On-batch steel hot galvanizing environment-friendly type multi-effect galvanization helping liquid and use method thereof

A hot-dip galvanizing and environmental-friendly technology, applied in hot-dip galvanizing process, coating, metal material coating process, etc., can solve the problems of zinc storm, large amount of smoke, and rapid rise of iron ions, etc., to reduce costs and reduce Iron salt content, effect of reducing surface tension

Inactive Publication Date: 2014-12-10
钱宏彬
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention not only solves the problems of large amount of smog and excessive zinc that are common in the current electroplating solution, but more importantly, solves the problem of rapid rise of iron ions, so as to reduce the production of zinc dust and zinc slag, reduce the production cost of enterprises, and prolong the Zinc pot service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Prepare 1000L steel batch hot-dip galvanizing environment-friendly multi-effect auxiliary plating solution, which is used for the auxiliary plating process before batch hot-dip galvanizing of steel parts.

[0051] Take zinc phytate 200kg, zinc bromide 50kg, sodium chloride 50kg, manganese chloride 25kg, potassium fluoroaluminate 75kg, tartaric acid 25kg, gallic acid 5kg, perfluoroalkyl ether quaternary ammonium salt cationic surfactant 8kg, balance for water. The 500mm long 50×50×5 angle steel is immersed in the plating flux solution after degreasing→water washing→pickling→water washing. The temperature is controlled at 60°C, the pH value is controlled at 5, and the fluxing time is 6 minutes. The angle steel after galvanizing is quickly dried within 3 to 4 minutes, and hot-dip galvanizing is carried out without drying. When the angle steel is immersed in the zinc solution, there is no zinc explosion, the zinc dust is reduced by nearly two-thirds, and the zinc fume is mi...

Embodiment 2

[0053] Prepare 1000L steel batch hot-dip galvanizing environment-friendly multi-effect auxiliary plating solution for batch of steel parts

[0054] Flux plating process for pre-treatment of calorimetric hot-dip galvanizing.

[0055] Take zinc bromide 200kg, zinc chloride 100kg, magnesium chloride 50kg, sodium chloride 50kg, bismuth chloride 20kg, potassium chloride 100kg, tartaric acid 35kg, phytic acid 5kg, phosphoric acid 5kg, octadecyltrimethylammonium chloride 3kg , coconut oil fatty acid diethanolamide 6kg, surplus is water. A 500mm long 50×50×5 angle steel is immersed in the plating flux after degreasing→water washing→pickling→water washing. The temperature is controlled at 50°C, the pH value is controlled at 3.5, and the fluxing time is 3 minutes. The angle steel after galvanizing is quickly dried within 3 to 4 minutes, and hot-dip galvanizing is carried out without drying. When the angle steel is immersed in the zinc solution, there is no zinc explosion, the zinc dust...

Embodiment 3

[0057] Prepare 1000L steel batch hot-dip galvanizing environment-friendly multi-effect auxiliary plating solution for batch of steel parts

[0058] Flux plating process for pre-treatment of calorimetric hot-dip galvanizing.

[0059] Take zinc phytate 250kg, zinc bromide 50kg, ammonium acetate 50kg, sodium chloride 100kg, barium chloride 25kg, potassium fluoride 75kg, tartaric acid 40kg, phytic acid 5kg, phosphoric acid 5kg, perfluoroalkyl ether quaternary ammonium salt cationic surface Active agent 4kg, coconut oil fatty acid diethanolamide 6kg, balance is water. A 500mm long 50×50×5 angle steel is immersed in the plating flux after degreasing→water washing→pickling→water washing. The temperature is controlled at 55°C, the pH value is controlled at 4, and the fluxing time is 5 minutes. The angle steel after galvanizing is quickly dried within 3 to 4 minutes, and hot-dip galvanizing is carried out without drying. When the angle steel is immersed in the zinc solution, there is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an on-batch steel hot-galvanizing environment-friendly type multi-effect galvanization helping liquid and a use method thereof. Each liter of the on-batch steel hot galvanizing environment-friendly type multi-effect galvanization helping liquid comprises the following substances: a filming agent, an accelerant, a complexing agent, an anti-explosion zinc agent and water. The invention further provides the use method of the on-batch steel hot galvanizing environment-friendly type multi-effect galvanization helping liquid. The use method requires that the working temperature is 50-60 DEG C, the pH value is 3.5-5, and the galvanization time is 3-6 minutes, and a workpiece can be directly fed to a next zinc immersion procedure after galvanization helping without being dried, so that the time is saved, and the efficiency is improved. In addition to the capability of meeting the common requirements of an on-batch steel hot-galvanizing process, the on-batch steel hot-galvanizing environment-friendly type multi-effect galvanization helping liquid further has the characteristics that the energy consumption for heating the galvanization helping liquid is reduced due to adoption of intermediate temperature galvanization helping, the investment is reduced as no drying is needed after galvanization helping, and the energy consumption for drying is reduced; the increase of Fe<2+> in the galvanization helping liquid is effectively controlled, zinc ash and zinc slag are reduced in zinc immersion, no dust is generated, explosion is effectively avoided, and multiple effects that a galvanization helped film layer is uniform and free of galvanization omission, a zinc layer is bright, and the like, are achieved.

Description

technical field [0001] The invention relates to an environment-friendly multi-effect plating aid solution for hot-dip galvanizing in batches of iron and steel and a method for using the same. Background technique [0002] my country's steel output ranks first in the world for many years in a row, and the problem of metal anti-corrosion has been paid more and more attention. The requirements for corrosion-resistant protection of steel parts using hot-dip galvanizing technology are increasing. According to statistics, the annual loss of steel materials due to corrosion accounts for one-fifth of the total output in the world. Corrosion has caused serious damage to modern industry, not only causing serious direct losses, but also causing indirect losses that are difficult to estimate, and even endanger human life and property safety. [0003] Hot-dip galvanizing has been widely used as an effective method for steel to prevent atmospheric corrosion. Compared with other metal an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/06C23C2/02
Inventor 钱宏彬
Owner 钱宏彬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com