Preparation method of fat-dispersed niobium boride silicon carbide-carbon fiber friction material
A niobium boride silicon carbide and friction material technology, which is applied in the field of friction material preparation, can solve problems such as reduced friction performance and potential safety hazards, and achieve the effects of improving wear resistance and high manufacturing cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] (1) Set the density to 1.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 900°C. The molar ratio of propane gas: nitrogen is 1:4, the flow rate is controlled at 50ml / min, and the carburizing treatment is performed for 24 hours to obtain a carburized carbon fiber blanket. ;
[0020] (2) Immerse the above-mentioned carburized carbon fiber blanket into a grease slurry with a particle size of less than 0.3 μm and a content of 5% niobium boride, place it in an ultrasonic cleaner and fill it with niobium boride for 50 minutes, take it out and dry it to obtain a filled boride Niobium carbon fiber blanket, synthetic fat slurry is ethanol solution containing 5% synthetic fat;
[0021] (3) Pass the above-mentioned filled niobium boride carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 900°C, and the molar ratio of trichloromethylsilane gas: hydroge...
Embodiment 2
[0025] (1) Set the density to 0.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixture of propane gas and nitrogen at a temperature of 1000°C. The molar ratio of propane gas: nitrogen is 1:5, the flow rate is controlled at 350ml / min, and the carburizing treatment is performed for 18 hours to obtain a carburized carbon fiber blanket. ;
[0026] (2) Immerse the above-mentioned carburized carbon fiber blanket into a grease slurry with a particle size of less than 0.3 μm and a content of 12% niobium boride, place it in an ultrasonic cleaner and fill it with niobium boride for 40 minutes, take it out and dry it to obtain a filled boride Niobium carbon fiber blanket, synthetic fat slurry is an ethanol solution containing 12% synthetic fat;
[0027] (3) Pass the above-mentioned filled niobium boride carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 1000 °C, and the molar ratio of trichloromethylsilane gas: ...
Embodiment 3
[0031] (1) Set the density to 0.1g / cm 3 The graphitized carbon fiber blanket is passed into a mixed gas of propane gas and nitrogen at a temperature of 1100 ° C. The molar ratio of propane gas: nitrogen is 1: 6, the flow rate is controlled at 600ml / min, and the carburizing treatment is performed for 10 hours to obtain a carburized carbon fiber blanket. ;
[0032] (2) Immerse the above-mentioned carburized carbon fiber blanket in a synthetic grease slurry with a particle size of less than 0.3 μm and a content of 20% niobium boride, place it in an ultrasonic cleaner and fill it with niobium boride for 30 minutes, take it out and dry it to obtain a filled boride Niobium carbon fiber blanket, synthetic fat slurry is ethanol solution containing 20% synthetic fat;
[0033] (3) Pass the above-mentioned filled niobium boride carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 1100 °C, and the molar ratio of trichloromet...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap