Preparation method for colored eyeglass with colored coating

A spectacle lens and color technology, which is applied in the field of sunglass lens preparation, can solve the problems of affecting color consistency, difficulty in dyeing, and difficulty in achieving the depth of dyeing, so as to improve product performance and market competitiveness, reduce labor intensity and Stimulation by the solvent, fast dyeing effect

Active Publication Date: 2016-02-10
ZENNI OPTICAL
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to overcome some problems in the dyeing process, the current sun lenses are analyzed first, such as the sun lenses using the first method, which is dyed on the surface of the lens. The biggest problem of this method is that it is very different from the degree of polymerization of the monomers of the lens. The big relationship, the high degree of polymerization of the material makes it difficult to dye. The essential reason is that the degree of monomer polymerization is large, the gap between the monomers of the lens is small, and it is difficult for inorganic pigments to penetrate, which makes it difficult to achieve the depth of dyeing. At the same time It will also affect the consistency of the color
The sun lenses using the second method directly add pigments to monomers, such as PC materials. Since PC lenses are processed by injection molding, the pigments (particle diameter greater than 0.4 microns) can be directly entered into the mold through the screw of the injection molding machine. Finally, sun lenses are formed, but the monomers of other materials are produced by casting. This method requires that the pigments have good dispersion in the monomers, and at the same time, there is no or little filterability in the monomers. Only in this way can the color of the final lens be guaranteed, but this method has another defect, that is, when the sunglasses we wear have a prescription requirement, the lens at this time has a certain diopter, and the existence of this diopter causes the lens to be damaged. The thickness of the edge of the lens is not consistent with the thickness of the center. Even when the lens has astigmatism, the thickness of the edge will be different. In this case, the method of adding pigments to the body will have thick places and thin places. Defects of varying depth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for colored eyeglass with colored coating
  • Preparation method for colored eyeglass with colored coating
  • Preparation method for colored eyeglass with colored coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] As shown in the examples, the present invention is a method for preparing colored spectacle lenses with a coating, and the preparation method comprises the following steps:

[0037] (1) Dissolution of pigments or dyes: Dissolve 0.8-1g of Disperse Red in 50ml of deionized water, stir until completely dissolved, then set aside for later use, dissolve 1-2.8g of Disperse Yellow in 50ml of deionized water, stir until Dissolve completely, then put aside for use, dissolve 0.4-2.0g of Disperse Blue in 50ml of deionized water, stir until completely dissolved, then pour the dissolved Disperse Red solution, Disperse Yellow solution and Disperse Blue solution into a glass container , stir until completely dissolved, store the mixed solution of the three solutions at a temperature of 15 degrees and a humidity of 40% for 24 hours, and observe whether there is stratification and precipitation after 24 hours;

[0038] (2) Prepare the hardening solution to harden the substrate for the f...

Embodiment 1

[0044] The present invention is a kind of preparation method of the colored spectacle lens of coating coloring, and preparation method comprises the following steps:

[0045] (1) Dissolution of pigments or dyes: Dissolve 1g of Disperse Red in 50ml of deionized water, stir until completely dissolved, then set aside for later use, dissolve 1g of Disperse Yellow in 50ml of deionized water, stir until completely dissolved, then put Stand aside, dissolve 2g of disperse blue in 50ml of deionized water, stir until completely dissolved, then pour the dissolved disperse red solution, disperse yellow solution and disperse blue solution into a 2000ml glass container, stir until completely dissolved , store the mixed solution of the three solutions at a temperature of 15 degrees and a humidity of 40% for 24 hours. After 24 hours, observe whether there is stratification and precipitation;

[0046] (2) Prepare the hardening solution to harden the substrate for the first time: Take 150ml of ...

Embodiment 2

[0049] The present invention is a kind of preparation method of the colored spectacle lens of coating coloring, and this preparation method comprises the following steps:

[0050] (1) Dissolution of pigments or dyes: Dissolve 1g of Disperse Red in 50ml of deionized water, stir until completely dissolved, then set aside for later use, dissolve 1g of Disperse Yellow in 50ml of deionized water, stir until completely dissolved, then put Stand aside, dissolve 2g of disperse blue in 50ml of deionized water, stir until completely dissolved, then pour the dissolved disperse red solution, disperse yellow solution and disperse blue solution into a 2000ml glass container, stir until completely dissolved , store the mixed solution of the three solutions at a temperature of 15 degrees and a humidity of 40% for 24 hours. After 24 hours, observe whether there is stratification and precipitation;

[0051] (2) Prepare the hardening solution to harden the substrate for the first time: Take 150m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method for colored eyeglass with colored coating. The preparation method comprises the following steps that (1) a pigment or dye is dissolved; (2) a hardening solution is prepared to harden basic glass primarily; and (3) secondary hardening is carried out to obtain a finished product, namely, the eyeglass which is hardened and solidified in the step (2) is hardened at the surface at the temperature of 110 DEG C for 2 hours, cooled, detected and form the finished product if qualified. According to the method, the dye or pigment is directly added to the hardening solution, the solution is in the color to be dyed, the basic eyeglass is immersed in the hardening solution and hardened to form the colored eyeglass, the dye added into the hardening solution is controlled to achieve different colors and darkness, the method is fully automatic and does not need manual operation, the labor intensity as well as stimulation to a solvent are reduced, the dyeing speed is very high, and the efficiency is very high.

Description

technical field [0001] The invention belongs to the technical field of lens processing, and in particular relates to a method for preparing colored sunglass lenses with colored layers. Background technique [0002] At present, the materials used as lenses are allyl diglycol carbonate lenses with a refractive index of 1.499, acrylic lenses with a refractive index of 1.56, polyurethane lenses with a refractive index of 1.60 and 1.67, polycarbonate PC lenses, and 1.74 refractive index lenses. The lenses of the episulfide polymer, all these spectacle lenses are mainly realized by the following method when they are used as the lenses of sunglasses. First, the lenses are poured and solidified or injection molded through a glass mold or a plastic mold to obtain the molded lenses. The lens has all the characteristics required by optical lenses, and then the surface of the lens is dyed through the dyeing solution. The main component of the dyeing solution contains benzyl alcohol dyei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B1/10
Inventor 赵志刚
Owner ZENNI OPTICAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products