Slag-doped high-intensity ceramic floor tile

A high-strength, steel slag technology, applied in the field of ceramic floor tile manufacturing, can solve the problems of lack of raw materials in the ceramic tile industry, deviation from clean production, environmental pollution, etc., and achieve the effects of spraying glaze, not easy to fall off and crack, and wide application range

Inactive Publication Date: 2015-09-30
方堃
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional ceramic tiles use high-quality kaolin, feldspar, clay, etc. as the main raw materials, and are prepared by wet pulverization and spray drying processes. However, this preparation method has high energy consumption and produces a large amount of water vapor, nitrogen oxides, and sulfur oxides Heavy pollutants such as waste and dust pollute the tail gas, which seriously pollutes the environment and seriously deviates from the requirements of clean production in the ceramic industry, and more and more kaolin is used in papermaking, coatings, fertilizers, refractory materials, rubber, plastics, petrochemicals and other industries. The raw materials for the ceramic tile industry are very scarce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] A high-strength ceramic floor tile doped with steel slag, made of the following raw materials in parts by weight (kg): sepiolite 4, perlite 8, converter steel slag 42, talcum powder 22, kaolin 7, waste glass powder 20, hydroxyethyl Dimethylcellulose 1, water glass powder 3, zinc oxide 3, brown sugar 7, polyvinylpyrrolidone 0.1, appropriate amount of distilled water;

[0016] A ceramic floor tile with high strength doped with steel slag according to the present invention is made by the following specific steps:

[0017] (1) Add converter steel slag to 2-3 times the weight of distilled water and soak for 1-2 days, then add it to a ball mill for ball milling, dry it through a 200-mesh sieve after ball milling, and age the steel slag powder at room temperature for 20- 30 days standby;

[0018] (2) Dissolve the brown sugar with 5 times the amou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a slag-doped high-intensity ceramic floor tile, which comprises the following raw materials by weight part: 4-6 parts of meerschaum, 6-10 parts of perlite, 30-50 parts of converter slag, 20-25 parts of powdered steatile, 5-10 parts of kaolin, 15-25 parts of waste glass micro powder, 1-2 parts of hydroxyethyl methyl cellulose, 2-4 parts of water glass powder, 2-4 parts of zinc oxide, 5-8 parts of brown sugar, 0.1-0.3 parts of polyvinylpyrrolidone and a proper amount of distilled water. The floor tile has the advantages of high hardness, high mechanical strength, good heat stability and ageing resistance, little pollution, and wide application scope.

Description

technical field [0001] The invention relates to the field of manufacturing ceramic floor tiles, in particular to a high-strength ceramic floor tile doped with steel slag and a preparation method thereof. Background technique [0002] my country is a big country of iron and steel, and about 150 kilograms of steel slag is produced for every ton of steel produced. Steel slag stacked in the slag yard occupies a large amount of land and pollutes the environment. For steel slag containing trivalent chromium, it will transform into hexavalent state after being placed in the open air for a long time, which will cause great harm to the ecological environment and the growth of animals and plants. Steel slag mainly contains calcium oxide, silicon dioxide, aluminum oxide, iron oxide, manganese oxide and carbon sulfide, and has potential gelling activity and broad application prospects. At present, it is of great social significance to study how to efficiently utilize steel slag to prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/132C04B33/138
CPCY02P40/60
Inventor 方堃
Owner 方堃
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products