A kind of carbon/carbon composite material and preparation method thereof

A carbon composite material and carbon fiber preform technology, which is applied in the field of C/C composite material and its preparation, can solve the problems of high synthesis temperature, pollute the environment, discharge a large amount of waste gas or soot particles, etc., and achieve low reaction temperature and preparation cost. Low, avoid the effect of surface crusting

Active Publication Date: 2017-12-05
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method still uses non-renewable fossil fuels as raw materials to prepare carbon / carbon composite materials. The synthesis temperature is high, and a large amount of waste gas or soot particles with complex structures will be discharged during the cracking process, polluting the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of carbon/carbon composite material and preparation method thereof
  • A kind of carbon/carbon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1): glucose is dissolved in water to obtain a glucose solution with a concentration of 100g / L;

[0033] (2): Set the density to 0.2g / cm 3 The cylindrical overall carbon felt is set on the heating tube; the outer diameter of the cylindrical carbon felt is 1 / 3 of the inner diameter of the reactor.

[0034] (3): Add the glucose solution obtained in step (1) into the reaction kettle, assemble the heating tube with the carbon fiber prefabricated body in step (2) and the reaction kettle, and start the heating reaction. The reaction temperature is controlled at 120°C. The time is controlled at 8h, and the filling ratio is controlled at 0.4.

[0035] (4): Open the reaction kettle after the reaction of step (3), pour out the liquid in the reaction kettle, then add the glucose solution in the step (1), the filling ratio is controlled at 0.4, then heat the reaction, and the reaction temperature is controlled at 120°C, the reaction time is controlled at 8h.

[0036] (5): Repeat...

Embodiment 2

[0039] (1): Dissolving sucrose in water to obtain a sucrose solution with a concentration of 200g / L;

[0040] (2): Set the density to 0.4g / cm 3 The cylindrical carbon fiber needle felt is set on the heating tube, and the outer diameter of the cylindrical carbon fiber needle felt is 1 / 2 of the inner diameter of the reactor.

[0041] (3): Add the sucrose solution obtained in step (1) into the reaction kettle, assemble the heating tube of the carbon fiber prefabricated body in step (2) and the reaction kettle, and start the heating reaction. The reaction temperature is controlled at 150°C, and the reaction time is Controlled at 4h, the filling ratio is controlled at 0.5.

[0042](4): Open the reaction kettle after the reaction of step (3), pour out the liquid in the reaction kettle, then add the sucrose solution in the step (1), the filling ratio is controlled at 0.5, then heat the reaction, and the reaction temperature is controlled at 150°C, the reaction time is controlled at...

Embodiment 3

[0047] (1): Stir the starch in water evenly, and the concentration of the starch in the solution is 300g / L;

[0048] (2): Set the density to 0.2g / cm 3 The cylindrical needle-punched carbon felt is set on the heating tube; the outer diameter of the cylindrical needle-punched carbon felt is 2 / 3 of the inner diameter of the reactor.

[0049] (3): Add the starch solution obtained in step (1) into the reaction kettle, assemble the heating tube with the carbon fiber prefabricated body in step (2) and the reaction kettle, and start the heating reaction. The reaction temperature is controlled at 180°C, and the reaction time is Controlled at 6h, the filling ratio is controlled at 0.6.

[0050] (4): Open the reaction kettle after the reaction of step (3), pour out the liquid in the reaction kettle, then add the starch solution in step (1), the filling ratio is controlled at 0.6, and then heat the reaction, and the reaction temperature is controlled at 160°C, the reaction time is contr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
densityaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

A carbon / carbon composite material and its preparation method, the biomass carbon source is dissolved or dispersed in water to prepare a carbon source aqueous solution or suspension; the carbon source aqueous solution or suspension is added to a reaction kettle, and then the The heating tube of the carbon fiber prefabricated body is put into the reaction kettle, and then heated for hydrothermal carbonization reaction; the liquid in the reaction kettle is poured out, and the carbon source aqueous solution or suspension is added into the reaction kettle, and then heated for hydrothermal carbonization reaction to obtain Carbon / Carbon Composite Composites. The present invention provides a new method for thermal gradient hydrothermal preparation of carbon / carbon composite materials. On the basis of inheriting the renewable hydrothermal carbonization raw materials, low synthesis temperature, and environmental protection, it combines thermal gradient deposition technology with high densification efficiency specialty.

Description

technical field [0001] The invention belongs to the technical field of composite material preparation, and in particular relates to a C / C composite material and a preparation method thereof. Background technique [0002] As a new type of carbon material with unique properties, carbon / carbon composite material combines the excellent performance of carbon fiber and carbon material. It is not limited to aviation, aerospace and other cutting-edge technology fields, but has been extended to many civilian fields such as transportation, chemical industry, sports and medicine. From the liquid phase impregnation technology using petroleum or coal tar pitch, to the chemical vapor deposition technology using gaseous hydrocarbons, and the latest film boiling deposition technology using liquid hydrocarbons, petrochemical fuels and their derivatives are the best choice for the preparation of carbon / carbon composites. important carbon source. However, fossil fuels are non-renewable resour...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/83
Inventor 欧阳海波李翠艳黄剑锋费杰曹丽云孔新刚许占位
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com