Mesoporous magnesium silicate/hydroxyapatite/polyetheretherketone composite material, bone prosthesis, preparation method and application thereof

A technology of hydroxyapatite and polyether ether ketone, which is applied in the field of materials, can solve the problems of bone repair materials such as looseness, poor mechanical compatibility, and lack of biological activity, so as to accelerate bone healing, shorten bone healing time, and process easy effect

Inactive Publication Date: 2017-12-15
SHENZHEN KEJU NEW MATERIAL
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to overcome the loosening and bone resorption of bone repair materials caused by stress shielding caused by the poor mechanical compatibility of existing bone repair materials, or the bone healing speed is too slow and lacks biological activity, which cannot be combined with Defects in the formation of strong bonds in bone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mesoporous magnesium silicate/hydroxyapatite/polyetheretherketone composite material, bone prosthesis, preparation method and application thereof
  • Mesoporous magnesium silicate/hydroxyapatite/polyetheretherketone composite material, bone prosthesis, preparation method and application thereof
  • Mesoporous magnesium silicate/hydroxyapatite/polyetheretherketone composite material, bone prosthesis, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] A preparation method of mesoporous magnesium silicate, comprising the steps of:

[0067] (1) Mix 8.5g of P123, 240mL of deionized water and 8g of absolute ethanol, and stir until the solution is clear, then add 20mL of hydrochloric acid with a concentration of 11.9mol / L at 40°C and stir to mix, then add 24g of TEOS Add dropwise into the solution, stir until the solution becomes white and turbid, then add 29.5g of magnesium nitrate hexahydrate, and continue stirring for 2.5h to obtain a reaction solution;

[0068] (2) Aging the reaction solution at 98°C for 48 hours, then removing the supernatant by suction filtration, drying the precipitate at 85°C, and sintering at 600°C for 7 hours to obtain mesoporous magnesium silicate.

[0069] The scanning electron micrographs and transmission electron micrographs of the mesoporous magnesium silicate / hydroxyapatite are shown in figure 1 (a), (b) and figure 1 (c), (d); the mesoporous magnesium silicate / hydroxyapatite has a mesopo...

Embodiment 2

[0071] The preparation method of mesoporous magnesium silicate / hydroxyapatite / polyether ether ketone composite material, it comprises the following steps:

[0072] 1.5kg (15wt%) of hydroxyapatite, 6.5kg (65wt%) of polyetheretherketone (10 μm in particle size) and 2kg (20wt%) of the mesoporous magnesium silicate prepared in Example 1 were placed in a mixer Mix evenly to obtain a mixed powder; mix the mixed powder with absolute ethanol, disperse it ultrasonically for 30 minutes at a power of 60W, and then place it in an oven at 65°C to evaporate the absolute ethanol; then use a mold to compress the composite powder (use non-bone prosthesis product mold), and then heated up in a sintering furnace, sintered and formed, and obtained; wherein, the sintering temperature is 350 ° C; the heating rate of the sintering furnace is 1 ° C / min; the holding time is 140 min. The mechanical properties of the mesoporous magnesium silicate / hydroxyapatite / polyether ether ketone composite are sho...

Embodiment 3

[0074] A method for preparing a bone prosthesis, comprising the steps of:

[0075] The hydroxyapatite powder of 1.5kg (15wt%), 7kg (70wt%) polyether ether ketone (particle diameter is 15 μ m) and 1.5kg (15wt%) the mesoporous magnesium silicate that embodiment 1 makes in mixer Mix the raw materials uniformly in the process to obtain a mixed powder; mix the mixed powder with absolute ethanol, disperse it ultrasonically for 30 minutes with a power of 70W, and then place it in an oven at 70°C to evaporate the absolute ethanol to obtain a composite powder; then press the composite powder with a mold Molding (the mold of the bone prosthetic product), and then heating up in a sintering furnace, sintering and molding, and the obtained; wherein, the sintering temperature is 360°C; the heating rate of the sintering furnace is 1°C / min; the holding time is 140min. The mechanical properties of the bone restoration are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a mesoporous magnesium silicate / hydroxyapatite / polyether ether ketone composite material, a bone repair body, a preparation method and an application thereof. The preparation method of the mesoporous magnesium silicate / hydroxyapatite / polyether ether ketone composite material is as follows: 15wt%-20wt% mesoporous magnesium silicate, 10wt%-15wt% hydroxyapatite and 65wt%- 75wt% polyetheretherketone is uniformly mixed to obtain a mixed powder; then the mixed powder is mixed with absolute ethanol, ultrasonically dispersed, and then evaporated at 65°C to 80°C to obtain a composite powder; Composite powder processing and molding, vested; the composite material has good bioactivity and biocompatibility, has good mechanical compatibility with bone tissue, can stimulate bone growth, accelerate bone healing, and reduce the healing of bone implant materials time. The bone prosthesis has good bone mechanical compatibility and antibacterial property, high strength, good fatigue resistance, good corrosion resistance and long service life.

Description

technical field [0001] The invention relates to the field of materials, in particular to a mesoporous magnesium silicate / hydroxyapatite / polyetheretherketone composite material and its preparation method and application, and also relates to a bone restoration and its preparation method. Background technique [0002] At present, the clinically used bone implant materials are mostly titanium-based bone implant materials and ceramic bone implant materials, but these materials have some shortcomings that are difficult to overcome. For example, the structural properties of metal materials are quite different from those of bone, and they lack active, unable to form osseointegration with bone, and easily cause bone resorption. In addition, the dissolution of metal ions may easily lead to fluid accumulation, inflammation, and necrosis; for example, ceramic bone implant materials are not easy to form and process, and have poor toughness, etc. shortcoming. Therefore, the research and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/22C08L71/08C08K7/26C08K3/32A61L27/46A61L27/54A61L27/50
Inventor 徐东马旭辉魏杰张珏蔡亮宋文华邬迎阳莫品书杨海灵
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com