Rare earth europium complex and preparation method for europium red light transparent film based on PVB matrix

A technology of rare earth complexes and europium complexes, which is applied in the field of synthesis of new europium complexes, can solve problems such as poor film transparency and insufficient luminous film strength, and achieve improved coordination ability, excellent luminous efficiency, and good photostability Effect

Inactive Publication Date: 2014-09-24
CHONGQING UNIV OF TECH
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the above-mentioned deficiencies in the prior art, the object of the present invention is to solve the problems of poor transparency of the existing film and insufficient strength of the luminescent film, and provide a novel europium complex and a preparation method thereof;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth europium complex and preparation method for europium red light transparent film based on PVB matrix
  • Rare earth europium complex and preparation method for europium red light transparent film based on PVB matrix
  • Rare earth europium complex and preparation method for europium red light transparent film based on PVB matrix

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Accurately weigh 0.0495g PVB, 0.0005g Eu(TTA) 2 Tpy-OCH 3 , Dissolve Eu(TTA) with an appropriate amount of DMF (N-N-dimethylformamide) 2 Tpy-OCH 3 , Pour the dissolved solution into a beaker, then add 20ml of absolute ethanol and 30ml of THF to make a 1g / L solution. Drop an appropriate amount of the solution into a watch glass with a dropper, and let the solvent evaporate naturally at room temperature.

[0042] Use PVB as a substrate to prepare a film. If the solvent volatilizes faster, the prepared film will turn white, and PVB is not easy to form a film, and it takes a long time to form a film. Therefore, choose to volatilize at room temperature for 36 hours to prepare the complex Eu(TTA) 2 Tpy-OCH 3 The mass is 1% PVB red light film.

[0043] attached figure 1 In , the typical asymmetry of the carbonyl group in TTA occurs at 1600 cm -1 , the absorption peaks at 580 and 460 cm-1 are assigned to the stretching vibration peaks of the europium complexes N→Eu and ...

Embodiment 2

[0048] Accurately weigh 0.2425g PVB, 0.0075g Eu(TTA) 2 Tpy-OCH 3 , Dissolve Eu(TTA) with an appropriate amount of DMF (N-N-dimethylformamide) 2 Tpy-OCH 3 , Pour the dissolved solution into a beaker, then add 20ml of absolute ethanol and 30ml of THF to make a 5g / L solution. Drop an appropriate amount of the solution into a watch glass with a dropper, and let the solvent evaporate naturally at room temperature to prepare the complex Eu(TTA) 2 Tpy-OCH 3 The mass is 5% PVB red light film.

Embodiment 3

[0050] Accurately weigh 0.465g PVB, 0.035g Eu(TTA) 2 Tpy-OCH 3 , Dissolve Eu(TTA) with an appropriate amount of DMF (N-N-dimethylformamide) 2 Tpy-OCH 3 , Pour the dissolved solution into a beaker, then add 20ml of absolute ethanol and 30ml of THF to make a 10g / L solution. Drop an appropriate amount of the solution into a watch glass with a dropper, and let the solvent evaporate naturally at room temperature to prepare the complex Eu(TTA) 2 Tpy-OCH 3 PVB red light film with a mass of 7%.

[0051] It can be clearly seen from the fluorescence test spectrum of the film that the characteristic emission peak of europium ions after doping is still at 617nm. And it can be seen that the luminous intensity of simple europium complexes is not high when dispersed in PVB film, and within the scope of experimental research, it increases with the increase of the content of europium complexes, and does not appear to increase with the increase of the content of europium complexes. Conce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tgaaaaaaaaaa
Thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a rare earth europium complex and a preparation method for europium red light transparent film based on a PVB matrix. A preparation method of the rare earth europium complex Eu(TTA)2Tpy-OCH3 comprises the following steps that Eu(TTA)2.4H2O and Tpy-OCH3 serve as initial raw materials, the molar ratio of the Eu(TTA)2.4H2O to the Tpy-OCH3 is 2:1, tetrahydrofuran serves as solvent, and a reaction is carried out for three hours at 75 DEG C under the backflow condition to obtain the europium complex. The synthesized europium complex and the polyvinyl butyral (PVB) matrix are dissolved with good solvent, and the europium red light film is obtained after the solvent naturally volatilizes completely. According to the rare earth europium complex and the preparation method for the europium red light transparent film based on the PVB matrix, the PVB is creatively selected as the matrix, the prepared novel efficient red light transparent film material has the advantages of the europium complex of being high in color purity and high in luminous efficiency, and the advantage of the PVB matrix of being high in mechanical strength, and the luminous material can be applied to electronic terminals such as computers, television sets and mobile phones, and mainly serves as the luminous material in the field of panel display.

Description

technical field [0001] The invention relates to the synthesis of a novel europium complex and a preparation method of a rare earth europium polymer luminescent film material. [0002] Background technique [0003] As an emerging flat-panel display technology, OLED has the characteristics of all solid state, self-illumination, wide viewing angle, fast response, low power consumption and soft screen, and is considered to be the next generation of dreamy display technology. At present, organic light-emitting display devices are not only widely used in fields such as mobile phone tablets, automotive instruments, and digital cameras, but also at the CES2012 exhibition in 2012, Samsung and LG successively demonstrated epoch-making 55-inch OLED TVs. Panasonic and Apple will also plan to launch large-size OLED TVs. However, red light materials for OLEDs have shortcomings such as low color purity, insufficient thermal stability, and poor film-forming performance, which limit the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C07F5/00C09K11/06
Inventor 杨朝龙刘少君张芝铭尚明勇李川王国霞高宝
Owner CHONGQING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com