Composite printing and dyeing auxiliary as well as preparation method and application of auxiliary

A technology of printing and dyeing auxiliaries and methylol acrylamide, which is applied in the field of composite printing and dyeing auxiliaries and printing and dyeing auxiliaries, can solve the problems of lack of effect, color enhancement, unsatisfactory color protection performance, and increased requirements, so as to improve color fastness, The effect of excellent synergy, broad industrialization prospects and market value

Inactive Publication Date: 2014-04-30
傅科杰
View PDF10 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although there are many dyeing auxiliaries in the prior art, their color enhancement and color protection performance are still not ideal, and the antibacterial and antistatic functions may be missing or have poor effects. With the improvement of public life quality, the antibacterial and antistatic The requirements for multi-functional fabrics such as static electricity are also intensified, which makes the printing and dyeing auxiliaries in the existing market far from meeting people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite printing and dyeing auxiliary as well as preparation method and application of auxiliary
  • Composite printing and dyeing auxiliary as well as preparation method and application of auxiliary
  • Composite printing and dyeing auxiliary as well as preparation method and application of auxiliary

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) 5g of polyoxyethylenediamine with a weight average molecular weight of 1000-2000, 25g of N-methylolacrylamide, 1g of sodium dodecylbenzenesulfonate, 2g of camphor leaf extract, 2g of white orchid extract 1. Put 2g of Chuanqiong extract into the reaction kettle according to the above weight ratio and stir evenly, then heat up to 120°C, add 3g of ammonium persulfate, keep the temperature for 1h, and cool down to 55°C to obtain the reaction solution;

[0044] (2) 3g dirhamnolipid, 1g tannic acid, 2g sodium taurate, 0.5g 1-carboxy-N,N,N-trimethylbetaine, 1.5g tetradecyldimethyl chloride Benzyl ammonium, 1g1-phenoxy-2-propanol, 1g2-p-sulfonic acid anilino-4-chloro-6-β-naphthyloxytriazine and 20g ethanol were added to the above reaction solution in turn, and the temperature was raised to 70 °C and continued to stir for 1 h to obtain a mixed solution;

[0045] (3) Finally, add 5g of silicon dioxide (particle size: 200nm), 0.5g of europium trichloride and 5g of polyethylen...

Embodiment 2

[0047] (1) 15g weight-average molecular weight is 2000-3000 polyoxyethylenediamine, 15g N-methylolacrylamide, 5g sodium dodecylbenzenesulfonate, 3g camphor leaf extract, 3g white orchid extract 1. Put 3g of Chuanqiong extract into the reaction kettle according to the above weight ratio and stir evenly, then heat up to 100°C, add 1g of ammonium persulfate, keep the temperature for 1.5h, cool down to 50°C to obtain the reaction solution;

[0048] (2) Mix 0.5g dirhamnolipid, 2.5g tannic acid, 1g sodium taurate, 3g 1-carboxy-N,N,N-trimethylbetaine, 0.5g tetradecyl dimethyl chloride Benzyl benzyl ammonium, 2g1-phenoxyl-2-propanol, 0.5g2-p-sulfonic acid anilino-4-chloro-6-β-naphthyloxytriazine and 25g ethanol were added to the above reaction solution in sequence, and the temperature was raised To 65°C, continue stirring for 0.5h to obtain a mixed solution;

[0049] (3) Finally, add 1g of silicon dioxide (particle size: 300nm), 1g of europium trichloride and 10g of polyethylene glyc...

Embodiment 3

[0051] (1) 10g of polyoxyethylenediamine with a weight average molecular weight of 3000-4000, 20g of N-methylolacrylamide, 3g of sodium dodecylbenzenesulfonate, 2g of camphor leaf extract, 2g of white orchid extract 1. Put 2g of Chuanqiong extract into the reaction kettle according to the above weight ratio and stir evenly, then heat up to 110°C, add 5g of ammonium persulfate, keep the temperature for 2h, cool down to 55°C to obtain the reaction solution;

[0052] (2) 2g dirhamnolipid, 2g tannic acid, 2.5g sodium taurate, 1.5g 1-carboxy-N,N,N-trimethylbetaine, 3g tetradecyldimethyl chloride Benzyl ammonium, 1.5g of 1-phenoxy-2-propanol, 0.8g of 2-p-sulfonic acid anilino-4-chloro-6-β-naphthyloxytriazine and 15g of ethanol were added to the reaction solution in turn, and the temperature was raised. To 60°C, continue to stir for 1h to obtain a mixed solution;

[0053] (3) Finally, add 3g of silicon dioxide (particle size: 400nm), 0.7g of europium trichloride and 8g of polyethyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite printing and dyeing auxiliary as well as a preparation method and an application of the auxiliary. The composite printing and dyeing auxiliary is prepared by compounding polyethylene glycol diamine, N-methylol acrylamide, sodium dodecyl benzene sulfonate, ammonium persulfate, di-rhamnolipid, a plant extract, tannic acid, sodium taurate, 1-carboxyl-N,N,N-trimethyl polycrylactone, tetradecyl dimethyl ammonium chilride, 1-phenoxy-2-propyl alcohol, 2-p-toluene sulfonic acid phenylamino-4-chloro-6-beta-naphthoxy triazine, silicon dioxide, europium chloride, ethanol and polyethylene glycol 600. As specific polymer components, the plant extract, quaternary ammonium salt, natural amino acid and natural esters are introduced, a rare earth complex is formed and other suitable components are added under compounding and synergistic effects, the composite printing and dyeing auxiliary has excellent technical effects of burnishing, protecting the color and improving the color fastness, and has the certain antibacterial and antistatic functions, and therefore, the composite printing and dyeing auxiliary has a wide industrial application prospect in the textile printing and dyeing industry.

Description

technical field [0001] The invention relates to a printing and dyeing auxiliary agent, more specifically to a multifunctional composite printing and dyeing auxiliary agent, which belongs to the field of preparation of functional fabric materials. Background technique [0002] Printing and dyeing is a necessary process of fabric treatment. Clothes, bedding, decorative curtains, dust jackets, and pendants that people wear in daily life all involve printing and dyeing processes in the preparation process, and fabrics with poor color fastness touch When exposed to water, sweat, sun, saliva or physical friction, the dyes are easy to fall off and fade, affecting the appearance, and the fallen dye molecules or heavy metal ions may be absorbed by the human body through the skin and endanger health. Therefore, auxiliaries are often used in the printing and dyeing process, which are used to improve the effect of dyeing, increase color fastness, etc. There are reports of various print...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P1/44D06P1/607D06P1/613D06P1/642D06P1/62D06P1/673D06P1/653
Inventor 傅科杰保琦蓓傅丹华武莉莉杨力生冯云张弛任清庆
Owner 傅科杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com