A production process and veneer technology, which is applied in the direction of manufacturing tools, wood layered products, wood processing appliances, etc., can solve the problems of limiting the application range of wood products, small bending range, and poor practicability, etc., to achieve strong practicability, The effect of improving product grade and facilitating processing

Inactive Publication Date: 2013-01-02
徐州亚森木业工艺品有限公司
View PDF9 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing wood products are hard and straight materials that cannot be bent arbitrarily, and they will break after forced bending, which limits the application range of wood products
At present, there are also very thin veneer products on the market. Although it can achieve the effect of bending, the bending range is not large, and it will break after repeated bending, which is not very practical.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Softened veneer and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Below in conjunction with embodiment the present invention is further described.

[0021] Such as figure 1 As shown, a softened veneer comprises a cork layer I1 and a cork layer II3, and a solid glue layer 2 is fixed between the cork layer I1 and the cork layer II3, and the solid glue layer 2 binds the cork layer The above-mentioned cork layer I1 and cork layer II3 are connected into a softened veneer whole.

[0022] The thickness of the cork layer I1 and the cork layer II3 is 0.2-0.5 cm; the thickness of the solid glue layer 2 is 0.1-0.2 cm.

[0023] A kind of manufacture craft of described softening veneer, comprises the following steps:

[0024] 1. Material selection, choose wood without cracks, cut it into thin plates with a thickness of 0.2-0.5 cm, and prepare materials for cork layer Ⅰ1 and cork layer Ⅱ3;

[0025] 2. Prepare solid glue, use ethylene propylene as the main raw material to prepare solid glue, and then evenly coat it on the underlying cork layer Ⅰ1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses softened veneer and a manufacturing process thereof, belonging to the technical field of timber processing. The softened veneer comprises a soft wood piece layer I and a soft wood piece layer II, a solid glue layer is fixed between the soft wood piece layer I and the soft wood piece layer II, and the soft wood piece layer I and the soft wood piece layer II are connected by the solid glue layer into the whole softened veneer. The softened veneer can be bent freely without breakage and is soft and durable. The appearance and properties of timber are adopted by the two wood surface layers, and the softened veneer is a novel material with strong practicality.

Description

technical field [0001] The invention relates to a cork veneer that can be bent arbitrarily, and belongs to the technical field of wood processing. Background technique [0002] Existing wood products are hard and straight materials that cannot be bent arbitrarily, and will break after forced bending, which limits the application range of wood products. There are also very thin veneer products on the market at present. Although it can achieve the effect of bending, the bending range is not large, and it will break after repeated bending, so the practicability is not strong. Contents of the invention [0003] In order to overcome the shortcomings of the above-mentioned prior art, the present invention provides a softened veneer and its manufacturing process, which can realize the veneer being bent arbitrarily without breaking. [0004] The present invention is achieved through the following technical scheme: a softened veneer, which includes a cork layer I and a cork layer ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B32B21/13B27D1/08
Inventor 柳承彬柳德岭
Owner 徐州亚森木业工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap