Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

A kind of fly ash-made petroleum fracturing proppant and preparation method thereof

A fracturing proppant and fly ash technology, applied in chemical instruments and methods, earthwork drilling, clay products, etc., can solve the problems of restricting the development of fracturing proppant, high energy consumption, etc. Good wetting performance

Active Publication Date: 2015-12-23
HEBI TIANRUI PETROLEUM PROPPANT
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Chinese patent with the application number 02157202.X is currently a commonly used formula for proppant production and entrepreneurship, but the fracturing proppant provided by this patent relies on super-grade bauxite or first-grade bauxite and MnO 2 High-quality resources such as manganese ore with a content of more than 50% are prepared at relatively high temperatures. Therefore, high energy consumption and high resource consumption in the preparation process limit the further development of fracturing proppants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The present invention also provides a kind of preparation method of fly ash-made oil fracturing proppant, comprising the following steps:

[0036] A) Mix fly ash, potassium feldspar powder and bauxite powder, perform homogenization and refinement treatment, and sieve after granulation to obtain a mixture;

[0037] B) After the mixture is fired and sieved, the proppant for petroleum fracturing pressure made from fly ash is obtained.

[0038] In the present invention, firstly, the fly ash, potassium feldspar powder and bauxite powder are mixed for homogenization and refinement treatment, and there is no special limitation on the manner of the homogenization and refinement treatment, and the specific method is as follows:

[0039] The fly ash, potassium feldspar powder and bauxite powder are placed in a forced mixer for homogenization and refinement. In the invention, the raw material is homogenized and refined, so that the particle size distribution of the raw material i...

Embodiment 1

[0056] After mixing 50Kg of dust removal waste ash from Hebi Wanhe Power Plant, 25Kg of potassium feldspar powder, and 25Kg of bauxite powder with an aluminum content of 70%, it is homogenized and refined by a forced mixer, then granulated, and the particle size is obtained by sieving. 900-600μm mixture, the mixture is fired at 1180-1220℃ for 4 hours in a rotary kiln with a size of 2.5m x 45m under normal pressure, and the mesh size of 20-40 mesh can be obtained after cooling and screening. (850~425μm) fly ash to make petroleum fracturing proppant.

[0057] The bulk density of the petroleum fracturing proppant measured by the fly ash is 1.60g / cm 3 , the apparent density is 2.7g / cm 3 , Under the closing pressure of 86Mpa, the broken rate is ≤7%.

Embodiment 2

[0059] After mixing 60Kg of waste dust from Hebi Wanhe Power Plant, 15Kg of potassium feldspar powder, and 25Kg of bauxite powder with an aluminum content of 70%, it is homogenized and refined by a forced mixer, then granulated, and the particle size is obtained by sieving. 900-600μm mixture, the mixture is fired at 1140-1200°C for 4 hours in a rotary kiln with a size of 2.5m x 45m under normal pressure, and the mesh size of 20-40 mesh can be obtained after cooling and screening. (850~425μm) fly ash to make petroleum fracturing proppant.

[0060] The bulk density of the petroleum fracturing proppant measured by the fly ash is 1.56g / cm 3 , the apparent density is 2.66g / cm 3 , Under the closing pressure of 86Mpa, the broken rate is ≤7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

Provided is a petroleum fracturing proppant prepared from flyash, the petroleum fracturing proppant being prepared from the following components: 1 wt.% - 60 wt.% of flyash; 1 wt.% - 30 wt.% of potassium feldspar powder, and the balance being bauxite powder. The present invention utilizes low-cost flyash as raw material, and in the preparation process, Al2O3 in the flyash is prepared into mullite, and the surplus SiO2 in the raw material is converted into a low apparent-density mineral such as tridymite, etc., thus reducing the apparent density of the product; K2O in the potassium feldspar powder is used as mineralizer to further densify the material, thus increasing the strength of the petroleum fracturing proppant. In addition, when dissolved to a certain concentration, Al2O3 and SiO2 in the raw material react with each other to give acicular mullite for crystallization, followed by continuous dissolution and crystallization, such that the solid phase reaction of the mullite is transformed into a liquid phase reaction, thus greatly accelerating the reaction and reducing the temperature required for the reaction.

Description

technical field [0001] The invention belongs to the technical field of petroleum fracturing proppants, and in particular relates to a fly ash-made petroleum fracturing proppant and a preparation method thereof. Background technique [0002] In oilfield oil and gas extraction, fracturing technology is widely used in order to increase oil well production, prolong oil well high-yield life, and exploit difficult-to-use resources. In order to prevent the closure of underground fractures, preserve oil and gas channels, and maintain flow conductivity, proppant must be used to fill fractures. Due to different depths of oil layers and different oil viscosities, the requirements for proppant properties such as strength, apparent density, and particle size are also different. According to the bulk density, fracturing proppants are divided into three categories: high-density and high-strength, medium-density and high-strength, and low-density and high-strength. In recent years, there h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/80C04B33/135
CPCC04B33/1352C04B35/185C04B35/62204C04B35/62695C04B2235/3217C04B2235/3267C04B2235/3472C04B2235/77C04B2235/78C09K8/80Y02P40/60
Inventor 张胜杰张林群王英军
Owner HEBI TIANRUI PETROLEUM PROPPANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com