A kind of anti-corrosion and anti-rust type post-tensioning method prestressed channel pressure slurry and preparation method thereof

A technology of channel grouting and post-tensioning method, which is applied in the field of building materials, can solve the problems of corrosion damage of prestressed steel bars, poor prestressed steel bar holding force, and insufficient grouting, and achieves reduced shrinkage, high strength, and slurry. Good flow performance

Active Publication Date: 2017-08-22
石家庄市易达恒联路桥材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The adverse phenomena that are easy to occur when using this material for grouting are generally manifested as: 1) The grouting is not full; 2) Bleeding and lead to poor grip with prestressed steel bars; 3) In northwest or coastal areas, it is easy to cause corrosion of prestressed steel bars destroy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-corrosion and anti-rust type post-tensioning method prestressed channel pressure slurry and preparation method thereof
  • A kind of anti-corrosion and anti-rust type post-tensioning method prestressed channel pressure slurry and preparation method thereof
  • A kind of anti-corrosion and anti-rust type post-tensioning method prestressed channel pressure slurry and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An anti-corrosion and anti-rust type post-tensioned prestressed tunnel pressure slurry, the formula of which is as follows:

[0029]

[0030] Its preparation method is as follows: Weigh each raw material component into a dry powder mixer and mix evenly, then move it into a cement mortar mixer, add 840g of mixing water at 20°C, stir for 1min at a slow speed, and then use a fast speed of 1000r / min. Stirring for 4 minutes, the product was discharged, and then the performance test of the grouting slurry was carried out under the ambient temperature of 20°C.

Embodiment 2

[0032] An anti-corrosion and anti-rust type post-tensioned prestressed tunnel pressure slurry, the formula of which is as follows:

[0033]

[0034]

[0035] The preparation method is as follows: Weigh each raw material component into a dry powder mixer and mix evenly, then move it into a cement mortar mixer, add 826g of mixing water at 23°C, stir for 1.5min at a slow speed, and then use a 1000r / min Stir at high speed for 4.5 minutes, discharge the product, and then carry out the performance test of the grouting slurry under the ambient temperature condition of 23°C.

Embodiment 3

[0037] An anti-corrosion and anti-rust type post-tensioned prestressed tunnel pressure slurry, the formula of which is as follows:

[0038]

[0039]

[0040] Its preparation method is as follows: Weigh each raw material component into a dry powder mixer and mix evenly, then move it into a cement mortar mixer, add 760g of stirring water at 15°C, stir for 0.5min at a slow speed, and then use a 1000r / min Stir at high speed for 3 minutes, discharge the product, and then carry out the performance test of the grouting slurry under the ambient temperature of 15°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an anti-corrosion and anti-rust type post-tensioned prestressed tunnel press slurry and a preparation method thereof. The press slurry includes cement, expansion agent, mineral powder, water reducer, retarder, rust inhibitor, and preservative , carboxymethyl cellulose, defoamer and other components, the water-to-binder ratio is 0.28, after mixing with a cement mortar mixer at a slow speed, and then at a fast speed of 1000r / min to obtain the product. The grout material provided by the invention has good slurry fluidity, no delamination, no bleeding, fullness, no shrinkage and high strength after hardening, which is beneficial to protect prestressed steel bars from corrosion and improve prestressed bridges. The service life of the structure is especially suitable for post-tensioning prestressed tunnel grouting in northwest or coastal areas, and has the function of anti-corrosion and anti-rust.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a post-tensioned prestressed tunnel pressure slurry and a preparation method thereof. Background technique [0002] The recommended standard for the transportation industry of the People's Republic of China "Technical Specifications for Construction of Highway Bridges and Culverts" (JTG / T F50-2011) stipulates in the technical conditions for grouting of post-tensioned prestressed concrete beam channels: the water-binder ratio of the grouting slurry is 0.26 to 0.28; A high-speed mixer with a rotation speed of 1000 rpm is used during construction; at the same time, the fluidity of the slurry is required: initial 10-17s, 30min 10-20s, 60min 10-25s; bleeding rate 0%; pressure bleeding rate 0%; free expansion rate 0-3%; filling degree qualified; setting time: initial setting time ≥ 5h, final setting time ≤ 24h; 3d compressive strength ≥ 20MPa, 7d compressive strength ≥ 40MPa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B22/16C04B22/08C04B24/42C04B24/38C04B24/12C04B24/10C04B24/24C04B111/26
Inventor 李建永刁书磊胡志秀
Owner 石家庄市易达恒联路桥材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com