Ni-base alloy material and preparation method thereof

A technology of alloy materials and base alloys, which is applied in the field of Ni-base alloy materials and their preparation, can solve the problems that cannot fully satisfy the needs of engines and gas turbines, and achieve the effects of good high-temperature mechanical properties, long-term high-temperature durability, and uniform distribution

Active Publication Date: 2013-05-01
常州优磁科技有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the high-temperature durable life and high-temperature mechanical properties of the existing Rene'220 alloy cannot fully meet the needs of engines and gas turbines used in aviation, aerospace, military industry, thermal power plants, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ni-base alloy material and preparation method thereof
  • Ni-base alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The composition and weight percentage of formula 1: C 0.03%, Cr 18.8%, Co 12%, Nb 4.5%, Mo 3.2%, Al 0.5%, Ti 1.0%, Ta 3.0%, B 0.008%, and Ni .

[0019] According to formula 1, the ingredients are put into a vacuum induction furnace for smelting to obtain alloy liquid. The molten alloy is cast at a casting temperature of 1390°C and a mold temperature of 960°C, and cooled to room temperature within about 10 minutes to obtain an alloy ingot.

[0020] The alloy ingots are processed in turn as follows:

[0021] Pre-treatment: put the alloy ingot in a heat treatment furnace, heat up to 1140°C, keep it warm for 4 hours, take it out and cool it in air; put the alloy ingot in a heat treatment furnace, heat it up to 1090°C, keep it warm for 1 hour, take it out and air cool it;

[0022] Intermediate treatment: place the alloy ingot in a heat treatment furnace, heat up to 950°C, keep it warm for 2 hours, take it out and cool it in air;

[0023] The first stage of aging treatment...

Embodiment 2

[0027] The composition and weight percentage of formula 2: C 0.03%, Cr 18.8%, Co 12%, Nb 4.5%, Mo 3.2%, Al 0.5%, Ti 1.0%, Ta 3.0%, B 0.010%, the rest is Ni .

[0028] According to formula 1, the ingredients are put into a vacuum induction furnace for smelting to obtain alloy liquid. The molten alloy is cast at a casting temperature of 1390°C and a mold temperature of 960°C, and cooled to room temperature within about 10 minutes to obtain an alloy ingot.

[0029] The alloy ingots are processed in turn as follows:

[0030] Pre-treatment: Put the alloy ingot in a heat treatment furnace, heat it up to 1140°C, keep it warm for 4 hours, take it out and cool it in air; put the alloy ingot in a heat treatment furnace, heat it up to 1090°C, keep it warm for 1 hour, take it out and air cool it;

[0031] Intermediate treatment: place the alloy ingot in a heat treatment furnace, heat up to 950°C, keep it warm for 2 hours, take it out and cool it in air;

[0032] The first stage of agin...

Embodiment 3

[0036] The composition and weight percentage of formula 3: C 0.03%, Cr 18.8%, Co 12%, Nb 4.8%, Mo 3.2%, Al 0.5%, Ti 1.0%, Ta 2.5%, B 0.011%, the balance is Ni.

[0037] According to formula 1, the ingredients are put into a vacuum induction furnace for smelting to obtain alloy liquid. The molten alloy is cast at a casting temperature of 1390°C and a mold temperature of 960°C, and cooled to room temperature within about 10 minutes to obtain an alloy ingot.

[0038] The alloy ingots are processed in turn as follows:

[0039] Pre-treatment: put the alloy ingot in a heat treatment furnace, heat up to 1140°C, keep it warm for 4 hours, take it out and cool it in air; put the alloy ingot in a heat treatment furnace, heat it up to 1090°C, keep it warm for 1 hour, take it out and air cool it;

[0040] Intermediate treatment: place the alloy ingot in a heat treatment furnace, heat up to 950°C, keep it warm for 2 hours, take it out and cool it in air;

[0041] The first stage of aging...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a Ni-base alloy material and a preparation method thereof, relating to the field of a high-temperature material. The material comprises the following components in percentage by weight: 0.02-0.03 percent of C, 18-19 percent of Cr, 12-13 percent of Co, 4.5-4.8 percent of Nb, 3.2-3.3 percent of Mo, 0.4-0.6 percent of Al, 0.8-1.2 percent of Ti, 2.5-3.0 percent of Ta, 0.008-0.011 percent of B and the balance of Ni. The preparation method of the Ni-base alloy material comprises the following steps of: proportioning, smelting and casting to obtain an alloy ingot; heating the alloy ingot to 1,135-1,145 DEG C, preserving heat and air-cooling; heating to 1,085-1,095 DEG C, preserving heat and air-cooling; heating to 940-960 DEG C, preserving heat and air-cooling; heating to 820-840 DEG C, preserving heat and cooling with a furnace; and heating to 745-765 DEG C, preserving heat and air-cooling. The material has longer high-temperature long-term life and good high-temperature mechanical performance.

Description

technical field [0001] The invention relates to the field of high-temperature materials such as engines and gas turbines used in aviation, aerospace, military industry, thermal power plants, etc., and specifically relates to a Ni-based alloy material and a preparation method thereof. Background technique [0002] Rene'220 alloy is a Ni-Cr-Co-based high-temperature resistant alloy developed on the basis of Ni-Cr-Fe-based alloy Inconel718 in the United States. Compared with Inconel718, Co is used in Rene'220 alloy instead of Fe, and Ta content. Due to the removal of Fe in the new alloy, the influence of the harmful phase Laves is reduced. And after replacing Fe with Co, the durable life of the alloy can be greatly improved. The increase of Ta causes the alloy to form a large number of precipitation strengthening phases during aging, which makes up for the strength loss caused by the removal of Fe. The compositional design of the Rene’220 alloy increases the stability of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C19/05C22F1/10
Inventor 王玲于永泗姚义俊娄琅洪朱耀宵
Owner 常州优磁科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com