A detection method for the equivalent thickness of the oxide layer on the surface of ultrafine aluminum powder particles

A particle surface and detection method technology, applied in particle size analysis, particle and sedimentation analysis, measuring devices, etc., can solve the problems of lack of precision, cumbersome detection method of micron aluminum powder oxide layer thickness, etc., and achieve high precision and simple detection method Effect

Inactive Publication Date: 2016-12-07
JIANGSU UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a method for detecting the equivalent thickness of the oxide layer on the surface of ultra-fine aluminum powder particles, aiming to solve the problems of cumbersome and lack of precision in the existing detection methods for the thickness of the oxide layer of micron aluminum powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A detection method for the equivalent thickness of the oxide layer on the surface of ultrafine aluminum powder particles
  • A detection method for the equivalent thickness of the oxide layer on the surface of ultrafine aluminum powder particles
  • A detection method for the equivalent thickness of the oxide layer on the surface of ultrafine aluminum powder particles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0032] A method for detecting the equivalent thickness of an oxide layer on the surface of ultrafine aluminum powder particles, comprising the following steps:

[0033] (1) Determination of oxide species: use "D / MAX2500PC X-ray instrument" to detect the X-ray structure of ultrafine aluminum powder samples, analyze the oxide species according to the PDF map, and determine the existence of alumina species in the aluminum powder particles ; figure 1 is the X-ray image of sample No. 1, figure 2 It is the X-ray image of No. 2 sample. The test results show that the aluminum powder particles only cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for detecting the equivalent thickness of the oxide layer on the surface of ultrafine aluminum powder particles. By performing X-ray structure detection on ultrafine aluminum powder samples and analyzing oxide species according to the PDF atlas, it is determined that the oxide layer in the aluminum powder particles is Existence of aluminum species; particle distribution detection of aluminum powder, each sample is tested three times to determine the volume average diameter D of aluminum powder; respectively detect the heat absorption value △H of the raw material 1A99 industrial pure aluminum in the heating process 0 and the heat absorption value △H of the prepared aluminum powder in the heating process, according to the thermodynamic characteristics of the phase transition, determine the mass percentage content of alumina in the aluminum powder particles and the heat absorption value △H0, the heat absorption value △ The relationship between H; the equivalent thickness of the oxide layer is calculated according to the particle structure of the aluminum powder and the mass percentage of alumina. The detection method of the invention is simple and intuitive, conforms to the production process and has high precision.

Description

technical field [0001] The invention belongs to the technical field of material processing and inspection, and in particular relates to a method for detecting the equivalent thickness of an oxide layer on the surface of ultrafine aluminum powder particles. Background technique [0002] Ultrafine aluminum powder has a wide range of applications. It is mainly used as fuel for rocket propulsion in the aerospace industry, and is also used as a primary raw material for military explosives, etc.; it is also used as a raw material for external metallic paints for high-end cars, mobile phones, motorcycles, and bicycles. Or steelmaking degassing, deoxidation, or used in chemical industry, fireworks and firecrackers, etc. [0003] Because ultrafine aluminum powder is an aluminum matrix, it is difficult to detect the oxide content in it by physical and chemical analysis methods. On the other hand, due to the small particle size of the prepared aluminum powder, the general physical det...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G01B21/08G01N15/02
Inventor 傅明喜李冬升
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap