A fire-resistant, flame-resistant and anti-corrosion coating

A technology of anti-corrosion coatings and anti-corrosion materials, applied in the field of coatings, can solve problems such as poor resistance to strength, poor adhesion, and poor water resistance, and achieve the effects of enhancing flame resistance, promoting firmness, and improving safety

Active Publication Date: 2016-02-24
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] In view of the deficiencies in the prior art, one of the purposes of the present invention is to provide a fire-resistant, flame-resistant and anti-corrosion coating, which solves the technical defects of existing products such as poor water resistance, non-fire resistance, poor adhesion and poor strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A fire-resistant, flame-resistant and anti-corrosion coating
  • A fire-resistant, flame-resistant and anti-corrosion coating
  • A fire-resistant, flame-resistant and anti-corrosion coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] The present embodiment adopts following formula to prepare coating:

[0059] The main ingredient is composed of the following components according to the mass percentage:

[0060]

[0061]

[0062] Wherein the mass ratio of the main agent to the cashew nut shell oil modified polyamide K54 is 3:1, and the anticorrosion material is a mixture of silica micropowder and micaceous iron oxide ash.

[0063] The preparation method is as follows: dispersion→sanding→paint mixing→inspection→filtering→packaging.

[0064] The paint was tested and the test results are shown in Table 1.

Embodiment 2

[0066] The present embodiment adopts following formula to prepare coating:

[0067] The main ingredient is composed of the following components according to the mass percentage:

[0068]

[0069] Wherein the mass ratio of the main agent to the cashew nut shell oil modified amine is 8:1, and the anti-corrosion material is silicon micropowder.

[0070] The preparation method is as follows: dispersion→sanding→paint mixing→inspection→filtering→packaging.

[0071] The paint was tested and the test results are shown in Table 1.

Embodiment 3

[0073] The present embodiment adopts following formula to prepare coating:

[0074] The main ingredient is composed of the following components according to the mass percentage:

[0075]

[0076] Wherein the mass ratio of the main agent to the cashew nut shell oil modified amine is 5:1, and the anticorrosion material is silicon micropowder and / or micaceous iron oxide ash.

[0077] The preparation method is as follows: dispersion→sanding→paint mixing→inspection→filtering→packaging.

[0078] The paint was tested and the test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fireproof, flame-resistant and anticorrosive paint. The fireproof, flame-resistant and anticorrosive paint comprises the following components in percentage by weight: main agents consisting of 15-40% of epoxy resin, 0.1-1.5% of flame retardant, 5-25% of antimonous oxide, 10-30% of metal phosphate, 5-25% of polyamine phosphate, 3-12% of pentaerythritol, 5-25% of halogenous resin and 3-15% of an anticorrosive material; and a curing agent, wherein the mass ratio of the main agents to the curing agent is 3:1 to 8:1; and the anticorrosive material is silica powder and / or mica iron oxide ash. The fireproof, flame-resistant and anticorrosive paint provided by the invention is waterproof, can be used indoors and outdoors, and has fire resistance, good adhesive and excellent tensile strength.

Description

technical field [0001] The invention relates to the field of coatings, in particular, the invention relates to a fire-resistant, flame-resistant and anti-corrosion coating. Background technique [0002] Fireproof coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. The fire retardant coating is coated on the surface of the substrate. In addition to its flame retardant effect, it also has anti-rust, waterproof, anti-corrosion, wear-resistant, heat-resistant, coating toughness, colorability, adhesion, easy-drying and a certain gloss, etc. performance. [0003] The fire prevention mechanism of fire retardant coatings can be roughly summarized into the following five points: [0004] (1) The fire retardant coating itself is flame retardant or non-combustible, so that the protected substrate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/18C09D5/08
Inventor 王和山
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com