Temperature-resistant natural rubber composition for damping member

A natural rubber and composition technology, applied in the field of temperature-resistant natural rubber composition, can solve the problems of short service life, easy aging of rubber ring sleeves, high calorific value, etc., achieve long service life and overcome long-term working defects.

Active Publication Date: 2014-11-05
TAIZHOU CITY GANG YANG RUBBER
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The outboard engine has the characteristics of high frequency vibration and high heat generation, so the shock absorber rubber sleeve on the outboard engine needs to have the characteristics of high elasticity and high temperature resistance. However, the shock absorber rubber sleeve on the outboard engine currently uses Most of the rubber used is ordinary shock-absorbing rubber products, and its elasticity and high temperature resistance cannot meet the requirements, resulting in the aging of rubber ring sleeves, short service life, and poor quality and reliability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Temperature-resistant natural rubber composition for damping member
  • Temperature-resistant natural rubber composition for damping member

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The temperature-resistant natural rubber composition used in this embodiment for shock absorbers is composed of the following raw materials in parts by weight:

[0032] Natural rubber: 100 parts; white carbon black: 15 parts; N220 carbon black: 15 parts; vulcanizing agent (sulfur): 1.5 parts; filler (kaolin): 50 parts; zinc oxide: 5 parts; stearic acid: 2.8 parts ; Antiaging agent RD: 0.8 parts; Antiaging agent MB: 0.8 parts; Accelerator CZ: 3 parts; Dispersant EP418: 2 parts; Coloring agent (iron oxide): 8 parts;

Embodiment 2

[0034] The temperature-resistant natural rubber composition used in this embodiment for shock absorbers is composed of the following raw materials in parts by weight:

[0035] Natural rubber: 100 parts; white carbon black: 25 parts; N330 carbon black: 25 parts; vulcanizing agent (dicumyl peroxide): 1.9 parts; filler (calcium carbonate): 65 parts; magnesium oxide: 6 parts; Zinc stearate: 3.5 parts; antioxidant RD: 2 parts; antioxidant MB: 1.4 parts; accelerator TMTD: 4 parts; dispersant EP2000: 2.8 parts; coloring agent (iron oxide): 10 parts; naphthenic paraffin 45 parts of engine oil.

Embodiment 3

[0037] The temperature-resistant natural rubber composition used in this embodiment for shock absorbers is composed of the following raw materials in parts by weight:

[0038] Natural rubber: 100 parts; white carbon black: 20 parts; N660 carbon black: 20 parts; vulcanizing agent (sulfur): 1.7 parts; filler (kaolin): 58 parts; zinc oxide 4 parts, magnesium oxide 1 part; stearin Acid: 3 parts; Anti-aging agent RD: 1.8 parts; Anti-aging agent MB: 1.7 parts; Accelerator DM: 3.5 parts; Dispersant EP2000: 2.4 parts; Colorant (iron oxide): 9 parts; .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a temperature-resistant natural rubber composition for a damping member. The composition is composed of the following raw materials, by weight, 100 parts of natural rubber, 0.8-2 parts of a dihydroquinoline anti-aging agent, 0.8-2 parts of an imidazole anti-aging agent, 15-25 parts of white carbon black, 15-25 parts of carbon black, 1.5-1.9 parts of a vulcanizing agent, 30-45 parts of naphthenic paraffin machine oil, 5-6 parts of zinc oxide and / or magnesium oxide, 2.8-3.5 parts of eleaostearic acid or zine stearate, 3-4 parts of a promoter, 2-2.8 parts of a dispersant and 50-65 parts of a filler. The sum of weight parts of the dihydroquinoline anti-aging agent and the imidazole anti-aging agent is less than or equal to 3.5 parts. A formula system with the combination of the anti-aging agents RD / MB is selected. With cooperation of the two types of anti-aging agents, experiments show that the optimum effect can be achieved. According to the temperature-resistant natural rubber composition for a damping member, elasticity of natural rubber can fully be maintained, and the defect that natural rubber cannot operate for a long time at 120 DEG C is overcome. The temperature-resistant natural rubber composition provided by the invention is temperature resistant, has high elasticity and has long service life.

Description

technical field [0001] The invention relates to a temperature-resistant natural rubber composition used for a shock absorber, and belongs to the technical field of rubber compositions. Background technique [0002] An outboard motor means that the engine is outside the hull, or directly immersed in water, or above the water surface. At present, outboard motors are mostly used in small-sized hulls such as yachts, such as fishing boats and rubber boats on rivers, and are often found in rivers and lakes where fisheries are intensive. [0003] The outboard engine has the characteristics of high-frequency vibration and high heat generation, so the shock absorber rubber sleeve on the outboard engine needs to have the characteristics of high elasticity and high temperature resistance. However, the shock absorber rubber sleeve on the outboard engine currently uses The rubber used is mostly ordinary shock-absorbing rubber products, and its elasticity and high temperature resistance ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08K13/02C08K5/3437C08K5/37C08K3/36C08K3/04C08K5/01C08K3/22C08K5/09C08K5/098C08K3/34C08K3/26
Inventor 阚智谦丁乃秀林广义孟亮
Owner TAIZHOU CITY GANG YANG RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products