A method of making insulation board by using foam glass waste

A foam glass and foam glass powder technology, applied in chemical instruments and methods, solid waste management, sustainable waste treatment, etc., can solve the problems of inability to recycle and utilize, waste pollution, etc., and achieve the effect of economic and social benefits

Active Publication Date: 2016-09-07
JIAXING AOTAI NEW BUILDING MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is very brittle, and a large number of fragments of foam glass are formed in the process of production, transportation and sales. This fragment of foam glass cannot be recycled and utilized, causing waste pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of making insulation board by using foam glass waste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A method for making thermal insulation boards from waste foam glass, which is characterized in that foam glass fragments, foam glass powder, cellulose, rubber powder, cement and lime are mixed evenly with water, cast into a rectangular body by using a mold, and cut into pieces after natural drying Plate-shaped recycled material finished product, the weight ratio of the above foam glass fragments is 64%, the block diameter is 30mm-150mm, the weight ratio of foam glass powder is 16%, the weight ratio of cellulose is 0.24%, the weight ratio of rubber powder The weight ratio of cement is 0.12%, the weight ratio of cement is 15%, and the weight ratio of lime is 4.64%.

[0011] Above-mentioned embodiment has adopted the cellular glass fragment of different sizes,

[0012] Table 1

[0013]

Embodiment 2

[0015] Divide the rectangular body poured by the above method into recycled material sheets, place two recycled material sheets on the upper layer and the lower layer, sandwich a layer of non-recycled material sheets in the middle, and glue them together to make a finished composite insulation board. The indicators are shown in Table 2:

[0016] Table 2

[0017] index Density (kg / m3) Compression (MPa) Thermal conductivity (W / m·K) (25°C) Volume water absorption average value 352 0.75 0.074 4.62%

Embodiment 3

[0019] Divide the rectangular body poured by the above method into recycled material sheets, place two non-recycled material sheets on the upper layer and the lower layer, sandwich a layer of recycled material sheets in the middle, and bond them with glue to make a finished composite insulation board.

[0020] table 3

[0021] index Density (kg / m3) Compression (MPa) Thermal conductivity (W / m·K) (25°C) Volume water absorption average value 284 0.64 0.062 4.23%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for manufacturing a heat-preservation plate by using a foam glass waste material. The method is characterized by comprising the following steps: uniformly stirring foam glass fragments, foam glass powder, cellulose, rubber powder, cement and lime by using water, pouring to obtain a rectangular body by using a mold, naturally drying, and then slitting into a platy reclaimed material finished product, wherein the weight percentage of the foam glass fragments is 60-65%; the block diameter of each foam glass fragment is 30-150mm; the weight percentage of the foam glass powder is 15-17%; the weight percentage of cellulose is 0.2-0.3%; the weight ratio of the rubber powder is 0.1-0.15%; the weight percentage of the cement is 14-16%; the weight percentage of lime is 4-5%; meanwhile, a reclaimed material and a non-reclaimed material are compounded, so that each performance index can be further improved, and more application requirements can be met. More importantly, the method disclosed by the invention is used for creatively solving the difficulties of recycling foam glass fragment wastes, and has economic and social benefits.

Description

technical field [0001] The invention relates to a method for making a heat preservation board, in particular to a method for making a heat preservation board by using foam glass waste. Background technique [0002] The foam glass plate is an inorganic non-metallic glass material made of cullet, foaming agent, modified additive and foaming accelerator, etc., after finely pulverizing and uniformly mixing, then melting at high temperature, foaming and annealing. A light-weight building material with superior performance in heat insulation (cold preservation), sound absorption, moisture resistance and fire prevention. It is very brittle, and a large number of fragments of foam glass are formed in the process of production, transportation and sales. This fragment of foam glass cannot be recycled and utilized, causing waste pollution. Contents of the invention [0003] The purpose of the present invention is to address the above problems, to propose a method for waste utilizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00B32B13/04C04B18/04
CPCY02W30/91
Inventor 樊明祥许益民叶国挺吴国祥
Owner JIAXING AOTAI NEW BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com