A technology of release agent and cast iron machine, which is applied in the direction of casting molding equipment, casting molds, casting mold components, etc., can solve the problems of poor performance, achieve low production costs, improve working conditions, and stabilize chemical properties

Inactive Publication Date: 2013-03-27
高金菊
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problem of poor performance of the release agent for cast iron machines in the prior art, and provides a preparation method for the release agent for cast iron machines. The release agent prepared by the invention is used to coat cast iron After the inner surface of the mould, an effective isolation is formed between the molten iron and the cast iron mold, and the cast iron ingot can fall off the cast iron mold smoothly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The preparation method of the release agent of the present embodiment, its steps are as follows:

[0036] (1) Weigh 17kg of soybean oil and 17kg of bentonite, mix and stir the above soybean oil and bentonite in a mixer for 25 minutes at a stirring speed of 200 r / min, and mix well to obtain mixture A;

[0037] (2) Weigh 20kg of blast furnace gas mud according to the mass ratio, 10kg of dust removal dust from the sintering machine head, and 16kg of dust removal dust from the mine trough in front of the furnace. The particle size can be 38-74 microns, and the above-mentioned blast furnace gas mud, sintering machine head electric dust removal dust and furnace front mine tank dust removal dust are mixed, and after mixing, they are roasted at a temperature of 800 ° C for 30 minutes to obtain a mixture B;

[0038] (3) Weigh 5kg of limestone, 10kg of alumina, 11kg of dolomite, 4kg of zirconia, and 7kg of iron red epoxy ester primer according to the mass ratio, and mix the abov...

Embodiment 2

[0043] The preparation method of the release agent of the present embodiment, its steps are as follows:

[0044] (1) Weigh 16kg of soybean oil and 18kg of bentonite, mix and stir the above soybean oil and bentonite in a mixer for 28 minutes at a stirring speed of 150 r / min, and mix well to obtain mixture A;

[0045] (2) Weigh 23kg of blast furnace gas mud according to the mass ratio, 11kg of dust removal dust from the sintering machine head, and 19kg of dust removal dust from the mine trough in front of the furnace. The particle size can be 38-74 microns, and the above-mentioned blast furnace gas mud, sintering head electric dust removal dust and furnace front mine tank dust removal dust are mixed, and after mixing, they are roasted at a temperature of 700 ° C for 32 minutes to obtain a mixture B;

[0046](3) Weigh 6kg of limestone, 9kg of alumina, 13kg of dolomite, 5kg of zirconia, and 8kg of iron red epoxy ester primer according to the mass ratio, and mix the above limeston...

Embodiment 3

[0051] The preparation method of the release agent of the present embodiment, its steps are as follows:

[0052] (1) Weigh 15kg of soybean oil and 19kg of bentonite, mix and stir the above soybean oil and bentonite in a mixer for 30 minutes at a stirring speed of 100 r / min, and mix well to obtain mixture A;

[0053] (2) Weigh 25kg of blast furnace gas mud according to the mass ratio, 13kg of dust removal dust from the sintering machine head, and 23kg of dust removal dust from the mine trough in front of the furnace. The particle size can be 38-74 microns, and the above-mentioned blast furnace gas mud, sintering machine head electric dust removal dust and furnace front mine trough dust removal dust are mixed, and then roasted at a temperature of 600 ° C for 35 minutes to obtain a mixture B;

[0054] (3) Weigh 7kg of limestone, 9.5kg of alumina, 15kg of dolomite, 3kg of zirconia, and 7.5kg of iron red epoxy ester primer according to the mass ratio, and mix the above-mentioned l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a releasing agent for an iron casting machine, belonging to the technical field of releasing agents for metallurgy casting. The preparation method disclosed by the invention comprises the following steps of: weighing 15-17 parts of soybean oil and 17-19 parts of bentonite according to the mass ratio, and uniformly mixing to obtain a mixture A; weighing 20-25 parts of blast sludge, 10-13 parts of electric dust-removing ash of a sintering machine head and 16-23 parts of dust-removing ash of a bunker in the front of a furnace according to the mass ratio, uniformly mixing, and roasting at 600-800 DEG C for 30-35 min to obtain a mixture B; weighing 5-7 parts of limestone, 9-10 parts of alumina, 11-15 parts of dolomite, 3-5 parts of zirconia and 7-8 parts of iron red epoxy ester primer according to the mass ratio, adding the above components into the mixture B and mixing uniformly so as to obtain a mixture C; mixing the mixture C and the mixture A to obtain a mixture D; and mixing the mixture D and 800-1000 parts of water, and uniformly stirring to obtain the releasing agent. The releasing agent prepared by the invention can be effectively attached to the inside surface of a casting mould, therefore, the surface of a cast iron ingot is smooth.

Description

technical field [0001] The invention relates to the technical field of release agents for metallurgical casting, and more specifically, to a preparation method of release agents for cast iron machines. Background technique [0002] The iron casting machine is a device for continuously casting molten iron into iron blocks. It is a circular chain belt with many iron molds and chain plates tilted upwards. It revolves around the star-shaped large gears at the upper and lower ends. The gear is a transmission wheel driven by a motor, and the star-shaped large gear at the lower end is a guide wheel, and its bearing position can be moved to adjust the tightness of the chain belt. According to the fixed situation of the roller, the cast iron machine is divided into a fixed roller cast iron machine and a movable roller cast iron machine. The process of cast iron machine is that the locomotive transports the molten iron tank car or mixed iron car loaded with molten iron from the blast...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
Inventor 高金菊
Owner 高金菊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap