A method for preparing zr/al reactive laminated foils using ebpvd

A technology of reactive lamination and lamination, which is applied in the field of preparation of Zr/Al reactive laminated foils, can solve the problems of easy introduction of impurities, unfavorable self-propagation rate, and low production efficiency at the Zr/Al layer interface, and achieve a complete and clear interface , low cost and high production efficiency

Active Publication Date: 2017-11-17
HARBIN INST OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the technical problems of low production efficiency, high production cost, easy introduction of impurities at the interface of the Zr / Al layer, causing pollution, and unfavorable acquisition of a higher self-spreading rate in the current preparation method of Zr / Al laminated foil, and proposes A method for preparing Zr / Al reaction laminated foil by EBPVD

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing zr/al reactive laminated foils using ebpvd
  • A method for preparing zr/al reactive laminated foils using ebpvd
  • A method for preparing zr/al reactive laminated foils using ebpvd

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0030] Embodiment 1: This embodiment is a method for preparing Zr / Al reaction laminated foil by EBPVD according to the following steps:

[0031] 1. Preliminary preparations for EBPVD: clean the ingots I and II, clean the vacuum chamber of the EBPVD equipment, and install the substrate. There are two electron guns in the vacuum chamber of the EBPVD equipment, which are electron guns I and II. The ingot I is placed under the electron gun I, the cleaned ingot II is placed under the electron gun II, the separation layer material is placed between the ingot I and the ingot II, the substrate is wiped, and the baffle is closed; The ingot I is pure Zr, and the ingot II is pure Al;

[0032]2. Preheating the ingot: close the vacuum chamber and evacuate until the vacuum degree is 6×10 -3 At Pa, turn on the electron gun Ⅰ and electron gun Ⅱ, set the current of the electron gun Ⅰ to 0.02A~0.1A, and the current of the electron gun Ⅱ to 0.02A~0.1A, use the electron gun Ⅰ to scan the ingot Ⅰ...

specific Embodiment approach 2

[0039] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the material of the separation layer in step 1 is sodium chloride or calcium chloride. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0040] Embodiment 3: The difference between this embodiment and Embodiment 1 or 2 is that the substrate described in Step 1 is a large heat sink integral substrate, a circulating water-cooled substrate, a static water-cooled substrate, a segmented substrate, The base plate of the radiation tube or the base plate of the water cooling box, and the thickness of the base plate is greater than 40mm. Other steps are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A method for preparing Zr / Al reaction laminated foil by EBPVD relates to a preparation method of Zr / Al reaction laminated foil. The present invention aims to solve the technical problems of low production efficiency and high production cost in the current Zr / Al laminated foil preparation method, easy introduction of impurities at the interface of the Zr / Al layer, causing pollution, and being unfavorable for obtaining a higher self-propagating rate. The present invention: 1. Preliminary preparation work for EBPVD; 2. Preheating the ingot; 3. Depositing the separation layer; 4. Depositing laminated foils. The Zr / Al reaction laminated foil of the present invention has uniform structure, controllable layer thickness, complete and clear interface, high production efficiency and low cost, and various substrates of the present invention can make the temperature of the substrate during the preparation process lower than 200°C In order to avoid burning of the Zr / Al reactive laminated foil; the Zr / Al reactive laminated foil prepared by the invention can release extremely large heat in a self-propagating manner in a short period of time, and can be applied to the field of special welding.

Description

technical field [0001] The invention relates to a preparation method of Zr / Al reaction laminated foil. Background technique [0002] With the rapid development of high-tech represented by space technology, information technology, new energy and new materials, higher requirements are put forward for material connection technology. Taking the space environment as an example, due to the limitation of aircraft load, traditional fusion welding cannot be used in space; while brazing with high reliability often has a complicated process and is difficult to achieve in space. In VLSI manufacturing, it is necessary to accurately and quickly solder some original devices on the circuit board, and electronic devices are often very sensitive to heat, which requires shortening the connection time as much as possible and reducing the impact on surrounding devices. Zr / Al reactive laminated foil is a new type of layered energetic composite material, which can be used as a local heat source t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/30C23C14/14
Inventor 芦强强宋广平孙跃赫晓东
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products