Paper surface sizing agent and method for raising paper permeability resistance
A technology of surface sizing and surface sizing agent, applied in the field of papermaking, can solve the problems of increasing production cost and high price of softwood pulp, and achieve the effect of improving air permeability resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0023] The enzymatic starch is formulated into a surface sizing solution. Then borax is prepared into a solution with a concentration of 3%, and then added to the surface sizing solution, mixed evenly, and the amount of borax added is 0.1% of the absolute dry mass of the enzymatic starch. Then use the above-mentioned surface sizing solution after adding borax and the surface sizing solution without adding borax to carry out double-sided surface sizing experiments on paper. Before surface sizing, the raw materials and physical properties of the two groups of paper were the same. After sizing, related tests were carried out on the two groups of papers, and the experimental results are shown in the table below. The control group is the experimental data of double-sided surface sizing of paper with the surface sizing solution without adding borax.
[0024] It can be seen from the table below that the air resistance of the paper surface sized with the surface sizing solution adde...
example 2
[0027] The enzymatic starch is formulated into a surface sizing solution. Then borax was prepared into a solution with a concentration of 3%, added to the surface sizing solution, and mixed evenly. The amount of borax added was 10% of the absolute dry weight of the enzymatic starch. Then use the above-mentioned surface sizing solution after adding borax and the surface sizing solution without adding borax to carry out double-sided surface sizing experiments on paper. Before surface sizing, the raw materials and physical properties of the two groups of paper were the same. After sizing, related tests were carried out on the two groups of papers, and the experimental results are shown in the table below. The control group is the experimental data of double-sided surface sizing of paper with the surface sizing solution without adding borax.
[0028] It can be seen from the table below that the air resistance of the paper surface sized by adding 10% borax to the surface sizing s...
example 3
[0031] The oxidized starch is formulated into a surface sizing solution. Then borax and zinc borate were prepared into 3% concentration solutions, mixed according to the absolute dry mass ratio of 1:9, and added to the surface sizing solution.
[0032]The total amount of boron-containing compound (that is, the mixture of borax and zinc borate) added is 0.1% of the absolute dry weight of the oxidized starch.
[0033] Then use the above-mentioned surface sizing solution after adding the boron-containing compound and the surface sizing solution without adding the boron-containing compound to carry out double-sided surface sizing experiments on the paper. Before surface sizing, the raw materials and physical properties of the two groups of paper were the same. After sizing, related tests were carried out on the two groups of papers, and the experimental results are shown in the table below. The control group is the experimental data of double-sided surface sizing of paper with t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com