Microalloyed weathering steel, cored wire containing iron alloys, application of cored wire, molten steel and preparation method of molten steel

A cored wire and ferroalloy technology is applied to the cored wire of weather-resistant microalloy steel and ferrous alloy and its application, molten steel and its preparation field, and achieves the effect of improving yield strength and high yield strength

Inactive Publication Date: 2014-09-10
SICHUAN PAN YAN TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although vanadium nitride alloys contain vanadium and have high nitrogen content, for different microalloying technology routes in microalloyed steels, especially composite microalloyed steels, such as V-Ti-N, or even V-Ti-Nb -N, also can not meet the demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microalloyed weathering steel, cored wire containing iron alloys, application of cored wire, molten steel and preparation method of molten steel
  • Microalloyed weathering steel, cored wire containing iron alloys, application of cored wire, molten steel and preparation method of molten steel

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The invention provides a method for preparing molten steel. The method comprises: feeding the cored wire of the invention into molten steel to be alloyed with vanadium and nitrogen to perform vanadium-nitrogen alloying.

[0036]According to the preparation method of molten steel of the present invention, in order to facilitate the rapid feeding of the cored wire into the molten steel, and at the same time in order to improve the yield strength of the steel, it is preferable to perform vanadium-nitrogen alloying under dynamic conditions during the vanadium-nitrogen alloying process. The condition can be achieved by shaking or turning the ladle, for example, the ladle can be shaken while the cored wire is being fed into the molten steel in the ladle by the wire feeding device.

[0037] According to the preparation method of molten steel of the present invention, wherein, in the vanadium-nitrogen alloying process, preferably when the cored wire is fed into the molten steel ...

Embodiment 1

[0054] A cored wire A1 (with an outer diameter of 13 mm), comprising a core layer and an outer layer wrapping the core layer, the core layer being composed of vanadium-iron alloy, silicon-manganese nitride and iron alloy powder (with a particle size of 2 mm or less) , the outer layer is a skin made of cold-rolled strip steel (brand St12), wherein, in the powder, contains vanadium-iron alloy (FeV50A, V content is 50.0% by weight, and the rest is Fe and other unavoidable impurity elements): 85% by weight %, silicon manganese nitride (N content is 28% by weight, Si content is 40% by weight, Mn content is 10% by weight, the rest is a small amount of Fe and unavoidable other impurity elements): 10% by weight, iron alloy: 5% by weight %. Among them, the ferroalloy is a mixed alloy of ferro-niobium alloy and ferro-titanium alloy, wherein the weight ratio of ferro-niobium alloy to ferro-titanium alloy is 2:1, and the ferro-niobium alloy is FeNb60 (Nb+Ta content is 65% by weight, the r...

Embodiment 2

[0056] It is the same as the cored wire in Example 1, except that, in the cored wire A2, the weight ratio of the ferro-niobium alloy to the ferro-titanium alloy is 1:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a cored wire containing iron alloys and an application thereof. The cored wire comprises a core and an outer layer wrapping the core, wherein the core is a mixture containing a vanadium-iron alloy, silicon-manganese nitride and the iron alloys; the iron alloys are a titanium-iron alloy and / or a niobium-iron alloy. The invention provides molten steel and a preparation method thereof. The method comprises the step of feeding the cored wire into the molten steel to be subjected to vanadium-nitrogen alloying to carry out vanadium-nitrogen alloying. The invention provides microalloyed weathering steel. The cored wire is used for achieving vanadium-nitrogen alloying of the molten steel, can effectively increase the nitrogen content according to the requirements, without affecting the vanadium content, and can produce vanadium-containing steel with higher nitrogen content according to the requirement of the molten steel. The steel obtained after casting the vanadium-nitrogen alloyed molten steel obtained by carrying out vanadium-nitrogen alloying on the molten steel by adopting the cored wire has high yield strength.

Description

technical field [0001] The invention relates to a cored wire containing iron alloy and its application in vanadium-nitrogen alloying of molten steel, a molten steel and a preparation method thereof, and a weather-resistant microalloy steel. Background technique [0002] Microalloyed steel mainly refers to the steel whose performance can be obviously improved by adding a small amount or a trace amount of certain elements in the steel, especially the strength index of the steel. Under the existing technical conditions, microalloyed steel is mainly obtained by adding a small amount or a trace amount of vanadium, niobium and titanium. The mechanism of microalloying is: after adding vanadium, niobium and titanium as trace elements into molten steel, they combine with carbon and nitrogen in molten steel to form carbon and nitrogen compound particles, namely V(C, N), Nb( C, N) and Ti (C, N) particles, these particles have a certain effect of precipitation strengthening and grain r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D7/00C22C38/12C22C38/14
Inventor 刘明张国才王义成仲剑丽陈平伍兵陆颉毕新强刘斌罗开金张起梦
Owner SICHUAN PAN YAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com