Tea foam vitreous enamel produced in Yaozhou kiln and manufacturing method thereof

A manufacturing method and technology of glazed porcelain, which is applied in Yaozhou kiln tea foam glazed porcelain and its manufacturing field, can solve the problems of precise glaze matching, narrow firing range, and difficult manufacturing process, and achieve the effect of high brightness and consistent hair color

Inactive Publication Date: 2014-05-21
孟树锋
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Second, the glaze is so precise, the production process is difficult, and the firing range is so narrow that folk kilns dare not easily lose money to try it, and it has continued to this day.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tea foam vitreous enamel produced in Yaozhou kiln and manufacturing method thereof
  • Tea foam vitreous enamel produced in Yaozhou kiln and manufacturing method thereof
  • Tea foam vitreous enamel produced in Yaozhou kiln and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The tire material of tea foam glaze porcelain according to the present invention is composed of the following raw materials in parts by weight: 40 parts of Yucai crucible, 30 parts of Dongshan crucible, and 30 parts of Shaliang crucible;

[0029] The glaze is composed of the following raw materials in parts by weight: 80 parts of black medicine soil, 5 parts of potassium feldspar and 15 parts of kaolin.

[0030] A manufacturing method of Yaozhou kiln tea foam glazed porcelain is as follows:

[0031] 1) The preparation process of the tire material is: weathering the Yucai crucible, Dongshan crucible, and Shaliang crucible in the open air for more than half a year → put it into the ball mill according to the proportion → add water with 70% weight of the tire material, finely grind for 3-4 hours → Pass through a 180-200 mesh sieve, remove iron in the iron remover, and get the sludge with a residue of <0.3% through a million-hole sieve → refine the mud with a filter press t...

Embodiment 2

[0044] The tire material of tea foam glaze porcelain according to the present invention is composed of the following raw materials in parts by weight: 45 parts of Yucai crucible, 25 parts of Dongshan crucible, and 30 parts of Shaliang crucible;

[0045] The glaze is composed of the following raw materials in parts by weight: 70 parts of black medicine soil, 10 parts of potassium feldspar and 10 parts of kaolin.

[0046] A manufacturing method of Yaozhou kiln tea foam glazed porcelain is as follows:

[0047] 1) The preparation process of the tire material is: weathering the Yucai crucible, Dongshan crucible, and Shaliang crucible in the open air for more than half a year → put it into the ball mill according to the proportion → add water with 70% weight of the tire material, finely grind for 3-4 hours → Pass through a 180-200 mesh sieve, remove iron in the iron remover, and get the sludge with a residue of <0.3% through a million-hole sieve → refine the mud with a filter press ...

Embodiment 3

[0060] The tire material of tea foam glaze porcelain according to the present invention is composed of the following raw materials in parts by weight: 50 parts of Yucai crucible, 25 parts of Dongshan crucible, and 25 parts of Shaliang crucible;

[0061] The glaze is composed of the following raw materials in parts by weight: 80 parts of black medicine soil, 5 parts of potassium feldspar and 15 parts of kaolin.

[0062] A manufacturing method of Yaozhou kiln tea foam glazed porcelain is as follows:

[0063] 1) The preparation process of the tire material is: weathering the Yucai crucible, Dongshan crucible, and Shaliang crucible in the open air for more than half a year → put it into the ball mill according to the proportion → add water with 70% weight of the tire material, finely grind for 3-4 hours → Pass through a 180-200 mesh sieve, remove iron in the iron remover, and get the sludge with a residue of <0.3% through a million-hole sieve → refine the mud with a filter press t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention particularly relates to a tea foam vitreous enamel produced in a Yaozhou kiln and a manufacturing method thereof. The tea foam vitreous enamel is in a matte glazing color which is yellowing in dark brown green; dense crystal points are formed in microcosm and are gorgeous and colorful; the glazing colors comprise cacalia blueness, snakeskin green, color of mud eel's skin, eel yellow, bronze color and the like, thus diversifying the series of the tea foam vitreous enamel. The tea foam vitreous enamel produced in the Yaozhou kiln comprises a tire material and glaze; the tire material comprises the following raw materials in parts by weight: 40-50 parts of Yucai crucible soil, 20-30 parts of Dongshan crucible soil and 15-30 parts of Shaliang crucible soil; the glaze comprises the following raw materials in parts by weight: 70-80 parts of black powder soil, 5-10 parts of potassium feldspa and 10-20 parts of kaolin. The vitreous enamel is prepared by adopting a certain preparation method.

Description

1. Technical field: [0001] The invention specifically relates to a Yaozhou kiln tea foam glazed porcelain and a manufacturing method thereof. 2. Background technology: [0002] Tea foam glaze is named for its color similar to foam tea. The ancients drank tea by crushing the leaf tea into foam and brewing it. The dark yellow rhizomes of the foam tea are dotted in the green tea, and the taste is long. Some literati named the similar glaze color as tea foam glaze. "Tao Ya" said: "Tea leaves are not yellow and mixed with green, enchanting but not vulgar, more colorful than flowers, and as beautiful as jade", which is an earlier record and high praise of tea foam glaze. Tea foam glazed porcelain was first fired occasionally in the black glazed porcelain of Yaozhou kiln in the Tang Dynasty and never seen again. In the Qing Dynasty, Jingdezhen Imperial Kiln Factory was fired from time to time. Because of its preciousness, it is also called "factory official glaze". Runny, with bl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/24C04B33/34C04B41/86
Inventor 孟树锋曹金刚陈水平梁义亭陈雪萍张玉梅
Owner 孟树锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com