Antistatic high-gloss wear-resistant floor coating composition

A coating composition and anti-static technology, which is applied in coatings, conductive coatings, polyurea/polyurethane coatings, etc., can solve problems such as insufficient gloss, insufficient hardness of coating materials, and inability to meet the trampling of high traffic , to achieve the effect of preventing static electricity

Inactive Publication Date: 2015-05-27
ECOLAB USA INC
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating materials presented in this document are not hard enough for high tr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic high-gloss wear-resistant floor coating composition
  • Antistatic high-gloss wear-resistant floor coating composition
  • Antistatic high-gloss wear-resistant floor coating composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] The preparation of embodiment 1 high-gloss antistatic coating composition

[0060] The coating composition A of the present invention was prepared according to the formulation in Table 1 below.

[0061] Table 1.

[0062]

[0063]

[0064] The preparation method is as follows:

[0065] Under the action of slow mechanical stirring (about 60rpm), add each component one by one according to the order of the substances listed in Table 1. When one component is uniformly dispersed or dissolved, add the next component while ensuring that agitation continues throughout the addition of components. After the last component was added, the resulting mixture was stirred evenly and the stirring was continued for another 30 minutes, thereby obtaining the coating composition A of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antistatic high-gloss wear-resistant floor coating composition. The antistatic high-gloss wear-resistant floor coating composition comprises, by weight, 3.0-20% of a styrene-acrylic acid copolymer film forming agent, 2.0-20% of a polyurethane film forming agent, 1.0-15% of a film forming assistant, 0.1-10% of a plasticizer, 0.1-5% of a cross-linking agent, 0.5-10% of wax emulsion, 0.1-5% of a quaternaryammonium ethyl sulfate compound and the balance water. The invention also provides a use of the floor coating composition in antistatic floor treatment.

Description

technical field [0001] The present invention relates to a floor coating, in particular, to a floor coating composition having antistatic properties, and simultaneously having high gloss and abrasion resistance to meet long-term use requirements. Background technique [0002] Ground surfaces of various substrates, such as plastic floors (such as PVC, linen, rubber floors), stone, wooden floors, and cement-based floors, are often treated with floor polishes or polishes for daily care to achieve aesthetics and protection. floor and prevent dirt from penetrating. Moreover, the performance of the coating in the prior art to disperse and conduct charges is relatively poor, on which articles can be loaded with high surface charges during production, processing and use, thus causing static electricity to accumulate on the floor surface. In general, adverse or dangerous situations caused by electrostatic loads include, for example, attracting dust, adhering impurities, destroying el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D125/14C09D175/04C09D7/12C09D5/24
CPCC09D125/14C08L2201/04C08L2205/035C09D5/24C09D7/63C08L75/04C08L23/06C08L83/04C08K5/41C08K5/521C08K5/06
Inventor 许剑杰
Owner ECOLAB USA INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap