Preparation method of water-saving easily cleaned closestool

A toilet, easy-to-clean technology, used in clay products, other household appliances, household appliances, etc., can solve the problems of product cracking, cracking, uneven density of slurry, etc., and achieve good formability, crack resistance, density, etc. And the effect of good finished product strength and small shrinkage ratio of green body

Inactive Publication Date: 2014-01-01
陈奕煌
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing ceramic toilet products have a grouting process, and the density of the grouted slurry is uneven, which leads to problems such as easy deformation, stress, and cracking. The problem of product cracking and deformation occurs. The ceramic toilet is firing, and it is also prone to high water absorption, easy to absorb sewage, and produce peculiar smell. After a long time, cracks and water leakage will also occur.
When the ceramic toilet is fired improperly, the glaze surface of the toilet is rough, and the internal pipe has no glaze. This kind of toilet is difficult to clean, and a large amount of water is required to clean it once.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing a water-saving and easy-to-clean toilet, comprising 20% ​​white clay, 18% clay, 7% black soil, 15% feldspar, 32% kaolin, and 8% waste porcelain powder to form a ceramic clay raw material Put it into a beater, beat the ceramic mud raw material into a slurry with a beater, add water glass additives to the slurry, and then pour it into a mixer for stirring and mixing evenly to prepare a grouting ceramic slurry.

[0021] Design the toilet mold, inject the grouting ceramic slurry into the toilet mold under high pressure, and dry it automatically. The drying time is between 40 hours. It will be dried automatically, and the water will be evaporated evenly. Made adobe toilet bowl,

[0022] The toilet clay adobe is first dried automatically, the drying time is 73 hours, and the water is evenly evaporated. When the drying degree of the toilet clay adobe reaches 48%, the toilet clay adobe is heated and dried for 26 hours, and the preparation Out of the drie...

Embodiment 2

[0027] A method for preparing a water-saving and easy-to-clean toilet, comprising 20% ​​white clay, 18% clay, 7% black soil, 15% feldspar, 32% kaolin, and 8% waste porcelain powder to form a ceramic clay raw material Use a beater to make slurry, add water glass additives to the slurry, and then pour it into a mixer for stirring and mixing evenly to prepare a grouting ceramic slurry.

[0028] Design the toilet mold, inject the grouting ceramic slurry into the toilet mold under high pressure, and dry it automatically. The drying time is between 38 hours. It will be dried automatically, and the water will be evaporated evenly. After the automatic drying, the demoulding will be carried out. Made adobe toilet bowl,

[0029] The toilet mud adobe is first dried automatically, and the drying time is 76 hours, and the water is evenly evaporated. When the drying degree of the toilet mud adobe reaches 48%, the toilet mud adobe is heated and dried for 28 hours, and the preparation Out of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of closestool technology, and relates to a preparation method of a water-saving easily cleaned closestool. The water-saving easily cleaned closestool is prepared by subjecting a ceramic slurry to grouting, moulding and sintering, wherein the ceramic slurry comprises 18 to 20% of white clay, 18 to 22% of clay, 7 to 9% of black soil, 17 to 19% of feldspar, 30 to 32% of kaolin and 6 to 10% of waste porcelain powder. The water-saving easily cleaned closestool is prepared by high temperature sintering, so that the water-saving easily cleaned closestool is capable of saving more water, and is easy to clean.

Description

technical field [0001] The invention relates to the technical field of toilets, and more particularly, to a method for preparing a toilet. Background technique [0002] Although the production of ceramic products has a history of thousands of years, ceramic toilets have been invented long ago, and people widely use ceramic toilets. The production process of ceramic toilets generally includes the following process steps: mold design; grouting molding, Unmoulded and dried, glazed and fired. [0003] The existing ceramic toilet products have a grouting process, and the density of the grouted slurry is uneven, which leads to problems such as easy deformation, stress, and cracking. The problem of product cracking and deformation occurs. The ceramic toilet is firing, and it is also prone to high water absorption, easy to absorb sewage, and produce peculiar smell. After a long time, cracks and water leakage will also occur. When the ceramic toilet is fired improperly, the glazed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/24C04B33/132
CPCY02P40/60
Inventor 陈奕煌
Owner 陈奕煌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com