Preparation method of medical film having sterilizing function

A function and material technology, applied in the field of medical film preparation, can solve the problem of rare materials for sterilization and disinfection, and achieve a significant killing effect

Inactive Publication Date: 2015-12-09
JIANGSU LANWAN BIOTECH
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among the currently used biomedical materials, there have been many researches and applications on materials that can play a role in antibacterial effect, but materials that can play a role in sterilization and disinfection are rare. Therefore, it is necessary to research and develop a material that can play a role in sterilization Disinfecting medical materials, better used in the field of medical and health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of medical film having sterilizing function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing a medical film with sterilizing effect, comprising the following preparation steps:

[0021] Step 1: Add 80 parts of PVC in parts by weight, 3 parts of phenolic resin, 5 parts of PET, 2 parts of stearic acid, 1 part of polyvinyl alcohol and 0.5 part of paraffin into the mixer and stir and mix evenly at a stirring speed of 180 rpm. The mixing time was 20 minutes to obtain material 1;

[0022] Step 2, transfer material 1 into the reactor, add 1 part of sodium dodecylbenzenesulfonate in parts by weight, 2 parts of melamine, 0.5 part of polyacrylamide, 2 parts of hydroxypropyl methylcellulose, Heat and stir for 20 minutes under a negative pressure of 0.01MPa, the heating temperature is 60°C, the stirring speed is 100 rpm, and the temperature is lowered to room temperature to obtain material 2;

[0023] Step 3: Add 10100.2 parts by weight of antioxidant, 0.3 part of auxiliary antioxidant TNP, and 0.5 part of barium stearate into material 2, stir and m...

Embodiment 2

[0027] A method for preparing a medical film with sterilizing effect, comprising the following preparation steps:

[0028] Step 1: Add 85 parts of PVC in parts by weight, 4 parts of phenolic resin, 7 parts of PET, 3 parts of stearic acid, 2 parts of polyvinyl alcohol and 0.6 part of paraffin into the mixer and stir and mix evenly. The stirring speed is 186 rpm. The mixing time was 24 minutes to obtain material 1;

[0029] Step 2, transfer material 1 into the reactor, add 2 parts by weight of sodium dodecylbenzenesulfonate, 3 parts of melamine, 0.7 part of polyacrylamide, 3 parts of hydroxypropyl methylcellulose, Heating and stirring for 25 minutes under a negative pressure of 0.02MPa, heating temperature 66°C, stirring speed 110 rpm, and cooling down to room temperature to obtain material 2;

[0030] Step 3: Add 0.4 part by weight of antioxidant DLTP, 0.4 part of auxiliary antioxidant TPP, and 1 part of barium stearate into material 2, stir and mix evenly to obtain material 3...

Embodiment 3

[0034] A method for preparing a medical film with sterilizing effect, comprising the following preparation steps:

[0035] Step 1, 92 parts by weight of PVC, 6 parts of phenolic resin, 8 parts of PET, 5 parts of stearic acid, 2 parts of polyvinyl alcohol and 0.7 part of paraffin are added to the mixer and stirred evenly, the stirring speed is 190 rpm, The mixing time was 26 minutes to obtain material 1;

[0036] Step 2, transfer material 1 to the reactor, add 2 parts by weight of sodium dodecylbenzenesulfonate, 4 parts of melamine, 1.5 parts of polyacrylamide, 4 parts of hydroxypropyl methylcellulose, Heating and stirring for 28 minutes under a negative pressure of 0.03MPa, heating temperature 65°C, stirring speed 120 rpm, and cooling down to room temperature to obtain material 2;

[0037] Step 3: Add 10100.6 parts by weight of antioxidant, 0.4 part of auxiliary antioxidant TNP, and 1 part of barium stearate to material 2, stir and mix evenly to obtain material 3;

[0038] S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a medical film having a sterilizing function. The preparation method comprises the following steps: stirring and uniformly mixing PVC, phenolic resin, PET, stearate, polyvinyl alcohol and paraffin in a stirrer to obtain a mixture I, then transferring the mixture I into a reaction kettle, adding sodium dodecyl benzene sulfonate, melamine, polyacrylamide and hydroxypropyl methyl cellulose into the reaction kettle, heating and stirring under a negative pressure condition, then cooling to the room temperature, adding an antioxidant, an auxiliary antioxidant and barium stearate, uniformly stirring and mixing to obtain a mixture II, extruding and granulating the mixture II in a dual-screw extruder to obtain a master batch; finally extruding and blowing the master batch by adopting a plastic film blowing machine to obtain the medical film having the sterilizing function. The medical film prepared in the method is good in sterilizing performance and physical performance and wide in application prospect.

Description

technical field [0001] The invention belongs to the field of medical and sanitary materials, and in particular relates to a preparation method of a medical film with sterilizing effect. Background technique [0002] With the development of social economy and the improvement of living standards, human beings are paying unprecedented attention to their own medical and health undertakings. The increasing pressure of survival, the accelerated pace of life, the intensification of environmental pollution, the frequent occurrence of food, transportation and production safety accidents, local wars, and natural disasters have caused diseases and traumas to become the ever-lingering haze of human beings. As an important means of modern medicine—an important basis and component of medical devices, biomaterials are used for the diagnosis and treatment of diseases, the repair, replacement or function enhancement of tissues and organs, so that a large number of patients who are struggling...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L61/06C08L67/02C08L29/04C08L91/06C08L33/26C08L1/28C08K5/42C08K5/3492C08K5/098B29C47/92B29C55/28B29C48/92
Inventor 章祥庆唐海健
Owner JIANGSU LANWAN BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products