Outer wall coating for buildings

A technology for exterior wall coatings and construction, applied in the field of coatings, can solve the problems of poor water resistance and alkali resistance, long drying time, etc., and achieve the effect of smooth surface and long storage time

Active Publication Date: 2014-12-10
广西瑞顺建材有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the above technical problems, the present application provides an exterior wall coating for buildings, which solves the technical problems of the existing exterior wall coatings for buildings such as poor water resistance and alkali resistance, and long drying time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of exterior wall paint for building, its raw material ratio is as follows by weight: 100 parts of acrylic resin solution; 15 parts of zinc naphthenate; 5 parts of ultramarine; 20 parts of xylene; 15 parts of talcum powder; ; 5 parts of light calcium carbonate; 25 parts of tea flower base; 35 parts of titanium dioxide; 50 parts of rosin modified phenolic resin; 10 parts of hydroxyethyl cellulose; 1 part of aluminum sulfate;

[0016] Put zinc naphthenate, ultramarine blue, xylene, talcum powder, rosin glyceride and light calcium carbonate into the ball mill, mill for 30 minutes, then add theophylline, titanium dioxide, rosin modified phenolic resin, hydroxyethyl fiber Add plain and aluminum sulfate, ball mill for 30 minutes, add acrylic resin solution, continue ball milling for 4 hours, and finally, put all the remaining raw materials into the ball mill and ball mill for 30 minutes to obtain the finished product.

[0017] The surface drying time of the product is 2...

Embodiment 2

[0019] A kind of exterior wall paint for building, its raw material ratio is as follows by weight: 100 parts of acrylic resin solution; 30 parts of zinc naphthenate; 10 parts of ultramarine; 30 parts of xylene; 25 parts of talcum powder; ; 15 parts of light calcium carbonate; 35 parts of tea flower base; 45 parts of titanium dioxide; 60 parts of rosin modified phenolic resin; 30 parts of hydroxyethyl cellulose; 10 parts of aluminum sulfate; 15 parts of propylene glycol;

[0020] Put zinc naphthenate, ultramarine blue, xylene, talcum powder, rosin glyceride and light calcium carbonate into the ball mill, mill for 30 minutes, then add theophylline, titanium dioxide, rosin modified phenolic resin, hydroxyethyl fiber Plain and aluminum sulfate, after ball milling for 30 minutes, add acrylic resin solution, continue ball milling for 5 hours, and finally, put all the remaining raw materials into the ball mill and ball mill for 30 minutes to obtain the finished product.

[0021] The ...

Embodiment 3

[0023] A kind of exterior wall coating for building, its raw material ratio is as follows by weight: 100 parts of acrylic resin solution; 25 parts of zinc naphthenate; 8 parts of ultramarine; 25 parts of xylene; 20 parts of talcum powder; 10 parts of light calcium carbonate; 30 parts of tea flower base; 40 parts of titanium dioxide; 55 parts of rosin modified phenolic resin; 20 parts of hydroxyethyl cellulose; 5 parts of aluminum sulfate; 10 parts of propylene glycol;

[0024] Put zinc naphthenate, ultramarine blue, xylene, talcum powder, rosin glyceride and light calcium carbonate into the ball mill, mill for 30 minutes, then add theophylline, titanium dioxide, rosin modified phenolic resin, hydroxyethyl fiber Add plain and aluminum sulfate, ball mill for 30 minutes, add acrylic resin solution, continue ball milling for 4.5 hours, and finally, put all the remaining raw materials into the ball mill and mill for 30 minutes to obtain the finished product.

[0025] The surface dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an outer wall coating for buildings. The outer wall coating is prepared from the following raw materials in parts by weight: 100 parts of an acrylic resin solution, 15-30 parts of zinc naphthenate, 5-10 parts of ultramarine, 20-30 parts of xylene, 15-25 parts of talcum powder, 15-35 parts of glycerol ester of rosin, 5-15 parts of light calcium carbonate, 25-35 parts of a thickening agent, 35-45 parts of titanium dioxide, 50-60 parts of rosin modified phenolic resin, 10-30 parts of hydroxyethyl cellulose, 1-10 parts of fungicide, 5-15 parts of propylene glycol and 10-20 parts of methylbenzene. The outer wall coating for buildings is free of caking, is in a uniform state when being stirred, free of phenomenon such as foaming or powder dropping after the outer wall coating is soaked in water for 15-30 days, smooth in coating surface, free of abnormity when being soaked in alkali water for 15-30 days, long in storage time and can be widely produced and constantly replace existing materials, the surface drying time is 1-2 hours, and the coating film is resistant to brushing and washing for 1200-1800 times.

Description

technical field [0001] The application belongs to the field of coatings, in particular to an exterior wall coating for buildings. Background technique [0002] Paint, traditionally known as paint in China. The so-called paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, oil, or emulsion, with or without adding pigments, fillers, adding Corresponding additives, viscous liquid prepared with organic solvent or talcum powder. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called a coating film, also known as a paint film or a coating." The material coated on the sur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D193/04C09D161/14C09D101/26C09D7/12
Inventor 戴晓宸
Owner 广西瑞顺建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com