Low-carbon olefine oligomerization catalyst and preparation method thereof

A technology of low-carbon olefins and catalysts, which is applied in the field of low-carbon olefin superimposed catalysts and their preparation, which can solve the problems of resin catalysts that are not resistant to high temperatures, sulfonic acid groups are easy to fall off, and poor selectivity, and achieve good stability, High catalytic activity and stability improvement effect

Active Publication Date: 2013-12-18
KAIRUI ENVIRONMENTAL PROTECTION TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the deficiencies in the prior art, the technical problem to be solved by the present invention is to overcome the defects that the sulfonic acid group of the traditional styrene-based cation exchange resin is easy to fall off, the resin catalyst is not resistant to high temperature, the selectivity is not good, and the catalytic activity is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-carbon olefine oligomerization catalyst and preparation method thereof
  • Low-carbon olefine oligomerization catalyst and preparation method thereof
  • Low-carbon olefine oligomerization catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1). Suspension polymerization:

[0032] Step 1) Preparation of water phase:

[0033] In parts by weight, add 100 parts of water, 0.5 parts of polyvinyl alcohol, and 2 parts of inorganic dispersants into the reactor, and stir evenly;

[0034] Step 2) Preparation of oil phase:

[0035] In parts by weight, 100 parts of styrene and 10 parts of divinylbenzene monomers are added with N-vinylpyrrolidone accounting for 3% of the total monomers and trifluorobenzene accounting for 1% of the total monomers. Ethylene participates in the polymerization, then add 2 parts of peroxide initiator, 35 parts of porogen, and stir evenly;

[0036] Step 3) Suspension Polymerization:

[0037] Add the oil phase solution prepared in step 2) to the reaction kettle with the prepared water phase in step 1), stir, then react at 70°C for 16 hours, discharge after the reaction, and wash the obtained polymerized white balls to The water is clear, and the porogen is extracted after drying.

[0038]...

Embodiment 2

[0041] In step 2), N-vinylpyrrolidone, which accounts for 1% of the total amount of monomers, is added, and the other steps are exactly the same as in Example 1, and the sample number is KR02.

Embodiment 3

[0043] In step 2), N-vinylpyrrolidone, which accounts for 5% of the total amount of monomers, is added, and the other steps are exactly the same as in Example 1, and the sample number is KR03.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a low-carbon olefine oligomerization catalyst and a preparation method thereof. A monomer N-vinyl pyrrolidone and trifluorostyrene are added to participate into polymerization in a polymerization process, and then sulfonated to generate the syrene cation exchange resin containing pyrrolidone in a skeleton. The catalyst disclosed by the invention has a high temperature resistant characteristic, is good in stability and yield of liquid products, and still can keep high catalytic activity after running for a long period of time. The resin catalyst disclosed by the invention is suitable for C3 and C4 olefine oligomerization reaction, so as to prepare C6-C16 olefins, and is especially suitable for a technology for producing nonene and laurylene by virtue of propylene oligomerization, a technology for producing a high-octane gasoline by C4 olefin oligomerization, a technology for producing isooctane by virtue of isobutene dimerization, and the like.

Description

technical field [0001] The invention relates to a catalyst and a preparation method thereof, in particular to a low-carbon olefin composite catalyst and a preparation method thereof. technical background [0002] Superposition, also known as oligomerization, is a process in which two or more low-molecular-weight olefins catalyze the synthesis of a larger olefin molecule. In petroleum refineries, it is often used in the processing and utilization of refinery gas to superimpose propylene and butene to form a mixture of dimers, trimers and tetramers. The lamination process is divided into selective lamination and non-selective lamination according to the composition of raw materials. Macroporous strongly acidic ion exchange resins are currently widely used superposition catalysts at home and abroad. Snamprogetti, Fortum, UOP, CDTECH, etc. all use macroporous strong acidic ion exchange resins in the superposition reaction technology of C4 light olefins as a catalyst. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J31/10C08F212/08C08F212/36C08F226/10C08F214/18C08F8/36C08J9/26C07C2/28C07C11/02
CPCY02P20/52
Inventor 张勇王金明
Owner KAIRUI ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com