LFT-D (Long Fiber Reinforced Thermoplastic Direct) forming process of composite building template

A technology of LFT-D and building formwork, which is applied in the field of building formwork forming technology, can solve the problems of no building formwork data disclosure, failure to ensure uniform mixing of glass fibers, and inability to flexibly and accurately control the weight of glass fiber added, so as to avoid high costs , the effect of length guarantee

Active Publication Date: 2014-08-20
福建易安特新型建材有限公司
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this invention can obtain longer fiber lengths to reach the requirements of the final product, the D step in the process has the following defects in cutting the roving by the screw in the twin-screw extruder: 1. the process passes the number of screw revolutions and the glass fiber The amount of glass fiber added is controlled by the number of roots, so it is impossible to flexibly and accurately control the weight of glass fiber added, and it is not easy to change the proportion of glass fiber added; ②The method of screw shearing cannot ensure that the glass fiber is evenly mixed in the resin melt; ③Using the present invention The glass fiber is pre-cut by the metering and cutting system to ensure that the glass fiber is pre-dispersed to a certain extent in the PP melt before the two are mixed and dispersed in the screw, which reduces the wear of the screw; ④ the process of the present invention occurs when the glass fiber It can be automatically connected when it is interrupted abnormally, without stopping the processing
[0005] In addition, there is no specific information about the LFT-D process used to prepare building templates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • LFT-D (Long Fiber Reinforced Thermoplastic Direct) forming process of composite building template
  • LFT-D (Long Fiber Reinforced Thermoplastic Direct) forming process of composite building template
  • LFT-D (Long Fiber Reinforced Thermoplastic Direct) forming process of composite building template

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] like figure 1 Shown, the LFT-D molding process of composite building formwork of the present invention comprises

[0024] Step 10. The resin is quantified from the vacuum feeding system to the vector weighing system according to the weight of the template, and then enters the first-stage twin-screw extruder for heating and melting, and then enters the second-stage twin-screw extruder at the same time as the glass fiber at the feed port of the second-stage twin-screw extruder. The screw extruder performs mixing and plasticization, and the weight ratio of the resin to the glass fiber is: 50-70 wt% of the thermoplastic resin and 30-50 wt% of the glass fiber.

[0025] Among them, the glass fiber is sent to the glass fiber metering and cutting device through the glass fiber automatic feeding and conveying system, cut and added to the resin melt according to the set length of 24-25mm, and is subjected to a secondary process by the shearing action of the resin melt. The lengt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an LFT-D (Long Fiber Reinforced Thermoplastic Direct) forming process of a composite building template. The forming process comprises the following steps of (10) performing quantitative measurement on resin from a vacuum feeding system to a vector type weighing system according to the weight of the template; then feeding the resin to a first-stage twin-screw extruder to be heated and fused; feeding into a second-stage twin-screw extruder in a feed opening of the second-stage twin-screw extruder together with glass fibers, so as to be mixed and plasticized, wherein the glass fibers are cut according to the set length of 24 to 25mm by a glass fiber measuring and cutting device and then are added into the fused resin; performing the secondary length change under the shearing action of the fused resin; and (20) uniformly plasticizing by the second-stage twin-screw extruder, cutting raw materials by a second-stage screw die cutter according to the weight of the template, then insulating and conveying to a material taking and displacement position and putting the raw materials into a press mold by a manipulator for pressing and forming. By using the forming process, the glass fibers in a product are long, and the performance of a product is effectively improved.

Description

technical field [0001] The invention relates to a molding process of building templates, in particular to an LFT-D molding process of composite material building templates. Background technique [0002] Most of the internal fiber lengths of the composite templates currently being produced are in the range of 0.2 to 0.4mm due to their technology. Fiber length is the most important factor determining the performance of fiber-reinforced composite materials. Long fibers have a stronger reinforcing effect than short fibers. . The traditional LFT (LFT is the abbreviation of Long-Fiber Reinforce Thermoplastic in English, translated into Chinese as long fiber reinforced thermoplastics or customarily called long fiber reinforced thermoplastic composites) process is a prepreg process, including melt impregnation, solution impregnation and powder Dipping etc. The process of prepreg tape is complicated and the cost is high, which limits the application of LFT process. [0003] The LF...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C69/02B29C47/40B29C47/84
Inventor 王加志王永刚李娜杨玲娜
Owner 福建易安特新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products