Alcohol-soluble letterpress ink

An alcohol-soluble ink technology, which is applied in the field of printing ink, can solve the problems of unsatisfactory substrate adhesion and friction coefficient stability, achieve excellent fluidity, good dispersibility, and overcome the effects of slow water volatilization

Inactive Publication Date: 2014-03-26
SUZHOU YIHENG PRINTING
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the current environmentally friendly inks have greatly improved environmental performance compared with traditional inks, they still cannot achieve satisfactory results in terms of substrate adhesion and friction coefficient stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The present invention prepares an alcohol-soluble letterpress ink, which is composed of the following raw materials in parts by weight: 15 parts of iron oxide red, 35 parts of binder, 15 parts of barium sulfate, 20 parts of absolute ethanol, 91 parts of TX-91, 13 parts 1 part of alcohol, 1 part of di-n-butyltin dilaurate, 0.5 part of vaseline; the connecting material is composed of the following raw materials in parts by weight: 25 parts of polyvinyl butyral resin, 7 parts of acrylic acid monomer, 3 parts of phenolic resin , 4 parts of tung oil, 40 parts of absolute ethanol, 5 parts of nitrocellulose solution, and 0.5 part of paraffin.

Embodiment 2

[0011] The present invention prepares an alcohol-soluble letterpress ink, which is composed of the following raw materials in parts by weight: 20 parts of titanium dioxide, 38 parts of binder, 17 parts of barium sulfate, 25 parts of absolute ethanol, 92 parts of TX-3, tridecanol 2 parts, 2 parts of di-n-butyltin dilaurate, 1 part of vaseline; the connecting material is composed of the following raw materials in parts by weight: 27 parts of polyvinyl butyral resin, 10 parts of acrylic acid monomer, 5 parts of phenolic resin, 6 parts of tung oil, 43 parts of absolute ethanol, 6 parts of nitrocellulose solution, and 1 part of paraffin.

Embodiment 3

[0013] The present invention prepares an alcohol-soluble letterpress ink, which is composed of the following raw materials in parts by weight: 25 parts of lead chrome yellow, 40 parts of binder, 18 parts of barium sulfate, 30 parts of absolute ethanol, 92 parts of TX-92, thirteen parts 3 parts of alcohol, 2 parts of di-n-butyltin dilaurate, 1 part of vaseline; the connecting material is composed of the following raw materials in parts by weight: 28 parts of polyvinyl butyral resin, 13 parts of acrylic acid monomer, 7 parts of phenolic resin , 7 parts of tung oil, 45 parts of absolute ethanol, 7 parts of nitrocellulose solution, and 1.5 parts of paraffin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an alcohol-soluble letterpress ink which is prepared from the following raw materials in parts by weight: 15-25 parts of pigment, 35-40 parts of binder, 15-18 parts of barium sulfate, 20-30 parts of anhydrous ethanol, 1-2 parts of TX-9, 1-3 parts of tridecanol, 1-2 parts of di-n-butyltin dilaurate and 0.5-1 part of vaseline. The binder is prepared from the following raw materials in parts by weight: 25-28 parts of polyvinyl butyral resin, 7-13 parts of acrylic acid monomer, 3-7 parts of phenol aldehyde resin, 4-7 parts of tung oil, 40-45 parts of anhydrous ethanol, 5-7 parts of nitrocellulose solution and 0.5-1.5 parts of paraffin. The ink can be degrade in an alcohol solvent, has the advantages of environmental protection, no pollution, high adhesive force, favorable wear resistance and high glossiness, and is suitable for large-scale industrial production.

Description

technical field [0001] The invention relates to the technical field of printing ink, in particular to a green and environment-friendly ink formula. Background technique [0002] With the continuous improvement of people's quality of life and living environment, people's requirements for energy-saving, low-consumption, non-toxic, non-polluting, and easily degradable products are getting higher and higher, and printing ink is one of the most polluting materials. Solvent-based printing inks contain a large number of toxic and harmful chemicals, including heavy metals, residual solvents, organic volatiles, and polycyclic aromatic hydrocarbons. These toxic and harmful substances can send chemical transfer, so that people are contaminated with toluene, xylene, lead, mercury, arsenic, chromium and other harmful substances in life, work and study. At present, environmentally friendly inks represented by water-based inks, alcohol-soluble inks, and UV inks are increasingly favored by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/033
Inventor 陈明
Owner SUZHOU YIHENG PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products