Air-permeable and water-absorbent acrylate foam material with silver and zinc anti-bacteria particles, as well as preparation method and application of anti-bacteria air-permeable water-absorbent acrylate foam material

A technology of water-absorbing acrylate and foam materials, applied in absorbent pads, medical science, bandages, etc., can solve problems such as insufficient air permeability, easy breeding of bacteria, and itchy skin, and achieve excellent antibacterial performance, good water absorption, and absorption rate high effect

Active Publication Date: 2015-03-25
佛山市联塑万嘉新卫材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when sanitary products are contaminated by body fluids such as urine, bacteria are likely to breed, which can easily cause skin allergies and other problems; in addition, due to insufficient air permeability, it is also easy to cause itchy skin problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Air-permeable and water-absorbent acrylate foam material with silver and zinc anti-bacteria particles, as well as preparation method and application of anti-bacteria air-permeable water-absorbent acrylate foam material
  • Air-permeable and water-absorbent acrylate foam material with silver and zinc anti-bacteria particles, as well as preparation method and application of anti-bacteria air-permeable water-absorbent acrylate foam material
  • Air-permeable and water-absorbent acrylate foam material with silver and zinc anti-bacteria particles, as well as preparation method and application of anti-bacteria air-permeable water-absorbent acrylate foam material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] S1. Prepare the oil phase system, weigh 7.2g of isooctyl acrylate, 0.8g of isooctyl methacrylate, 4.8g of ethylene glycol dimethacrylate, 0.4g of hexanediol diacrylate, and 1.6g of silver zinc Bacteriostatic particles, Tween-80 1.2g, stir the oil phase evenly for use, wherein the mass ratio of isooctyl acrylate to isooctyl methacrylate is 9:1.

[0053] S2. Prepare the water phase system, weigh 0.096g of calcium chloride, add water to 480g to dissolve it, at this time, the mass fraction of the electrolyte is 0.02%, and wait for use; prepare the initiator phase, and weigh 1.71g of ammonium persulfate , add water to 10g to dissolve, set aside.

[0054] S3. Transfer 320 g of the prepared water phase into a 1000 ml three-necked flask, start stirring, raise the temperature to 75° C., and stir at a speed above 800 rpm, then add the uniformly stirred oil phase and 0.32 g of light calcium carbonate into the three-necked flask , before the emulsion becomes viscous, add 160g of t...

Embodiment 2

[0057] S1. Prepare the oil phase system, weigh 7g of isooctyl acrylate, 1g of isooctyl methacrylate, 4.8g of ethylene glycol dimethacrylate, 0.4g of hexanediol diacrylate, and 1.6g of silver zinc antibacterial Microparticles, Tween-80 1.2g, stir the oil phase evenly for use, wherein the mass ratio of isooctyl acrylate to isooctyl methacrylate is 7:1.

[0058] S2. Prepare the water phase system, weigh 0.096g of calcium chloride, add water to 480g to dissolve it, at this time, the mass fraction of the electrolyte is 0.02%, and wait for use; prepare the initiator phase, and weigh 1.71g of ammonium persulfate , add water to 10g to dissolve, set aside.

[0059] S3. Transfer 320 g of the prepared water phase into a 1000 ml three-necked flask, start stirring, raise the temperature to 75° C., and stir at a speed above 800 rpm, then add the uniformly stirred oil phase and 0.32 g of light calcium carbonate into the three-necked flask , before the emulsion becomes viscous, add 160g of t...

Embodiment 3

[0062] S1. Prepare the oil phase system, weigh 12g of isooctyl acrylate, 1.5g of isooctyl methacrylate, 0.4g of ethylene glycol dimethacrylate, 0.4g of hexanediol diacrylate, and 0.8g of silver-zinc pH Bacteria particles, Tween-80 0.8g, stir the oil phase evenly for use, wherein the mass ratio of isooctyl acrylate to isooctyl methacrylate is 8:1.

[0063] S2. Prepare the water phase system, weigh 0.096g of calcium chloride, add water to 480g to dissolve it, at this time, the mass fraction of the electrolyte is 0.02%, and wait for use; prepare the initiator phase, and weigh 1.71g of ammonium persulfate , add water to 10g to dissolve, set aside.

[0064] S3. Transfer 320 g of the prepared water phase into a 1000 ml three-necked flask, start stirring, raise the temperature to 75° C., and stir at a speed above 800 rpm, then add the uniformly stirred oil phase and 0.32 g of light calcium carbonate into the three-necked flask , before the emulsion becomes viscous, add 160g of the w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses an air-permeable and water-absorbent acrylate foam material with silver and zinc anti-bacteria particles, as well as a preparation method and application of the air-permeable and water-absorbent acrylate foam material. The size of foam cells of the prepared foam material is tiny, the average deionized water absorption rate, the average brine absorption rate, the average artificial urine absorption rate and the average artificial blood absorption rate are all larger than 18g / g, the water retention rate in an hour is more than 85%, and the acrylate foam material is suitable for dispersing and storing fluids containing water; additionally, due to addition of the silver and zinc anti-bacteria particles, the manufactured foam material has good anti-bacteria performance, and the anti-bacterial rate of escherichia coli and staphylococcus aureus are both more than 95%; due to addition of light calcium carbonate, the air penetration amount is larger than 1.5*10-2cm3 / (m2*Pa*d), which shows good air permeability. Therefore, the block-shaped soft water-absorbent material is especially suitable for the field of toilet articles.

Description

technical field [0001] The invention belongs to the field of water-absorbing materials, and in particular relates to a silver-zinc antibacterial breathable water-absorbing acrylate foam material and a preparation method and application thereof. Background technique [0002] In today's hygienic products, the water-absorbing material inside is mainly granular synthetic resin. After absorbing water, urine or blood, it will form a gel, which is easy to form agglomerates, making it difficult to fix in one position. It is very uncomfortable in the actual use process. Comfortable. Therefore, it is of great significance to develop block-shaped soft water-absorbing materials. [0003] Normal blood is composed of blood cells, plasma, etc. The diameter of blood cells is about 8 μm, and the diameter of acrylic acid molecules is much smaller than that of blood cells. Therefore, blood cells are not easily absorbed by the gel-like superabsorbent resin, and can only stay on the surface o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F222/14C08F2/30C08K3/08C08J9/28A61L15/24
Inventor 梁永江
Owner 佛山市联塑万嘉新卫材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com