Ceramic tile bonding mortar

A technology for bonding mortar and ceramic tiles, which is applied in the field of mortar bonding ceramic tiles, and can solve problems such as easy hollowing and weak adhesion

Inactive Publication Date: 2015-06-24
许勤峰
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above technical problems, the present invention provides a ceramic tile adhesive mortar, which solves the technical problems in the prior art such as weak adhesion and easy hollowing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1: A tile bonding mortar, its components and parts by weight are: 350 parts of ordinary portland cement, 530 parts of 40 mesh sand, 45 parts of heavy calcium powder, 2 parts of polymer xanthan gum powder, 1.5 parts of hydroxypropyl methylcellulose. Take ordinary Portland cement, sand, heavy calcium powder, polymer xanthan gum powder, and hydroxypropyl methylcellulose in proportion and mix them together, pour them into a mixer and stir evenly for about 25 minutes to obtain good workability, Mortar with high bond strength. Comprehensive performance of bonding mortar: consistency 6.8 g / cm s, water retention rate 0.147kg / m 3 , The flexural strength of 7d is 5.7MPa, the flexural strength of 28d is 6.3MPa, the compressive strength of 7d is 21.15MPa, the compressive strength of 28d is 34.1 MPa, and the bonding strength is 4.8 MPa.

Embodiment 2

[0012] Embodiment 2: a kind of tile bonding mortar, its components and parts by weight are: 380 parts of ordinary portland cement, 570 parts of 70 mesh sand, 50 parts of heavy calcium powder, 2.5 parts of polymer xanthan gum powder, 1.75 parts of hydroxypropyl methylcellulose, 2.5 parts of redispersible latex powder.

[0013] Take ordinary Portland cement, sand, heavy calcium powder, polymer xanthan gum powder, hydroxypropyl methylcellulose, and redispersible latex powder in proportion and mix them together, pour them into the mixer and stir evenly for about 25 minutes. A mortar with good workability and high bonding strength is obtained. Comprehensive performance of bonding mortar: consistency 6.9g / cm s, water retention rate 0.137kg / m 3 , The flexural strength of 7d is 5.3MPa, the flexural strength of 28d is 5.8MPa, the compressive strength of 7d is 19.15MPa, the compressive strength of 28d is 32.1 MPa, and the bonding strength is 5.48 MPa.

Embodiment 3

[0014] Embodiment 3: a kind of ceramic tile bonding mortar, its each component and the parts by weight are: 410 parts of ordinary Portland cement, 600 parts of 100 mesh sands, 55 parts of heavy calcium powder, 3 parts of polymer xanthan gum powder, 2 parts of hydroxypropyl methylcellulose, 5 parts of redispersible latex powder.

[0015] Take ordinary Portland cement, sand, heavy calcium powder, polymer xanthan gum powder, hydroxypropyl methylcellulose, and redispersible latex powder in proportion and mix them together, pour them into the mixer and stir evenly for about 25 minutes. A mortar with good workability and high bonding strength is obtained. Comprehensive performance of adhesive mortar: consistency 6.95g / cm s, water retention rate 0.153kg / m 3 , The flexural strength of 7d is 5.6MPa, the flexural strength of 28d is 6.1MPa, the compressive strength of 7d is 24.15MPa, the compressive strength of 28d is 37.28 MPa, and the bonding strength is 5.16 MPa.

[0016] The invent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flow consistencyaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic tile bonding mortar. The ceramic tile bonding mortar is composed of a base material and an additive; the base material comprises, by weight, 350 to 410 parts of ordinary portland cement, 530 to 600 parts of sand with a particle size of 40 to 100 meshes, and 45 to 5 parts of heavy calcium carbonate powder; and the additive comprises, 2 to 3 parts of high-molecular xanthan gum powder, 1.5 to 2 parts of hydroxypropyl methyl cellulose, and 0 to 5 parts of redispersible latex powder. According to the ceramic tile bonding mortar, adding of high-molecular xanthan gum powder and hydroxypropyl methyl cellulose is capable of increasing viscosity of the ceramic tile bonding mortar greatly; water holding effect is excellent; delayed coagulation is realized; operation time of operators is prolonged; the ceramic tile bonding mortar is suitable for long-distance transportation; strength after hardening is high; ceramic tile loosening or falling after bonding is avoided; adding of redispersible latex powder is capable of improving water resistance of the ceramic tile bonding mortar; and construction under moisture circumstances can be carried out.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a mortar for bonding ceramic tiles. Background technique [0002] At present, the bonding material between tiles and the ground or wall is completely mixed with mortar on site. This method is to mix sand, cement and water in a certain proportion on site to make simple cement mortar, and then paint this mortar. On the soaked tiles, then mechanically tap the tiles to ensure that the tiles are on the same level. Due to the poor flow resistance of mortar, when pasting vertical components such as walls, the tiling must start from the low end, and a locator is required between the tiles to achieve neat joints. The proportion of the components of the mortar in this mixing method is difficult Control, uneven viscosity, weak adhesion, prone to hollowing, tile bonding sinking, and uneven bonding. Contents of the invention [0003] In order to solve the above-ment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/06
Inventor 许勤峰
Owner 许勤峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com