Antibacterial coating

A technology of antibacterial coatings and raw materials, applied in antifouling/underwater coatings, alkali metal silicate coatings, coatings, etc., can solve the problems of strong irritating odor, poor film formation, serious environmental pollution, etc., and achieve antibacterial effect Durable, strong adhesion, good moldability

Inactive Publication Date: 2015-02-18
QINGDAO TONGSHENGTONG RUBBER & PLASTIC
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional oil coatings are mainly composed of organic components, which are toxic, pungent, and pollute the environment seriously, and have poor film-forming properties, resulting in rough surfaces and affecting decorative effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] An antibacterial coating, the formula is composed of the following raw materials in parts by weight: 50 parts of water glass, 20 parts of ethyl α-cyanoacrylate, 5 parts of titanium dioxide, 5 parts of talcum powder, 3 parts of imperate, 2-tert-butyl peroxide 2.5 parts, 0.1 part of glyoxal, 0.1 part of sodium hexametaphosphate, 3 parts of sodium chloride, 2 parts of sodium sulfate, 2 parts of ethylene glycol, 3 parts of borax, 1.5 parts of furanocoumarin, and 1 part of ketone .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an antibacterial coating which comprises the following raw materials in parts by weight: water glass, alpha-ethyl cyanoacrylate, titanium dioxide, talcum powder, cylindrin, di-tert-butyl peroxide, glyoxal, sodium hexametaphosphate, sodium chloride, sodium sulfate, ethylene glycol, borax, furocoumarin and bamboo leaf phenolic ketone. The coating contains natural antibacterial components, is lasting in antibacterial effect, strong in adhesive power and good in mould forming property, and can be widely applied to the surfaces of various objects.

Description

technical field [0001] The invention relates to coatings, in particular to an antibacterial coating. Background technique [0002] Traditional oil coatings are mainly composed of organic components, which are toxic and pungent, causing serious pollution to the environment, and poor film-forming properties, resulting in rough surfaces and affecting decorative effects. Contents of the invention [0003] The object of the present invention is to provide an antibacterial coating aiming at the deficiencies of the prior art. [0004] The technical scheme adopted in the present invention is as follows: a kind of antibacterial coating, formula is made up of the raw material of following parts by weight: 50 parts of water glass, 20 parts of ethyl α-cyanoacrylates, 5 parts of titanium dioxide, 5 parts of talcum powder, 3 parts of imperatae 2.5 parts of di-tert-butyl peroxide, 0.1 parts of glyoxal, 0.1 parts of sodium hexametaphosphate, 3 parts of sodium chloride, 2 parts of sodium ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/02C09D4/04C09D7/12C09D5/14
Inventor 孙梁博王岐山
Owner QINGDAO TONGSHENGTONG RUBBER & PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products