Method for freezing and vacuum-drying micro-nanopowder slurry

A freeze-vacuum drying, micro-nano technology, used in drying solid materials, method combination to dry solid materials, drying and other directions, can solve the problem of too wide, small as a few nanometers, as large as tens of micrometers or even hundreds of micrometers, unfavorable. Product application, etc.

Active Publication Date: 2014-07-02
江西竹生富纳米科技有限公司
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of this drying method is prone to agglomeration, causing the particle size distribution of the dried product to be too wide, ranging from a few nanometers to tens of microns or even hundreds of microns, making it unfavorable for the application of subsequent products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for freezing and vacuum-drying micro-nanopowder slurry
  • Method for freezing and vacuum-drying micro-nanopowder slurry

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The structure and effect of the present invention will be described in detail by citing the following embodiments in conjunction with the accompanying drawings. However, it should be understood that the present invention is not limited to the content described below, and all modifications and changes made without violating the spirit or scope of the present invention belong to the scope of the present invention.

[0029] The freeze-vacuum drying method of the micro-nano powder slurry provided by the present invention mainly includes the following steps, wherein the micro-nano powder can be but not limited to bamboo charcoal powder, activated carbon powder, coffee charcoal powder or coconut charcoal powder:

[0030] The first cooling step: put a tray containing a micro-nano powder slurry with a solid content of 20wt% to 30wt% into a closed cavity, and cool the micro-nano powder slurry to -11°C to - At 13°C, the micro-nano powder slurry contains a dispersant and a wetting...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for freezing and vacuum-drying micro-nanopowder slurry. The method for freezing and vacuum-drying the micro-nanopowder slurry comprises the steps of primary cooling, wherein the slurry is placed in a cavity and is cooled; secondary cooling, wherein the cavity is vacuumized to enable the slurry to be cooled again; low temperature and constant temperature maintaining, wherein the slurry is maintained at a low temperature; primary warming, wherein the slurry is warmed stage by stage; secondary warming, wherein the slurry is warmed stage by stage again; high temperature and constant temperature maintaining, wherein the slurry is maintained at a high temperature; material taking, wherein micro-nanopowder is taken out of the cavity. According to the method for freezing and vacuum-drying the micro-nanopowder slurry, the phenomenon of agglomeration of dried micro-nanopowder can be avoided, and compared with a learning method, the particle size distribution range of the dried powder is narrowed.

Description

technical field [0001] The invention relates to a drying method, in particular to a method for freezing and vacuum-drying micronano powder slurry. Background technique [0002] Bamboo charcoal or activated carbon is widely used in air purification, sewage treatment, textile and other fields because of its excellent adsorption, decolorization, and deodorization effects, especially in the textile field. In order to make bamboo charcoal or activated carbon evenly mixed into textiles In the plastic masterbatch of fiber, bamboo charcoal or activated carbon needs to be made into micron or nanometer powder, and then mixed with plastic raw materials to form masterbatch. Taking bamboo charcoal as an example, the traditional method is to grind bamboo charcoal into granules by wet physical ball milling method. For powders with a diameter of about 10nm to 1000nm (that is, micronano), since the product of the wet ball milling method is a slurry containing powder and liquid, it needs to b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): F26B7/00
Inventor 王贵王万贤王万杰
Owner 江西竹生富纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com