Well killing polyacrylamide strong gel and preparation method thereof

A technology of polyacrylamide and strong gel, which is applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of limited compressive strength, high cost, poor temperature resistance, etc., and achieve good compressive strength, Effect of High Viscosity Modulus and High Elastic Modulus

Active Publication Date: 2015-10-21
CHINA NAT PETROLEUM CORP CHUANQING DRILLING ENG CO LTD +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problems of high cost, limited compressive strength and poor temperature resistance of well killing polymer gels in the prior art, and provide a polyacrylamide strong gel for well killing and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Well killing polyacrylamide strong gel and preparation method thereof
  • Well killing polyacrylamide strong gel and preparation method thereof
  • Well killing polyacrylamide strong gel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A polyacrylamide strong gel for well killing consists of the following components and contents:

[0027] Base fluid: 1% polyacrylamide, 8% structural enhancer, 8% anti-dehydration agent, 0.2% anti-oxidant, and the balance is water, based on the total mass of the prepared polyacrylamide strong gel for well killing;

[0028] Cross-linking agent: based on the mass fraction of the cross-linking agent relative to the base liquid, the cross-linking agent accounts for 10%.

[0029] The viscosity of the polyacrylamide strong gel is greater than 100000 mPa?s (1.5s -1 , 100℃), the compressive strength reaches 0.4-1.7MPa / 10m.

[0030] In the present invention, the polyacrylamide is a mixture of one or more of nonionic, cationic, anionic and amphoteric polyacrylamide in any proportion.

[0031] In the present invention, the molecular weight of the polyacrylamide is between 1 million and 12 million.

[0032] In the present invention, the structural reinforcing agent is a mixture ...

Embodiment 2

[0039] This embodiment is basically the same as the above-mentioned embodiment, and the main differences are as follows:

[0040] A polyacrylamide strong gel for well killing consists of the following components and contents:

[0041] Base fluid: 6% polyacrylamide, 2% structural enhancer, 0.4% anti-dehydration agent, 4% antioxidant, and the balance is water, based on the total mass of the prepared polyacrylamide strong gel for well killing;

[0042] Cross-linking agent: based on the mass fraction of the cross-linking agent relative to the base liquid, the cross-linking agent accounts for 0.2%.

[0043] A preparation method of polyacrylamide strong gel for well killing, comprising: adding polyacrylamide, antioxidant, anti-dehydration agent and structure enhancer in sequence in water at a stirring speed of 450 rpm / min, and fully dissolving After that, add the cross-linking agent, and gelatinize at 120℃.

[0044] In the present invention, after adding the cross-linking agent, t...

Embodiment 3

[0046] This embodiment is basically the same as the above-mentioned embodiment, and the main differences are as follows:

[0047] A polyacrylamide strong gel for well killing consists of the following components and contents:

[0048] Base fluid: based on the mass of the total polyacrylamide strong gel solution for well killing, 3% polyacrylamide, 4% structural enhancer, 4% anti-dehydrating agent, 2% antioxidant, and the balance is water;

[0049] Cross-linking agent: based on the mass fraction of the cross-linking agent relative to the base liquid, the cross-linking agent accounts for 6%.

[0050] A preparation method of polyacrylamide strong gel for well killing, comprising: adding polyacrylamide, antioxidant, anti-dehydrating agent and structural enhancer in water at a stirring speed of 400 rpm, fully dissolving Finally, add a cross-linking agent and form a gel at 100°C.

[0051] In the present invention, after adding the crosslinking agent, the crosslinking reaction time i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyacrylamide strong gel for well control and a preparation method thereof. The polyacrylamide strong gel for well control consists of the following components in percentage by weight: a base solution comprising 1-6% of polyacrylamide, 2-8% of a structure reinforcing agent, 0.4-8% of an anti-dehydrating agent, 0.2-4% of an antioxidant and the balance of water according to the total solution mass of the prepared polyacrylamide strong gel for well control, and 0.2-10% of a crosslinking agent relative to the mass fraction of the base solution. The polyacrylamide strong gel prepared by the preparation method has the characteristics of high strength, good elasticity, good toughness, good adhesion, high compression strength, good gas tightness and the like, can be directly gelatinized and used in an N80 tube special for an oil field, can be adhered to a sleeve, and can effectively prevent gas from escaping out of a pit shaft to achieve good effects of well control and sealing.

Description

technical field [0001] The invention relates to a polyacrylamide strong gel for well killing and a preparation method thereof. The gel can be used as a well killing material in oil field workover and underbalanced drilling process. Background technique [0002] The development of oil and gas fields requires drilling, completion and workover operations. Conventional killing fluids are easily lost and cause great damage to the formation. In order to solve practical problems in the field, in recent years, oil workers have researched technologies such as low-damage and anti-leakage killing fluid, gel plugging technology, snubbing operation, and underbalanced drilling and completion. The above technologies have their own advantages. 2. Disadvantages, among which the snubbing device has the disadvantage that it takes a lot of time to install the equipment before use, and it takes a lot of time to trip out during use. However, the casing valve, which protects the formation in unde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/40C09K8/44
CPCC09K8/44C09K8/882C09K8/887
Inventor 任雁鹏汪小宇李志航王玉功李勇林梅钦王所良唐冬珠汪成马托王季鹏杨发金娜李童
Owner CHINA NAT PETROLEUM CORP CHUANQING DRILLING ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com