Production process for color steel tile

A production process and technology of color steel tiles, which are applied to the surface coating liquid device, pretreatment surface, coating, etc., can solve the problem of affecting the production progress of wear-resistant steel balls, the loss of wear-resistant steel ball factories, and the increase of wear-resistant Problems such as the production cost of steel ball factories can achieve the effect of improving the quality of electrostatic spraying, increasing the service life and avoiding easy oxidation

Inactive Publication Date: 2014-08-13
安徽杰宇力防护设施有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After all, the replacement of color steel tiles increases the production cost of wear-resistant steel ball factories (or similar industry factories), and the replacement of color steel tiles affects the production progress of wear-resistant steel balls, which brings huge losses to wear-resistant steel ball factories.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process for color steel tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A production process of color steel tiles mainly includes the following steps: taking a steel plate with a thickness of 0.8mm and extruding it into such as figure 1 The shape shown; the formed color steel tile is cleaned through the nozzle to remove dust, oil stains and other dirt on the surface of the color steel tile; the color steel tile after spraying and decontamination is dried at a drying temperature of 200°C to remove surface moisture ; Send the color steel tile to the spraying workshop to spray paint powder while it is hot; put the profile into the curing workshop for curing, and the curing temperature is 200°C; when the cured profile is cooled to room temperature, check the film-forming quality of the color steel tile, Eliminate the color steel tiles with defective electrostatic spraying; put the qualified color steel tiles into the ventilated warehouse and prepare for delivery.

Embodiment 2

[0019] A production process of color steel tiles mainly includes the following steps: taking a steel plate with a thickness of 1.6 mm and extruding it into such as figure 1 The shape shown; the formed color steel tile is cleaned through the nozzle to remove dust, oil stains and other dirt on the surface of the color steel tile; the color steel tile after spraying and decontamination is dried at a drying temperature of 300°C to remove surface moisture ; Send the color steel tile to the spraying workshop to spray paint powder while it is hot; put the profile into the curing workshop for curing, and the curing temperature is 210°C; when the cured profile cools to room temperature, check the film-forming quality of the color steel tile, Eliminate the color steel tiles with defective electrostatic spraying; put the qualified color steel tiles into the ventilated warehouse and prepare for delivery.

Embodiment 3

[0021] A production process of color steel tiles mainly includes the following steps: taking a steel plate with a thickness of 2.0mm and extruding it into such as figure 1 The shape shown; the formed color steel tile is cleaned through the nozzle to remove dust, oil stains and other dirt on the surface of the color steel tile; the color steel tile after spraying and decontamination is dried at a drying temperature of 350°C to remove surface moisture ; Send the color steel tile to the spraying workshop to spray paint powder while it is hot; put the profile into the curing workshop for curing, and the curing temperature is 230°C; when the cured profile cools to room temperature, check the film-forming quality of the color steel tile, Eliminate the color steel tiles with defective electrostatic spraying; put the qualified color steel tiles into the ventilated warehouse and prepare for delivery.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process for a color steel tile, mainly comprising the following steps: forming, spraying and cleaning, drying, electrostatic spraying, curing, quality inspection and warehousing. The production process for the color steel tile has the beneficial effects that electrostatic spraying is performed on the color steel tile, the problems of easy oxidation and corrosion of the traditional coating are avoided, so as to prolong the service life of the color steel tile. The color steel tile produced by the method can be used for 20-25 years in high temperatures and corrosive environments. Before spraying on the color steel tile is carried out, cleaning and drying of the color steel tile are performed, the situation that the spraying effect is influenced by the dirt on the surface of a steel sheet is avoided, and the electrostatic spraying quality of the color steel tile is improved.

Description

technical field [0001] The invention relates to a color steel tile, in particular to a production process of a color steel tile. Background technique [0002] Color steel tile is a new type of roof tile building material, because the main material is steel, so it is called steel tile. Because of its different composition materials, it can be divided into baking varnish steel tile and vermiculite steel tile. At present, the production of color steel tiles usually consists of two links, forming and painting (painting). Ningguo City is the capital of wear-resistant steel balls in the country. The top of the wear-resistant steel ball production workshop is colored steel tiles. The production process of wear-resistant steel balls consumes a lot of energy, generates a lot of heat, and generates corrosive gases. Therefore, the wear-resistant steel ball workshop The service life of the color steel tile on the top is relatively short; in general, the service life of the color steel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D3/00B05D1/04
Inventor 汪克忠滕举强
Owner 安徽杰宇力防护设施有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com