Room temperature-curing environment-friendly anticorrosive coating for circuit board and preparation method thereof

A room temperature curing, anti-corrosion coating technology, applied in anti-corrosion coatings, polyester coatings, polyurea/polyurethane coatings, etc., can solve health hazards and other problems, and achieve the effect of strong adhesion, low odor and fast curing speed

Inactive Publication Date: 2013-09-18
DONGGUAN BAOHAN LIGHT IND TECH
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to, aiming at the above-mentioned defects of the prior art, solve the problem that the existing conformal paint contains toluene, xylene, and other aromatic solvents that are harmful to health, and provide a room temperature curing environment-friendly anticorrosion coating for circuit boards. Relating to the method for preparing the anticorrosion coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Provide a room temperature curing environment-friendly anti-corrosion coating for circuit boards, which is made by mixing the following raw materials, each raw material is counted by parts, including: 50-90 parts of polyurethane modified alkyd resin, 20-80 parts of solvent, and main drier 0.01-2.0 parts, secondary drier A 0.01-3.0 parts, secondary drier B 0.01-6.0 parts, fluorescent agent 0.1-3.0 parts and stabilizer 0.01-2 parts.

Embodiment 2

[0017] Embodiment 2: Among them: 50 parts of polyurethane modified alkyd resin, 80 parts of solvent, 2.0 parts of main drier, 3.0 parts of secondary drier A, 6.0 parts of secondary drier B, 3.0 parts of fluorescent agent and stabilizer 2 share.

Embodiment 3

[0018] Example 3: Among them: 90 parts of polyurethane modified alkyd resin, 20 parts of solvent, 0.01 part of primary drier, 0.01 part of secondary drier A, 0.01 part of secondary drier B, 0.1 part of fluorescent agent and 0.01 part of stabilizer .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a room temperature-curing environment-friendly anticorrosive coating for a circuit board and a preparation method thereof. The anticorrosive coating is prepared through complex formulation of the following raw materials by mass: 50 to 90 parts of a polyurethane modified alkyd resin, 20 to 80 parts of an environment-friendly solvent, 0.01 to 2.0 parts of a main drier, i.e., cobalt naphthenate, 0.01 to 3.0 parts of a secondary drier A which is one or two selected from the group consisting of zinc isocaprylate and zinc naphthenate, 0.01 to 6.0 parts of a secondary drier B which is one or two selected from the group consisting of zircon isocaprylate and zirconium naphthenate, 0.1 to 3.0 parts of a fluorescent agent and 0.01 to 2 parts of a stabilizing agent. The tri-proof coating for the circuit board provided by the invention uses a plant extract as a resin source and is prepared through complex formulation of the resin, the environment-friendly solvent, corresponding metal driers and other auxiliary agents. The prepared coating does not contain aromatic solvents like xylene and ethylbenzene and has the advantages of little smell, a fast curing speed, good adhesion and excellent electrothermal performance.

Description

technical field [0001] The invention relates to an anti-corrosion coating, in particular to an anti-corrosion coating for a room temperature curing environment-friendly circuit board, and also relates to a method for preparing the anti-corrosion coating. Background technique [0002] The three anti-paints commonly used in the market are mainly composed of silicone, polyurethane, acrylic resin, epoxy resin and other types. The traditional paint production process comes from the large chemical industry, so it is inevitable to introduce aromatic hydrocarbons such as xylene and ethylbenzene as solvents. This kind of solvent has a strong smell and is very harmful to the health of workers. The curing time, electrical properties, thermal properties, etc. cannot meet the increasingly sophisticated development of the electronics industry. Contents of the invention [0003] The purpose of the present invention is to solve the problem that aromatic solvents such as toluene and xyle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D175/14C09D7/12C09D5/08
Inventor 石学堂苏晓明高鹏飞
Owner DONGGUAN BAOHAN LIGHT IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products