropyl cellulose, N-methyl Morpholine-N-oxide, anti-oxidant PG and water are mixed in a certain proportion, fully stirred and mixed at 60-80°C, and then the mixture is filtered, defoamed, and wormwood fiber is spun by wet spinning.

Embodiment 3

[0018] Embodiment 3: get the diameter and leaf part of wormwood, wash to remove impurities such as soil and dust on the diameter and leaves, and dry the diameter and leaves after the removal of impurities in an oven at a low temperature at a temperature of 60°C-80°C. The time is 4-8 hours, and the diameter and leaves after air-drying are put into a mechanical pulverizer and fully pulverized into wormwood powder. Morpholine-N-oxide, antioxidant PG and water are mixed in a certain proportion, fully stirred and mixed at 60-80°C, and then the mixture is filtered, defoamed, and wormwood fiber is spun by dry spinning.

[0019] The wormwood fiber of the invention has excellent moisture absorption and moisture conductivity, soft hand feeling, biodegradable and pollution-free; and the wormwood fiber has the functionality of the wormwood and the health care property for the human body. Wormwood fiber can be spun alone or blended with other fibers. In the blended yarn, the content of wor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of mugwort fiber comprising following steps: 1) washing to remove contaminant such as mud and dust on stems and leaves of the mugwort; 2) air drying at low temperature so that volatile oil of the mugwort is kept during water removal; 3) mechanical crushing completely using physical method; 4) mugwort pulping by fully mixing mugwort with dispersing agent and solvent, etc.; 5) spinning by dry method and wet method and extrusion spinning; 6) washing; 7) drying; 8) cutting. The mugwort fiber prepared by the invention has good moisture absorption and moisture transmitting performance, soft hand feel, bacteria resistance and bacteriostasis, expelling insects and mosquitoes, peculiar smell removing, and blood circulation promoting functions and health care property.

Description

technical field [0001] The invention belongs to the field of materials, in particular to a natural plant fiber. Background technique [0002] Wormwood is a perennial herb. Wormwood is closely related to the lives of Chinese people. On the occasion of the Dragon Boat Festival, people always put wormwood at home to "ward off evil spirits". The erect stem is 80-250 cm high, with obvious longitudinal ribs, brown or taupe, slightly lignified base, herbaceous upper part, and a few short branches, 3-5 cm long; stems and branches are covered by gray spider Silky pilose. The leaves are thick and papery, covered with off-white pubescence on the top, and have white glandular spots and small pits, and the back is densely covered with off-white spider silk-like dense downy; the basal leaves are long-stalked and withered during flowering; the leaves on the lower part of the stem are nearly round or wide Oval, pinnately parted, with 2-3 lobes on each side, lobes elliptic or obovate-oblon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01B1/10D01D1/00
Inventor 凌良仲赵殿栋刘松陆灯红孔劲松
Owner JIANGSU TRYD TEXTILE RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products