Insulated dust-proof coating

A technology of dust-proof coating and content, applied in the direction of polyester coating, polyurea/polyurethane coating, coating, etc., can solve the problems of poor insulation ability, easy solidification, poor weather resistance, etc., and achieve the effect of preventing high temperature influence

Inactive Publication Date: 2016-01-20
SUZHOU MINGXUAN FLOORING COATINGS
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem mainly solved by the present invention is to provide an insulating and dustproof coating, which solves the problems of easy solidification, poor insulation ability and poor weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1 of the present invention includes: an insulating and dust-proof paint, including components in the following proportions:

[0017] 20 parts of water-based polyurethane emulsion;

[0018] Dimethyldichlorosilane" 12 parts;

[0019] 34 parts of polyterephthalene;

[0020] 12 parts of oxalic acid polyester;

[0021] 8 parts of FRP particles;

[0022] 5 parts of titanium dioxide;

[0023] 8 parts of hydroxyethyl cellulose

[0024] Dispersant 3 parts

[0025] 100 parts of ionized water.

Embodiment 2

[0026] Embodiment 2 of the present invention includes: an insulating and dust-proof coating, including components in the following proportions:

[0027] 28 parts of water-based polyurethane emulsion;

[0028] Dimethyldichlorosilane 13 parts;

[0029] 38 parts of polyterephthalene;

[0030] 16 parts of oxalic acid polyester;

[0031] 11 parts of FRP particles;

[0032] 7 parts of titanium dioxide;

[0033] 10 parts of hydroxyethyl cellulose

[0034] 4 parts of dispersant

[0035] 105 parts of ionized water.

Embodiment 3

[0036] Embodiment 3 of the present invention includes: an insulating and dust-proof coating, including components in the following proportions:

[0037] 32 parts of water-based polyurethane emulsion;

[0038] Dimethyldichlorosilane 14 parts;

[0039] 42 parts of polyterephthalene;

[0040] 18 parts of oxalic acid polyester;

[0041] 14 parts of FRP particles;

[0042] 9 parts of titanium dioxide;

[0043] 12 parts of hydroxyethyl cellulose

[0044] 5 parts of dispersant

[0045] 110 parts of ionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insulated dust-proof coating. The insulated dust-proof coating comprises the following components in parts by weight: 20-32 parts of a waterborne polyurethane emulsion, 12-14 parts of dimethyldichlorosilance, 34-42 parts of poly-terephthalyl alcohol, 12-18 parts of oxalic acid polyester, 8-14 parts of glass steel particles, 5-9 parts of titanium dioxide, 8-12 parts of hydroxyethyl cellulose, 3-5 parts of a dispersing agent and 100-110 parts of ionized water. The insulated dust-proof coating has the characteristics of super weather resistance, high elasticity, super wear resistance, wind-sand resistance, high-low temperature performance resistance and the like. The insulated dust-proof coating has insulativity and is capable of preventing high temperature influences caused by electric conduction.

Description

Technical field [0001] The invention relates to the field of architectural coatings, in particular to an insulating and dustproof coating. Background technique [0002] At present, the wear resistance of the existing coatings is average, and the coating parts that need to be exposed are often exposed to friction coatings. It is easy to wear; moreover, in an environment with large temperature differences, the phenomenon of shelling and dry cracking is likely to occur, which is extremely The impact protection ability of the company has no effect on the protection of materials. Most of the existing insulating coatings are epoxy systems. This is due to the outstanding anti-corrosion and insulating properties of the epoxy system. However, the ether bond in the epoxy resin is easily broken by ultraviolet radiation, causing the coating to age and powder. The insulation capacity is weak. Summary of the invention [0003] The main technical problem solved by the present invention is to p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D171/12C09D167/02C09D101/28C09D5/25C09D7/12
Inventor 沈雪芬
Owner SUZHOU MINGXUAN FLOORING COATINGS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products