A kind of near-infrared absorption filter film and preparation method thereof

A near-infrared absorber and filter film technology, which is applied in chemical instruments and methods, pressure-sensitive films/sheets, film/sheet-shaped adhesives, etc., can solve problems such as difficult removal and cumbersome installation process, and achieve easy to install effects

Active Publication Date: 2018-08-31
HUBEI INST OF AEROSPACE CHEMOTECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The traditional design idea is to install a night vision compatible filter in the display or dashboard, which is not easy to move and disassemble after installation, and the installation process is cumbersome when some displays or dashboards without night vision compatible filters need to be installed.
There is no relevant literature report on this filter film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of near-infrared absorption filter film and preparation method thereof
  • A kind of near-infrared absorption filter film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Scratch-resistant coating solution preparation: Add 15 parts by weight of dipentaerythritol hexaacrylate (DPHA, Sartomer, USA) and 20 parts by weight of mixed diluent to 60 parts by weight of polyurethane acrylate (Sartomer, CN9006) resin (commercially available, toluene: propylene glycol methyl ether = 1:1), stir and mix evenly; add 5 parts by weight of a photoinitiator (Swiss Ciba, Irgacure 184) to the mixture, and stir evenly.

[0047] Composite adhesive layer coating solution preparation: 0.9 parts by weight of near-infrared absorber (0.3 parts by weight of EPOLIGHT TM 6661, absorption peak λ max =669nm, 0.3 parts by weight EPOLIGHT TM 4037, absorption peak λ max =743nm, 0.3 parts by weight EPOLIGHT TM 5587, absorption peak λ max =815nm, American Eprene Company) and 1.5 parts by weight of dispersant (Kerper, Kerper-602 in the United States) were added to 20.6 parts by weight of mixed diluent (commercially available dichloromethane: ethyl ketone = 1:1), stirred a...

Embodiment 2

[0054] Scratch-resistant layer coating solution preparation: to 50 parts by weight of polyurethane acrylate (Nippon Synthetic Chemical Company, brand 1700) resin, add 20 parts by weight of dipentaerythritol hexaacrylate (Sartomer, DPHA, USA) and 25 parts by weight of mixed Diluent (commercially available, toluene: propylene glycol methyl ether = 1:1), stirred and mixed uniformly; 5 parts by weight of photoinitiator (Swiss Ciba, Irgacure 184) was added to the mixed solution, and stirred evenly.

[0055] Composite adhesive layer coating solution preparation: 1 weight part of near-infrared absorber (0.5 weight part of EPOLIGHT TM 6661, absorption peak λ max =669nm, 0.5 parts by weight EPOLIGHT TM 3036, absorption peak λ max =773nm, American Eprene Company) and 1 weight part of dispersant (American Kerper, Kerper-602) were added to 20 weight parts of mixed diluent (commercially available dichloromethane: ethyl ketone = 1:1), stirred and mixed evenly; Add 70 parts by weight of...

Embodiment 3

[0062] Scratch-resistant coating solution preparation: Add 15 parts by weight of dipentaerythritol hexaacrylate (DPHA, Sartomer, USA) and 20 parts by weight of mixed diluent to 60 parts by weight of polyurethane acrylate (Sartomer, CN9006) resin (commercially available, toluene: propylene glycol methyl ether = 1:1), stir and mix evenly; add 5 parts by weight of a photoinitiator (Swiss Ciba, Irgacure 184) to the mixture, and stir evenly.

[0063] Composite glue layer coating liquid preparation: 0.5 weight part near-infrared absorber (0.25 weight part IR650, absorption peak λ max =798nm, 0.25 parts by weight IR852, absorption peak λ max =852nm Changchun Rainbow Technology Co., Ltd.) and 1 part by weight of dispersant (Kerper, Kerper-602 in the United States) were added to 21.5 parts by weight of mixed diluent (commercially available dichloromethane: methyl ethyl ketone = 1:1), stirred and mixed evenly; Add 70 parts by weight of polyurethane composite adhesive (Sanwo Aerospace, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a near-infrared absorption film filter and a preparation method and application thereof. The near-infrared absorption film filter comprises a transparent base material formed by compounding two layers of transparent films (2 and 4), a compound rubber layer is an adhesive layer (3) which contains a near-infrared absorbent and is 10-30 microns thick, one side of the transparent base material is coated with a scratch-resistant coating (1) which is 3-7 microns thick, the other side of the transparent base material is coated with a pressure-sensitive adhesive layer (5) which is 10-25 microns thick, and the surface of the pressure-sensitive adhesive layer is coated with a release film (6). The near-infrared absorption film filter has a night vision compatible function and a scratch resistant function, and can be easily mounted on the surfaces of such illuminating systems as LCD devices and instrument illuminating devices.

Description

technical field [0001] The invention relates to a near-infrared absorption filter film used for lighting systems such as liquid crystal display devices and instrument lighting and a preparation method thereof. The near-infrared absorption filter film is compatible with night vision imaging systems. Background technique [0002] In the electromagnetic spectrum, the human eye only responds to wavelengths between 380nm and 760nm, which is the color we usually see. In the darker the light, the human eye is less able to distinguish colors and details of objects. If In the dark night, the sense of color is completely lost, and the object object becomes a shadow, blurred. In fact, there is a small amount of natural light in the dark environment, such as moonlight, starlight, atmospheric glow, etc., which are collectively called night sky light. Because they are very weak compared with sunlight, they are also called night lights. In the dark environment at night, in addition to th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/24C09J7/25C09J7/38B32B27/06B32B37/12B32B37/10C09D175/14C09D7/63C09J175/04C09J11/00C09J183/04C08J7/04
Inventor 杨柱邓康清夏萍胡露熊中年袁东芝常征刘振宇龚露露邹美霞
Owner HUBEI INST OF AEROSPACE CHEMOTECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap