Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A preparation method of high-strength and high-conductivity copper alloy wire for automobile wire and cable

A technology for wires, cables and copper alloy wires is applied in the field of preparation of high-strength and high-conductivity copper alloy wires. , the effect of simple process

Inactive Publication Date: 2016-06-29
铜陵新辰汽车制造有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem of conflicting mechanical strength and electrical conductivity of existing copper alloy wires, the present invention provides a method for preparing high-strength and high-conductivity copper alloy wires for automotive wires and cables, while improving the mechanical strength and electrical conductivity of copper alloy wires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A method for preparing a high-strength and high-conductivity copper alloy wire for automobile wire and cable, comprising the following steps:

[0013] (1) Put the copper block into the melting furnace and raise the temperature to 1220°C to melt, then raise the temperature to 1250°C, add the relevant alloy ingredients, stir evenly, after it is completely melted, adjust the temperature to 1230°C and add refining agent to refine for 30 minutes, then grill After slag, heat preservation for 20 minutes; and then carry out rapid chemical analysis on the copper alloy liquid before the furnace, so that the weight percentage of each element in the copper alloy liquid meets the following requirements: Zn1.5-2.5, Cr0.8-1.6, Ni0.5-1.0, Mn0.3-0.6, Ag0.25-0.35, Ti0.1-0.2, Nb0.04-0.08, Sb0.03-0.05, B0.015-0.025, Te0.005-0.015, Ce0.03-0.04, Tm0. 02-0.03, S0.005-0.01, P0.003-0.005, the balance is copper and unavoidable impurities; after analysis, adjust the feed according to the weight p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a high-strength and high-conductivity copper alloy wire for an automotive electric wire and cable. The copper alloy wire comprises the following component elements in percentage by weight: 1.5-2.5% of Zn, 0.8-1.6% of Cr, 0.5-1.0% of Ni, 0.3-0.6% of Mn, 0.25-0.35% of Ag, 0.1-0.2% of Ti, 0.04-0.08% of Nb, 0.03-0.05% of Sb, 0.015-0.025% of B, 0.005-0.015% of Te, 0.03-0.04% of Ce, 0.02-0.03% of Tm, 0.005-0.01% of S, 0.003-0.005% of P and the balance of copper and inevitable impurities. By virtue of the method disclosed by the invention, the mechanical strength of the copper alloy wire can be greatly improved while the excellent electrical conductivity is maintained, and the problem of the contradiction between the mechanical strength and electrical conductivity of the copper alloy wire is effectively solved; the method has the advantages of rapid preparation, simple process, environment friendliness, low cost, high efficiency and convenience in control, and the automatic mass production can be achieved.

Description

technical field [0001] The invention relates to a method for preparing high-strength and high-conductivity copper alloy wires for automobile wires and cables, belonging to the technical field of copper alloy manufacturing. Background technique [0002] Copper alloy wire has excellent electrical conductivity, thermal conductivity, ductility and corrosion resistance, and is widely used in automotive wires and cables. In recent years, with the rapid development of the automobile industry, higher requirements have been placed on the performance of copper alloy wires. However, the strength and conductivity of existing copper alloy wires are often inversely proportional to each other, which affects their performance. Therefore, it is urgent to develop high-strength and high-conductivity copper alloy wires to meet market demand. Contents of the invention [0003] In order to solve the problem of conflicting mechanical strength and electrical conductivity of existing copper alloy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/02C22C1/06C22C9/04C22F1/08B21C37/04
Inventor 徐泽军
Owner 铜陵新辰汽车制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com