Fluorescent polyurethane emulsion based on diketopyrrolopyrrole derivative

A polyurethane emulsion and fluorescence technology, which is applied in the field of fluorescent polyurethane emulsion, can solve the problems of weak fluorescence intensity of fluorescent urethane emulsion, low molecular weight of fluorescent urethane emulsion, and narrow application field.

Active Publication Date: 2016-03-30
LILY GRP CO LTD +1
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the main disadvantages of the existing fluorescein urethane emulsion based on 1,8-naphthalene diimide derivatives are: ① the molecular weight of the fluorescein urethane emulsion is low; ② the fluorescence intensity of the fluorescein urethane emulsion is not strong
This will lead to a narrow field of application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorescent polyurethane emulsion based on diketopyrrolopyrrole derivative
  • Fluorescent polyurethane emulsion based on diketopyrrolopyrrole derivative
  • Fluorescent polyurethane emulsion based on diketopyrrolopyrrole derivative

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038]

[0039] (1) Under the protection of dry nitrogen, place 0.0001mol of the compound shown in formula Ia and 15mol of dehydrated diphenylmethane diisocyanate (MDI) in a reactor with a temperature control device and a stirring device, stir and heat up to 60°C-80°C, keep in this state for 6 hours, cool, and dry to constant weight to obtain mixture a;

[0040] (2) Add 2 mol of polypropylene glycol (Mw=500 to 3,000), 1 mol of 2,2-dimethylol propionic acid (DMPA), 1.5 mol of 1,4-butanediol and 0.001 mol of 0.2% dibutyltin dilaurate (Catalyst) added to the reaction with the above mixture a, stirred at 20°C to 30°C for 2 hours to 7 hours, then added 5mol triethanolamine to the reactor and stirred at 60°C to 70°C for at least 30 minutes, then added Stir and emulsify with water to obtain the target substance (abbreviated as "DPP-1WPU(A)"), whose fluorescence spectrum is shown in figure 1 ..

Embodiment 2

[0042]

[0043] (1) Under the protection of dry nitrogen, 0.001mol of the compound shown in formula Ib and 0.8mol of toluene-2,4-diisocyanate (TDI) after dehydration are placed in a reactor with a temperature control device and a stirring device, Stir and heat up to 60°C to 80°C, keep in this state for 6 hours, cool, and dry to constant weight to obtain mixture b;

[0044] (2) Add 0.1mol polypropylene glycol (Mw=500~3,000), 0.01mol DMPA, 1mol pentylene glycol and 0.076mol of 0.2% dibutyltin dilaurate (catalyst) to the reaction with the above mixture b, at 20°C Stir at ~30°C for 2 hours to 7 hours, then add 5mol triethylamine to the reactor and stir at 60°C to 70°C for at least 30 minutes, then add water to stir and emulsify to obtain the target product (abbreviated as "DPP-2WPU ”), and its fluorescence spectrum is shown in figure 1 ..

Embodiment 3

[0046]

[0047] (1) Under the protection of dry nitrogen, place 0.01mol of the compound shown in formula Ic and 3.8mol of MDI dehydrated in a reactor with a temperature control device and a stirring device, stir and heat up to 60°C to 80°C, and This state was maintained for 6 hours, cooled, and dried to constant weight to obtain a mixture c;

[0048] (2) 18mol polyethylene glycol (Mw=500~3,000), 1.8molDMPA, 35mol glycerol and 2.023mol of 0.2% dibutyltin dilaurate (catalyst) are added to the reaction of the above mixture c, 20 Stir at ℃~30℃ for 2 hours~7 hours, then add 6mol triethylamine to the reactor and stir at 60℃~70℃ for at least 30 minutes, then add water to stir and emulsify to obtain the target product (abbreviated as "DPP- 3WPU").

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fluorescenceaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fluorescent polyurethane emulsion, in particular to a fluorescent polyurethane emulsion based on a diketopyrrolopyrrole derivative. The fluorescent polyurethane emulsion has higher fluorescence intensity and higher molecular weight, and further, the fluorescence effect after film forming is better. The fluorescent polyurethane emulsion is more expected to be applied to the fields of anti-counterfeit marking, medical treatment, fluorescent paint and the like.

Description

technical field [0001] The invention relates to a fluorescent polyurethane emulsion, in particular to a fluorescent polyurethane emulsion based on diketopyrrolopyrrole derivatives. Background technique [0002] Fluorescent polymer material is a functional polymer material that emits fluorescence under ultraviolet light. In recent years, good progress has been made in the research and application of fluorescent sensors, drug carriers, fluorescent imaging, and fluorescent probes. Since the traditional water-based fluorescent polyurethane system is generally formed by blending fluorescent pigments and polyurethane emulsion, the stability of the system itself, the solvent elution resistance and the color fastness to light of the product are poor. [0003] Due to the poor compatibility between ordinary fluorescent pigment / dye molecules and polyurethane macromolecules, the method based on physical coating cannot completely prevent the migration and diffusion of fluorescent dye mol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/32
CPCC08G18/3844C08G18/6659C08G18/6692
Inventor 王利民胡阳王桂峰吴生英王峰田禾王振炎陈立荣黄卓
Owner LILY GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com