Heat-insulation film for high temperature molding, vacuum thermal insulator using same and process for fabricating vacuum thermal insulator

A technology of vacuum thermal insulation material and thermal insulation film, which is applied in the field of vacuum thermal insulation material and preparation of vacuum thermal insulation material, can solve the problems of reduced vacuum degree, deformation of thermal insulation film, defective products, etc.

Inactive Publication Date: 2015-04-29
DO YOUNG H S
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the case of bonding the heat insulating film to the outside of the core material by the vacuum high-frequency method, in the process of wrapping the heat insulating film on the outside of the core material, especially when wrapping the edge portion of the core material toward the center, The insulation film cannot be fully bonded to the core material
As a result, air or moisture enters through the heat-insulating film, and the degree of vacuum decreases over time, making it impossible to maintain heat-insulating properties. In particular, there are problems such as deformation of the heat-insulating film under high humidity.
[0004] In addition, conventionally, when the surface and corners of the core material were molded during the process of sealing the heat-insulating film for the manufacture of vacuum heat-insulating materials, wrinkles of the heat-insulating film would occur, resulting in a high possibility of product failure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-insulation film for high temperature molding, vacuum thermal insulator using same and process for fabricating vacuum thermal insulator
  • Heat-insulation film for high temperature molding, vacuum thermal insulator using same and process for fabricating vacuum thermal insulator
  • Heat-insulation film for high temperature molding, vacuum thermal insulator using same and process for fabricating vacuum thermal insulator

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Example 1 Preparation of heat insulating film

[0056] Polyethylene naphthalate (SKC, The back of the first film layer of NX10) is coated with an epoxy resin hot melt adhesive to form a 5 μm thick first adhesive layer. The first barrier layer made of aluminum foil was laminated with a thickness of 15 μm on the bottom surface of the first film layer using a laminator, and then a 20 μm thick modified epoxy resin hot-melt adhesive was coated on the first barrier layer. bottom of the layer.

Embodiment 2

[0057] Example 2 Preparation of heat insulating film

[0058] The procedure of Example 1 above was repeated except that a 20 μm-thick glass fiber was further laminated between the first film layer and the first adhesive layer, thereby preparing a heat insulating film.

Embodiment 3

[0059] Example 3 Preparation of heat insulating film

[0060] In addition to coating epoxy resin hot-melt adhesive between the first barrier layer and the hot-melt adhesive layer, thereby forming a second adhesive layer with a thickness of 15 μm, and further forming polyethylene naphthalate molded with a thickness of 100 μm Glycol esters (SKC, Except for the second thin film layer of NX10), the steps of Example 1 were repeated to prepare a thermal insulation film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention proposes a heat-insulation film laid so as to be molded at a high temperature, a vacuum thermal insulator having a core material with the outside coated with the heat-insulation film, and a method for fabricating the vacuum thermal insulator by coating the outside of the core material with the insulation film through a thermal-adhesion process. The heat-insulation film according to the present invention may be stably coated on the outside of the core material through the thermal-adhesion process at a high temperature.

Description

technical field [0001] The present invention relates to a thermal insulation film, and in more detail, relates to a thermal insulation film capable of thermal fusion molding, a vacuum thermal insulation material including the thermal insulation film, and a method for preparing the vacuum thermal insulation material by thermal fusion molding using the thermal insulation film. Background technique [0002] Recently, vacuum insulation materials are widely used instead of existing insulation materials such as polyurethane or foamed polystyrene. In general, a vacuum insulation material has a structure with a low gas or moisture permeability such as a core material (core) that is applied to a vacuum state as a skin material, and the demand for it has recently been greatly increased due to its excellent heat insulation effect. . [0003] Generally, a heat insulating film used as a skin material of a vacuum heat insulating material has a multi-layer film laminated structure, and in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/08B32B7/12B32B17/10F16L59/065
CPCB32B5/02B32B7/12B32B27/08B32B27/306B32B27/32B32B27/36B32B2260/046B32B2262/101B32B2307/306B32B9/005B32B9/045B32B27/065B32B27/10B32B27/12B32B27/38B32B37/1018B32B37/185B32B38/0004B32B38/0012B32B2266/0278B32B2305/022B32B2305/28B32B2307/304B32B2315/02B32B2315/085B32B2315/14B32B2375/00B32B2607/00Y10T156/1044Y10T428/2826Y10T428/31515B32B17/10F16L59/065B32B15/092B32B37/06B32B37/18B32B37/182B32B2255/06B32B2255/26C09J2400/143C09J2400/163C09J2463/00C09J2467/006
Inventor 金玎原
Owner DO YOUNG H S
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products