Forming process of electric wire fixing preformed armor rods
A forming process and pre-twisted wire technology, which is applied in the field of electric wire fixed pre-twisted wire forming process, can solve problems such as hidden dangers and steel wire surface corrosion, and achieve the effects of high twisting strength, good anti-corrosion effect, and reasonable process layout
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] Embodiment 1; A pre-twisted wire forming process for wire fixing, including the following steps:
[0018] (1) The length of the steel wire is sized;
[0019] (2) The steel wire is bent through the bending mechanism, and the steel wire is bent into a wave shape:
[0020] (3) Grind and polish the wave-shaped steel wire in step (2) until the surface is smooth;
[0021] (4) The surface formed in step (3) is quickly subjected to local cleaning treatment, and the treatment time is 20-40 seconds;
[0022] (5) Select groups of steel wires processed in step (4), and group 5 into groups;
[0023] (6) Twist a group of steel wires in the selected group, make each adjacent steel wire stick together, and bundle each group of twisted steel wires;
[0024] (7) Immerse the steel wire group treated in (6) in the glue solution for glue treatment, and then dry it after treatment, with the temperature controlled at 200℃-240℃;
[0025] (8) Mark (7) the steel wire group, lay sand, shank, and bend into sha...
Embodiment 2
[0026] Embodiment 2; A pre-twisted wire forming process for wire fixing, including the following steps:
[0027] (1) The length of the steel wire is sized;
[0028] (2) The steel wire is bent through the bending mechanism, and the steel wire is bent into a wave shape:
[0029] (3) Grind and polish the wave-shaped steel wire in step (2) until the surface is smooth;
[0030] (4) The surface formed in step (3) is quickly subjected to local cleaning treatment, and the treatment time is 20-40 seconds;
[0031] (5) Select groups of steel wires processed in step (4), and group 5 into groups;
[0032] (6) The two ends of each group of steel wires are treated with zinc, and the steel wires are put into the zinc bath. The zinc bath dipping time is 5-10 seconds, and the temperature of the zinc bath is maintained at 450℃-470℃. between.
[0033] (7) Twist a group of steel wires in the selected group, make each adjacent steel wire stick together, and bundle each group of twisted steel wires;
[0034] (...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com