Easy-welding tempering high-strength steel plate for ocean platform and production method thereof

A high-strength steel plate and offshore platform technology, which is applied in the field of low-alloy high-strength welded structural steel manufacturing, can solve the problems of inability to meet the market demand for thick plates, narrow specification range, etc., to improve equipment performance and service life, reduce precious metal content, Weight reduction effect

Inactive Publication Date: 2013-01-16
WUYANG IRON & STEEL +1
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As the amount of high-strength steel in the domestic construction machinery industry gradually increases, some domestic steel manufacturers produce steel plates of this level, but due to the narrow range of specifications, all are below 60mm, which cannot meet the growing market demand for thick plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The composition of the quenched and tempered high-strength steel in this example is as follows: C 0.14%, Si 0.27%, Mn 1.16%, P 0.015%, S 0.001%, Mo 0.41%, Ni 1.2%, Cr 1.04% , Nb 0.024%, V 0.033%, B 0.002%, Ti 0.015%, Al 0.064%, the balance is Fe and unavoidable impurities, rolled into 88mm steel plate.

[0023] Its mechanical properties: yield strength: 820MPa, tensile strength: 880MPa, A is 20%, -27°C impact energy AKV (longitudinal): 119, 129, 159J, -37°C impact energy AKV (longitudinal): 131, 126, 100J.

Embodiment 2

[0025] The composition of the quenched and tempered high-strength steel in this example is as follows: C 0.14%, Si 0.25%, Mn 1.15%, P 0.012%, S 0.002%, Mo 0.43%, Ni 1.25%, Cr 1.03% , Nb 0.027%, V 0.035%, B 0.0023%, Ti 0.019%, Al 0.050%, and the balance is Fe and inevitable inclusions. Ceq is 0.56%, rolled into 88mm steel plate.

[0026]Its mechanical properties: yield strength: 825MPa, tensile strength: 895MPa, A is 18%, -27°C impact energy AKV (longitudinal): 199, 199, 180J, -37°C impact energy AKV (longitudinal): 192, 190, 167J.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Impact energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses an easy-welding tempering high-strength steel plate for an ocean platform and a production method thereof. The easy-welding tempering high-strength steel plate for the ocean platform is prepared by the following chemical compositions in percent by weight: not higher than 0.18 percent of C, 0-0.15 to 0.35 percent of Si, 0.95 to 1.30 percent of Mn, not higher than 0.035 percent of P, not higher than 0.01 percent of S, 1.20 to 1.50 percent of Ni, 1.00 to 1.50 percent of Cr, 0.4 to 0.6 percent of Mo, not higher than 0.05 percent of Nb, 0.03 to 0.08 percent of V, not higher than 0.020 percent of Ti, not higher than 0.003 percent of B, 0.020 to 0.085 percent of Alt, and the balance of Fe and inevitable impurities. The thickness of the easy-welding tempering high-strength steel plate for the ocean platform is from 60 to 100 mm. The easy-welding tempering high-strength steel plate for the ocean platform is prepared by the following method: smelting-vacuum decarburization-LF furnace refining-pouring-cleaning-heating-rolling-water cooling after rolling-tempering-inspection and storage. The easy-welding tempering high-strength steel plate for the ocean platform has an outstanding combination property, is used for engineering machinery, has high surplus amount of impact toughness, can be widely used for engineering supports and other projects needing high-strength steel plates, and has a great application prospect. The easy-welding tempering high-strength steel plate for the ocean platform has simplicity in rolling technology, wide scope of tempering technology and easiness in operation, and is suitable for the production of the steel plant.

Description

technical field [0001] The invention belongs to the field of manufacturing low-alloy high-strength welded structural steel, and in particular relates to an easy-weld quenched and tempered high-strength A517GrQ Modified steel plate for offshore platforms, and also relates to a production method of the easy-weld quenched and tempered high-strength steel plate. Background technique [0002] Traditional quenched and tempered steel has the disadvantages of high carbon content, high alloy content and high carbon equivalent, which bring about high cost and unsatisfactory welding performance. Most of the high-strength steel in the domestic construction machinery industry comes from imports such as American A514Gr.B and DILLMAX690 steel plates produced by German DILLINGER Steel Company. The content of C (0.18%), Cr (1.50%), Ni ( 1.80%) alloy content is higher, and the cost price of steel plate rises. The prices of the above-mentioned imported steels are generally high. [0003] As ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/44C22C33/04C21D8/02
Inventor 宋向前袁忠业李劲峰孔祥丽齐燕管秀兵秦红新肖雄峰杨斌张晓克温冰
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com